Spark Plasma Sintering of Stainless Steel Powders Fabricated by High Energy Ball Milling
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The 304 stainless steel powders were prepared by high energy ball milling and subsequently sintered byspark plasma sintering, and the microstructural characteristics and micro-hardness were investigated. The initial size ofthe irregular shaped 304 stainless steel powders was approximately 42 μm. After high energy ball milling at 800 rpmfor 5h, the powders became spherical with a size of approximately 2 μm, and without formation of reaction compounds. From TEM analysis, it was confirmed that the as-milled powders consisted of the aggregates of the nano-sized particles. As the sintering temperature increased from 1073K to 1573K, the relative density and micro-hardness of sintered sampleincreased. The sample sintered at 1573K showed the highest relative density of approximately 95% and a micro-hardnessof 550 Hv.
Abstract
The 304 stainless steel powders were prepared by high energy ball milling and subsequently sintered byspark plasma sintering, and the microstructural characteristics and micro-hardness were investigated. The initial size ofthe irregular shaped 304 stainless steel powders was approximately 42 μm. After high energy ball milling at 800 rpmfor 5h, the powders became spherical with a size of approximately 2 μm, and without formation of reaction compounds. From TEM analysis, it was confirmed that the as-milled powders consisted of the aggregates of the nano-sized particles. As the sintering temperature increased from 1073K to 1573K, the relative density and micro-hardness of sintered sampleincreased. The sample sintered at 1573K showed the highest relative density of approximately 95% and a micro-hardnessof 550 Hv.
참고문헌 (10)
- J. S. Benjamin, , Metall. Trans., 1, pp.2943~ (1970)
- L. Gao, , J. Inorg. Mater., 12, pp.129~ (1997)
- M. Tokita, , J. Soc. Powder Technol. Japan, 30, pp.790~ (1993)
- T. Takeuchi, , J. Am. Ceram. Soc., 82, pp.939~ (1999)
- Z. J. Shen, , J. Am. Ceram. Soc., 85, pp.1921~ (2002)
- G. D. Zhan, , Nat. Mat., 2, pp.38~ (2003)
- S. I. Cha, , Mater. Sci. Eng. A, 351, pp.31~ (2003)
- M. Yue, , IEEE Trans. Magn., 39, pp.3551~ (2003)
- Diandra L. Leslie-Pelecky, , Nano-Structured Materials, 12, pp.887~ (1999)
- Japan Institute of Metals, "Ferrous Materials", 167~ (1988)