레이저 파우더 베드 퓨전 3차원 적층된 Cu-10Sn 합금의 미세조직 및 기계적 특성
Microstructure and Mechanical Properties of Laser Powder Bed Fusion 3D-Printed Cu-10Sn Alloy
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
This study investigated the optimal process conditions and mechanical properties of Cu-10Sn alloys produced by the powder bed fusion (PBF) method. The optimal PBF conditions were explored by producing samples with various laser scanning speeds and laser power. It was found that under optimized conditions, samples with a density close to the theoretical density could be fabricated using PBF without any serious defects. The microstructure and mechanical properties of samples produced under optimized conditions were investigated and compared with a commercial alloy produced by the conventional method. The hardness, maximum tensile strength, and elongation of the samples were significantly higher than those of the commercially available cast alloy with the same chemical composition. Based on these results, it is expected to be possible to use the PBF technique to manufacture Cu-10Sn products with complex 3D shapes that could not be made using the conventional manufacturing method.
Abstract
This study investigated the optimal process conditions and mechanical properties of Cu-10Sn alloys produced by the powder bed fusion (PBF) method. The optimal PBF conditions were explored by producing samples with various laser scanning speeds and laser power. It was found that under optimized conditions, samples with a density close to the theoretical density could be fabricated using PBF without any serious defects. The microstructure and mechanical properties of samples produced under optimized conditions were investigated and compared with a commercial alloy produced by the conventional method. The hardness, maximum tensile strength, and elongation of the samples were significantly higher than those of the commercially available cast alloy with the same chemical composition. Based on these results, it is expected to be possible to use the PBF technique to manufacture Cu-10Sn products with complex 3D shapes that could not be made using the conventional manufacturing method.
참고문헌 (26)
- B. Dutta, , Metal Powder Rep, 72, pp.96~ (2017)
- T. J. Kang, , Korean J. Metal Mater, 61, pp.714~ (2023)
- M. Ninomi, "Metals for Biomedical Devices" (2019), Woodhead publishing
- S. Jie, , Electrochim. Acta, 297, pp.87~ (2019)
- G. A. Gohar, , J. Alloys Compd, 817, pp.153281~ (2020)
- Y. Liu, , J. Alloys Compd, 775, pp.818~ (2019)
- J. B. Singh, , Wear, 263, pp.830~ (2007)
- G. Cui, , Tribology Int, 53, pp.76~ (2012)
- Z. Mao, , Mater. Sci. Eng. A, 721, pp.125~ (2018)
- Y. Sürme, , J. Alloys and Compd, 485, pp.98~ (2009)
- Y. Kang, , Surf. Interface Anal, 50, pp.138~ (2017)
- S. Scudino, , Mater. Lett, 156, pp.202~ (2015)
- P. Han, , Mater. Des, 53, pp.38~ (2014)
- E. Erzi, , Mater. Sci. Tech, 35, pp.2211~ (2019)
- X. Liu, , Progress in Natural Science: Materials International, 23, pp.94~ (2013)
- A. P. Ventura, , Metall. Mater. Trans. A, 48, pp.178~ (2017)
- A. M. Khorasani, , Virtual Phys. Prototyp, 14, pp.349~ (2019)
- S. Bai, , Appl. Sci, 9, pp.583~ (2019)
- M. Malý, , Mater, 12, pp.930~ (2019)
- N. Emminghaus, "Additive manufacturing of CuSn10 Powder via selective laser melting", Proceeding of Lasers in Manufacturing Conference, pp.1~ (2019)
- G. M. Karthik, , Addit. Manuf, 54, pp.102744~ (2022)
- W. Kurz, , Mater. Sci. Eng. A, 179, pp.46~ (1994)
- N. Saunders, , Bulletin of Alloy Phase Diagram, 11, pp.278~ (1990)
- P. Yang, , J. Mater. Res. Tech, 24, pp.5476~ (2023)
- S. Wolff, , J. Manuf. Process, 24, pp.397~ (2016)
- S. Li, , Inst. Mater. Miner. Min, 68, pp.605~ (2023)