다결정 다이아몬드 컴팩트(PDC)의 미세조직 및 내마모 특성에 미치는 초기 성형 압력의 영향
Effect of Molding Pressure on the Microstructure and Wear Resistance Property of Polycrystalline Diamond Compact
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
This study investigated the microstructure and wear resistance property of HPHT(high pressure high temperature) sintered PDC(polycrystalline diamond compact) in accordance with initial molding pressure. After quantifying an identical amount of diamond powder, the powder was inserted in top of WC-Co sintered material, and molded under four different pressure conditions (50, 100, 150, 200 kgf/cm2). The obtained diamond compact underwent sintering in high pressure, high temperature conditions. In the case of the 50 kgf/cm2 initial molding pressure condition, cracks were formed on the surface of PDC. On the other hand, PDCs obtained from 100~200 kgf/cm2 initial molding pressure conditions showed a meticulous structure. As molding pressure increased, low Co composition within PDC was detected. A wear resistance test was performed on the PDC, and the 200 kgf/cm2 condition PDC showed the highest wear resistance property.
Abstract
This study investigated the microstructure and wear resistance property of HPHT(high pressure high temperature) sintered PDC(polycrystalline diamond compact) in accordance with initial molding pressure. After quantifying an identical amount of diamond powder, the powder was inserted in top of WC-Co sintered material, and molded under four different pressure conditions (50, 100, 150, 200 kgf/cm2). The obtained diamond compact underwent sintering in high pressure, high temperature conditions. In the case of the 50 kgf/cm2 initial molding pressure condition, cracks were formed on the surface of PDC. On the other hand, PDCs obtained from 100~200 kgf/cm2 initial molding pressure conditions showed a meticulous structure. As molding pressure increased, low Co composition within PDC was detected. A wear resistance test was performed on the PDC, and the 200 kgf/cm2 condition PDC showed the highest wear resistance property.
참고문헌 (14)
- F. Bellin, , World Oil, 231, pp.41~ (2010)
- D. Belnap, , Diam. Relat. Mater., 13, pp.1914~ (2004)
- D. E. Scott, , Ind. Diam. Rev., 1, pp.48~ (2006)
- H. D. Stromberg, , Am. Ceram. Soc. Bull., 49, pp.1030~ (1990)
- H. Katman, , Science, 172, pp.1132~ (1971)
- H. T. Hall, , Science, 169, pp.868~ (1970)
- R. H. Wentorf, , Science, 208, pp.873~ (1980)
- P. A. Bex, , Ind. Diam. Rev., 44, pp.128~ (1984)
- V. Kanyanta, , Int. J. Refract. Met. Hard Mater., 31, pp.145~ (2014)
- C. Liu, , Int. J. Refract. Met. Hard Mater., 31, pp.187~ (2012)
- D. Miess, , Mater. Sci. Eng., 209, pp.270~ (1996)
- D. M. Bigg, , Polymer Engineering & Science, 17, pp.691~ (1997)
- M. Yahiaoui, , Wear, 298, pp.32~ (2013)
- F. Bellin, , World Oil, 231, pp.53~ (2010)