흑연블록 제조를 위한 등압성형 시 일축가압 예비성형의 압력변화에 따른 기계적 및 전기적 특성 변화
Changes in Mechanical and Electrical Properties as a Function of Unidirectional Pressure Changes in Preforming While Isostatic Pressing for Graphite Block Fabrication
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, a graphite block is fabricated using artificial graphite processing byproduct and phenolic resin as raw materials. Mechanical and electrical property changes are confirmed due to the preforming method. After fabricating preforms at 50, 100, and 150 MPa, CIP molding at 150 MPa is followed by heat treatment to prepare a graphite block. 150UP-CIP shows a 12.9% reduction in porosity compared with the 150 MPa preform. As the porosity is decreased, the bulk density, flexural strength, and shore hardness are increased by 14.9%, 102.4%, and 13.7%, respectively; and the deviation of density and electrical resistivity are decreased by 51.9% and 34.1%, respectively. Therefore, as the preforming pressure increases, the porosity decreases, and the electrical and mechanical properties improve.
Abstract
In this study, a graphite block is fabricated using artificial graphite processing byproduct and phenolic resin as raw materials. Mechanical and electrical property changes are confirmed due to the preforming method. After fabricating preforms at 50, 100, and 150 MPa, CIP molding at 150 MPa is followed by heat treatment to prepare a graphite block. 150UP-CIP shows a 12.9% reduction in porosity compared with the 150 MPa preform. As the porosity is decreased, the bulk density, flexural strength, and shore hardness are increased by 14.9%, 102.4%, and 13.7%, respectively; and the deviation of density and electrical resistivity are decreased by 51.9% and 34.1%, respectively. Therefore, as the preforming pressure increases, the porosity decreases, and the electrical and mechanical properties improve.
참고문헌 (25)
- K. Y. Cho, , Carbon Lett, 7, pp.196~ (2006)
- L. Xiaowei, , Nucl. Eng. Des, 227, pp.273~ (2004)
- G. D. Considine, "Van Nostrand's Encyclopedia of Chemistry" (2005), Wiley-Interscience
- N. Cunningham, , Carbon, 43, pp.3054~ (2005)
- K. Janerka, , Arch. Foundry Eng, 8, pp.55~ (2008)
- A. Roessler, , Dyes Pigm, 63, pp.29~ (2004)
- C. I. Fan, , J. Mater. Sci, 46, pp.2140~ (2011)
- S. Ragan, , J. Mater. Sci, 18, pp.3161~ (1983)
- 이상민, "Bulk graphite: materials and manufacturing process", Carbon Letters, 16(3), pp.135~146 (2015), 한국탄소학회
- An Donghae, "Effect of kneading and carbonization temperature on the structure of the carbon block for thermally conductive bulk graphites", Carbon Letters, 31(6), pp.1357~1364 (2021), 한국탄소학회[DOI]
- K. T. Kim, , J. Eng. Mater. Technol, 122, pp.238~ (2000)
- H. T. Lee, , Transactions of the Korean Society of Mechanical Engineers A, 21, pp.1116~ (1997)
- J. W. Jeong, , Transactions of the Korean Society of Mechanical Engineers A, 22, pp.330~ (1998)
- 백정현, "α-알루미나의 미세구조 및 기계적 성질에 미치는 성형방법의 영향", 전기전자재료학회논문지, 32(4), pp.333~340 (2019), 한국전기전자재료학회[DOI]
- S. Yeo, , J. Nucl. Mater, 515, pp.245~ (2019)
- N. Shinohara, , J. Eur. Ceram. Soc, 20, pp.843~ (2000)
- A. R. Rojas, , Mater. Res. Express, 5, pp.105602~ (2018)
- G. Y. Akimov, , Refract. Ind. Ceram, 39, pp.283~ (1998)
- 이상혜, "입자 크기별 가공부산물로 제조된 벌크흑연의 기계적 성질", 한국분말재료학회지, 28(1), pp.13~19 (2021), 한국분말재료학회
- S. M. Lee, , J. Mater. Sci, 28, pp.7~ (2021)
- S. H. Lee, , Materials, 15, pp.3259~ (2022)
- T. Sun, , New Carbon Materials, 28, pp.349~ (2013)
- G. Lu, , J. Porous Mater, 6, pp.359~ (1999)
- R. W. Rice, , J. Mater. Sci, 28, pp.2187~ (1993)
- K. Oshida, , Tanso, 1996, pp.142~ (1996)