일축가압법으로 벌크흑연 제조 시 성형압력에 따른 열린기공률 변화가 함침 후 밀도 향상에 미치는 영향
Effect of Change in Open Porosity as a Function of Uniaxial Molding Pressure on Density Improvement After Impregnation
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The change in the open porosity of bulk graphite as a function of the uniaxial molding pressure during manufacturing is studied using artificial graphite powder. Subsequently, the graphite is impregnated to determine the effect of the open porosity on the impregnation efficiency and to improve the density of the final bulk graphite. Bulk graphite is manufactured with different uniaxial molding pressures after mixing graphite powder, which is the by-product of processing the final graphite products and phenolic resin. The bulk density and open porosity are measured using the Archimedes method. The bulk density and open porosity of bulk graphite increase as the molding pressure increases. The open porosity of molded bulk graphite is 25.35% at 30 MPa and 29.84% at 300 MPa. It is confirmed that the impregnation efficiency increases when the impregnation process is performed on a specimen with large open porosity. In this study, the bulk density of bulk graphite molded at 300 MPa is 11.06% higher than that before impregnation, which is the highest reported increase. Therefore, it is expected that the higher the uniaxial pressure, the higher the density of bulk graphite.
Abstract
The change in the open porosity of bulk graphite as a function of the uniaxial molding pressure during manufacturing is studied using artificial graphite powder. Subsequently, the graphite is impregnated to determine the effect of the open porosity on the impregnation efficiency and to improve the density of the final bulk graphite. Bulk graphite is manufactured with different uniaxial molding pressures after mixing graphite powder, which is the by-product of processing the final graphite products and phenolic resin. The bulk density and open porosity are measured using the Archimedes method. The bulk density and open porosity of bulk graphite increase as the molding pressure increases. The open porosity of molded bulk graphite is 25.35% at 30 MPa and 29.84% at 300 MPa. It is confirmed that the impregnation efficiency increases when the impregnation process is performed on a specimen with large open porosity. In this study, the bulk density of bulk graphite molded at 300 MPa is 11.06% higher than that before impregnation, which is the highest reported increase. Therefore, it is expected that the higher the uniaxial pressure, the higher the density of bulk graphite.
참고문헌 (23)
- R. Setton, "Carbon Molecules and Materials, 14", pp.457~ (2002), Taylor & Francis
- C. L. Fan, , Electrochim. Acta, 75, pp.311~ (2012)
- 이상민, "Bulk graphite: materials and manufacturing process", Carbon Letters, 16(3), pp.135~146 (2015), 한국탄소학회
- K. Y. Cho, , Carbon Lett, 7, pp.196~ (2006)
- L. Xiaowei, , Nucl. Eng. Des, 227, pp.273~ (2004)
- G. D. Considine, "Van Nostrand's Encyclopedia of Chemistry" (2005), Wiley-Interscience
- N. Cunningham, , Carbon, 43, pp.3054~ (2005)
- H. J. Chung, , J. Kor. Ceram. Soc, 33, pp.1387~ (1996)
- 신영우, "고밀도 팽창흑연 성형품의 기계적 특성에 관한 연구(1)", 동력시스템공학회지, 9(4), pp.143~147 (2005), 한국동력기계공학회
- Seongyop Lim, "Carbon Materials as Catalysts", Carbon Letters, 9(1), pp.47~60 (2008), 한국탄소학회
- 한요셉, "반암(맥반석)으로 제조한 다공성 펠렛의 Ag 담지 및 항균 메디아로서의 적용", 한국세라믹학회지, 46(1), pp.16~23 (2009), 한국세라믹학회
- K. Ishizaki, (1998), Kluwer Academic Publishers
- 이상민, "Fabrication of isotropic bulk graphite using artificial graphite scrap", Carbon Letters, 15(2), pp.142~145 (2014), 한국탄소학회
- A. Cao, , Chem. Phys. Lett, 344, pp.13~ (2001)
- J. S. Roh, , Carbon Lett, 5, pp.27~ (2004)
- M. S. Seehra, , Carbon, 32, pp.431~ (1994)
- T. E. Weller, , Nat. Phys, 1, pp.39~ (2005)
- G. A. Slack, , Phys. Rev, 127, pp.694~ (1962)
- L. Lu, , Carbon, 39, pp.1821~ (2001)
- B. Manoj, , Int. J. Electrochem. Sci, 7, pp.3127~ (2012)
- J. B. Aladekomo, , Carbon, 28, pp.897~ (1990)
- T. D. Shen, , Nanostructured Materials, 7, pp.393~ (1996)
- 이상혜, "X-ray diffraction analysis of the effect of ball milling time on crystallinity of milled polyacrylonitrile-based carbon fiber", Carbon Letters, 26(1), pp.11~17 (2018), 한국탄소학회