고압 가스 분무법을 이용한 Fe-Hf-B-Nb-P-C 연자성분말 제조 및 특성 평가
Investigation on Fe-Hf-B-Nb-P-C Soft Magnetic Powders Prepared by High-Pressure Gas Atomization
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, ultra-fine soft-magnetic micro-powders are prepared by high-pressure gas atomization of an Fe-based alloy, Fe-Hf-B-Nb-P-C. Spherical powders are successfully obtained by disintegration of the alloy melts under high-pressure He or N2 gas. The mean particle diameter of the obtained powders is 25.7 μm and 42.1 μm for He and N2 gas, respectively. Their crystallographic structure is confirmed to be amorphous throughout the interior when the particle diameter is less than 45 μm. The prepared powders show excellent soft magnetic properties with a saturation magnetization of 164.5 emu/g and a coercivity of 9.0 Oe. Finally, a toroidal core is fabricated for measuring the magnetic permeability, and a μr of up to 78.5 is obtained. It is strongly believed that soft magnetic powders prepared by gas atomization will be beneficial in the fabrication of high-performance devices, including inductors and motors.
Abstract
In this study, ultra-fine soft-magnetic micro-powders are prepared by high-pressure gas atomization of an Fe-based alloy, Fe-Hf-B-Nb-P-C. Spherical powders are successfully obtained by disintegration of the alloy melts under high-pressure He or N2 gas. The mean particle diameter of the obtained powders is 25.7 μm and 42.1 μm for He and N2 gas, respectively. Their crystallographic structure is confirmed to be amorphous throughout the interior when the particle diameter is less than 45 μm. The prepared powders show excellent soft magnetic properties with a saturation magnetization of 164.5 emu/g and a coercivity of 9.0 Oe. Finally, a toroidal core is fabricated for measuring the magnetic permeability, and a μr of up to 78.5 is obtained. It is strongly believed that soft magnetic powders prepared by gas atomization will be beneficial in the fabrication of high-performance devices, including inductors and motors.
참고문헌 (15)
- Y. K. Joon, , J. KIEEME, 9, pp.76~ (1996)
- 김휘준, "고에너지효율 연자성 복합 분말 소재의 연구개발 동향", 한국자기학회지, 21(2), pp.77~82 (2011), 한국자기학회
- Y. Liu, , J. Magn. Magn. Mater., 330, pp.119~ (2013)
- L. Svensson, , J. Magn. Magn. Mater., 324, pp.2717~ (2012)
- G. Herzer, , Acta Mater., 61, pp.718~ (2013)
- H. R. Lashgari, , J. Non-Cryst. Solids, 391, pp.61~ (2014)
- M. H. Lee, "KR 10-2015-0082316", ~ (2015)
- T. Ma, , Scr. Mater., 58, pp.243~ (2008)
- S. Lagutkin, , Mater. Sci. Eng.A, 383, pp.1~ (2004)
- K. Yoshida, , AIP Advances, 6, pp.055933~ (2016)
- A. Ünal, , Mater. Sci. Technol., 3, pp.1029~ (1987)
- G. Antipas, , Metals, 2, pp.202~ (2012)
- M. Nabia³ek, , J. Alloys Compd., 615, pp.S56~ (2014)
- J. D. Ayers, , Acta Mater., 46, pp.1861~ (1998)
- C. H. Chia, , Ceram. Int., 36, pp.605~ (2010)