분무건조된 Nd-Fe-B 전구체 입자의 크기조절 및 환원-확산후 자기 특성에 미치는 영향
Size Control of Nd-Fe-B Precursor Particles Prepared by Spray Drying and Its Effect on the Magnetic Properties of Nd-Fe-B Alloy Powders after Reduction-Diffusion
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this study, we fabricated Nd2Fe14B hard magnetic powders with various sizes via spray drying combined with reduction-diffusion process. Spray drying is widely used to produce nearly spherical particles that are relatively homogeneous. Thus, the precursor particles were prepared by spray drying using the aqueous solution containing Nd salts, Fe salts and boric acid with the target stoichiometric composition of Nd2Fe14B. The mean particle sizes of the spray-dried powders are in the range from one to seven micrometer, which are adjusted by controlling the concentrations of precursor solutions. After debinding the as-prepared precursor particles, ball milling was also conducted to control the particle sizes of Nd-Fe-B oxide powders. The resulting particles with different sizes were subjected to subsequent treatments including hydrogen reduction, Ca reduction and washing for CaO removal. The size effect of Nd-Fe-B oxide particles on the formation of Nd2Fe14B phase and magnetic properties was investigated.
Abstract
In this study, we fabricated Nd2Fe14B hard magnetic powders with various sizes via spray drying combined with reduction-diffusion process. Spray drying is widely used to produce nearly spherical particles that are relatively homogeneous. Thus, the precursor particles were prepared by spray drying using the aqueous solution containing Nd salts, Fe salts and boric acid with the target stoichiometric composition of Nd2Fe14B. The mean particle sizes of the spray-dried powders are in the range from one to seven micrometer, which are adjusted by controlling the concentrations of precursor solutions. After debinding the as-prepared precursor particles, ball milling was also conducted to control the particle sizes of Nd-Fe-B oxide powders. The resulting particles with different sizes were subjected to subsequent treatments including hydrogen reduction, Ca reduction and washing for CaO removal. The size effect of Nd-Fe-B oxide particles on the formation of Nd2Fe14B phase and magnetic properties was investigated.
참고문헌 (13)
- M. Sagawa., , J. Appl. Phys, 55, pp.2083~ (1984)
- J. G. Lee., , Trends in Metals & Materials Engineering, 24, pp.4~ (2010)
- J. J. Croat., , J. Appl. Phys, 55, pp.2078~ (1984)
- N. C. Koon., , J. Appl. Phys, 55, pp.2063~ (1984)
- R. E. Cech, , JOM, 26, pp.32~ (1974)
- A. Kawamoto, , IEEE Trans Magn, 35, pp.3322~ (1999)
- K. Ohmori., , J. Appl. Phys, 69, pp.5504~ (1991)
- D. C. Jiles, , Acta Mater, 51, pp.5907~ (2003)
- E. F. Kneller., , IEEE Trans. Magn, 27, pp.3588~ (1991)
- R. K. Sidhu, , J. Alloys Comp, 346, pp.250~ (2002)
- Okajima., , US Patent No. 4, 681, 623~ (1987)
- R. E. Cech., , US Patent No. 3, 748, 193~ (1973)
- K. Masters, "Spray Drying Handbook , 3rd editio" (1979), Longman Scientific & Technical