Core-shell 구조를 지니는 하모닉분말의 성형거동 분석
Effect of Core-Shell Structure on Compaction Behavior of Harmonic Powder
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, effect of core-shell structure on compaction behavior of harmonic powder is investigated. Harmonic powders are made by electroless plating method on Fe powders. Softer Cu shell encloses harder Fe core, and the average size of Fe core and thickness of Cu shell are 34.3 μm and 3.2 μm, respectively. The powder compaction procedure is processed with pressure of 600 MPa in a cylindrical die. Due to the low strength of Cu shell regions, the harmonic powders show better densification behavior compared with pure Fe powders. Finite element method (FEM) is performed to understand the roll of core-shell structure. Based on stress and strain distributions of FEM results, it is concluded that the early stage of powder compaction of harmonic powders mainly occurs at the shell region. FEM results also well predict porosity of compacted materials.
Abstract
In this study, effect of core-shell structure on compaction behavior of harmonic powder is investigated. Harmonic powders are made by electroless plating method on Fe powders. Softer Cu shell encloses harder Fe core, and the average size of Fe core and thickness of Cu shell are 34.3 μm and 3.2 μm, respectively. The powder compaction procedure is processed with pressure of 600 MPa in a cylindrical die. Due to the low strength of Cu shell regions, the harmonic powders show better densification behavior compared with pure Fe powders. Finite element method (FEM) is performed to understand the roll of core-shell structure. Based on stress and strain distributions of FEM results, it is concluded that the early stage of powder compaction of harmonic powders mainly occurs at the shell region. FEM results also well predict porosity of compacted materials.
참고문헌 (10)
- H. S. Kim, , J. Kor. Inst. Met. Metal., 30, pp.37~ (1992)
- R. M. German, "Powder Metallurgy of iron and Steel", pp.128~ (1998), John Wiley & Sons, Inc
- A. Salak, "Ferrous powder metallurgy", pp.62~ (1996), CISP
- J. S. Hirschhorn, , Powder Tech., 5, pp.72~ (1971)
- I. Nikolakakis, , Powder Tech., 56, pp.95~ (1988)
- D. Poquillon, , Powder Tech., 126, pp.65~ (2002)
- D. Poquillon, , Powder Tech., 126, pp.75~ (2002)
- 김형섭, "분말 응집체의 치밀화에 관한 모델", 한국분말야금학회지, 11(4), pp.301~307 (2004), 한국분말야금학회
- R. M. German, "Powder Metallurgy of iron and Steel", pp.152~ (1998), John Wiley & Sons, Inc
- 송명엽, "PCT Curve and Cycling Performance of MgH2-Ni-NaAlH4-Ti Alloy Milled under H2", 대한금속·재료학회지, 52(5), pp.391~396 (2014), 대한금속·재료학회