Linear Ion Source에 의해 증착된 Diamond-Like Carbon(DLC) 박막의 질화층 형성에 따른 밀착력 특성 연구
Study on the Adhesion of Diamond Like Carbon Films Using the Linear Ion Source with Nitriding Layers
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Diamond-like carbon (DLC) has many outstanding properties such as low friction, high wear resistance and corrosion resistance. However, it is difficult to achieve enough adhesion on the metal substrates because of weak bonding between DLC film and the metal substrate. The purpose of this study is to enhance an adhesion of DLC film. For improving adhesion, the substrate was treated by active screen plasma nitriding before DLC film deposing. Nitrided substrates were investigated by Glow Discharge Spectrometer (GDS),Micro-Vickers Hardness. DLC films were deposited on several metals by linear ion source, and characteristics of the films were investigated using nano-indentation, Field Emission Scanning Electron Microscope (FESEM). The adhesion was measured by scratch tester. The adhesion of DLC films was increased when nitriding layer was formed before DLC deposition. Therefore, the adhesion of DLC film can be enhanced as increasing the hardness of materials.
Abstract
Diamond-like carbon (DLC) has many outstanding properties such as low friction, high wear resistance and corrosion resistance. However, it is difficult to achieve enough adhesion on the metal substrates because of weak bonding between DLC film and the metal substrate. The purpose of this study is to enhance an adhesion of DLC film. For improving adhesion, the substrate was treated by active screen plasma nitriding before DLC film deposing. Nitrided substrates were investigated by Glow Discharge Spectrometer (GDS),Micro-Vickers Hardness. DLC films were deposited on several metals by linear ion source, and characteristics of the films were investigated using nano-indentation, Field Emission Scanning Electron Microscope (FESEM). The adhesion was measured by scratch tester. The adhesion of DLC films was increased when nitriding layer was formed before DLC deposition. Therefore, the adhesion of DLC film can be enhanced as increasing the hardness of materials.
참고문헌 (19)
- M.Zlatanovic, , Surf. Coat. Tech., 45, pp.19~ (1991)
- A. Matthews, , Diam. Relat. Mater., 3, pp.902~ (1994)
- H. Kakiuchi, , Nucl. Inst. Meth. Phys. Res. B, 166, pp.415~ (2000)
- K. J. Clay, , Diam. Relat. Mater., 7, pp.1100~ (1998)
- R. Lappalanen, , Diam. Relat. Mater, 7, pp.482~ (1998)
- G. H. Jeong, , J. Kor. Inst. Met. & Mater, 37 (1999)
- H. Dimigen, , Philips Tech. Rev., 41(6), pp.186~ (1984)
- A. Grill, , Surf. Coat. Technol, 94, pp.507~ (1997)
- K. Taube, , Surf. Coat. Technol, 68, pp.662~ (1994)
- K.-R. Lee, , thin Solid films, 388, pp.261~268 (2000)
- H.-J. Spies, , Surf. Coat. Tech., 60, pp.441~ (1993)
- T. Gredic, , Thin Solid Films, 228, pp.261~ (1993)
- E. Menthe, , Surf. Coat. Technol, 74, pp.412~ (1995)
- E. I. Meletis, , Surf. Coat. Technol, 73, pp.39~ (1995)
- B. Larisch, , Surf. Coat. Technol, 116, pp.205~ (1999)
- J. Choi, "Nuclear Instruments and Methods in Physical Research B" (2011)
- 선주현, "열노출 온도에 따른 CP 티타늄, Ti-6Al-4V 합금의 미세조직", 기계적성질 변화 및 저온브레이징 특성, 2010, pp.23(1), 3~9[DOI]
- T. Czerwiec, , Surf. Coat. Technol., 108, pp.182~190 (1998)
- W. R. Kim, , J. Kor. Inst. Surf. Eng, 42 (2009)