수분사법으로 제조된 순철분말의 성형성에 미치는 분말크기의 영향
Effect of Particle Size on Compactibility of Water-atomized Pure Iron Powder
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In the current study, the effects of particle size on compaction behavior of water-atomized pure iron powders are investigated. The iron powders are assorted into three groups depending on the particle size; 20-45μm, 75-106 μm, and 150-180 μm for the compaction experiments. The powder compaction procedures are processed with pressure of 200, 400, 600, and 800 MPa in a cylindrical die. After the compaction stage, the group having 150-180 μm of particle size distribution shows the best densification behavior and reaches the highest green density. The reason for these results can be explained by the largest average grain size in the largest particle group, due to the low plastic deformation resistance in large grain sized materials.
Abstract
In the current study, the effects of particle size on compaction behavior of water-atomized pure iron powders are investigated. The iron powders are assorted into three groups depending on the particle size; 20-45μm, 75-106 μm, and 150-180 μm for the compaction experiments. The powder compaction procedures are processed with pressure of 200, 400, 600, and 800 MPa in a cylindrical die. After the compaction stage, the group having 150-180 μm of particle size distribution shows the best densification behavior and reaches the highest green density. The reason for these results can be explained by the largest average grain size in the largest particle group, due to the low plastic deformation resistance in large grain sized materials.
참고문헌 (13)
- H. S. Kim, , J. Kor. Inst. Metal, 20, pp.37~ (1992)
- R. M. German, "Powder Metallurgy of iron and Steel", pp.128~ (1998), John Wiley & Sons, Inc
- A. Salak, "Ferrous powder metallurgy", pp.62~ (1996), CISP
- J. S. Hirschhorn, , Powder Tech, 5, pp.72~ (1971)
- I. Nikolakakis, , Powder Tech, 56, pp.95~ (1988)
- D. Poquillon, , Powder Tech, 126, pp.65~ (2002)
- D. Poquillon, , Powder Tech, 126, pp.75~ (2002)
- D. P. Debrincat, , Mineral Proc, 87, pp.17~ (2008)
- H. S. Kim, , J. Kor. Inst. Metal, 11, pp.301~ (2004)
- R. M. German, "Powder Metallurgy of iron and Steel", pp.152~ (1998), John Wiley & Sons, Inc
- E. O. Hall, , Proc. Phys. Soc, 64, pp.747~ (1951)
- N. J. Petch, , J. Iron Steel Inst, 174, pp.25~ (1953)
- R. M. German, "Powder Metallurgy of iron and Steel", pp.149~ (1998), John Wiley & Sons, Inc