선택적 레이저 용융공정으로 제조된 Al-Si-Mg 합금의 열처리에 따른 미세조직 및 특성평가
Microstructures and Characterization of Al-Si-Mg Alloy Processed by Selective Laser Melting with Post-Heat-treatment
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this study, Al-Si-Mg alloys are additively manufactured using a selective laser melting (SLM) process from AlSi10Mg powders prepared from a gas-atomization process. The processing parameters such as laser scan speed and laser power are investigated for 3D printing of Al-Si-Mg alloys. The laser scan speeds vary from 100 to 2000 mm/ s at the laser power of 180 and 270W, respectively, to achieve optimized densification of the Al-Si-Mg alloy. It is observed that the relative density of the Al-Si-Mg alloy reaches a peak value of 99% at 1600 mm/s for 180W and at 2000 mm/s for 270W. The surface morphologies of the both Al-Si-Mg alloy samples at these conditions show significantly reduced porosities compared to those of other samples. The increase in hardness of as-built Al-Si-Mg alloy with increasing scan speed and laser power is analyzed due to high relative density. Furthermore, it was found that cooling conditions after the heat-treatment for homogenization results in the change of dispersion status of Si phases in the Al-Si matrix but also affects tensile behaviors of Al-Si-Mg alloys. These results indicate that combination between SLM processing parameters and post-heat treatment should be considered a key factor to achieve optimized Al-Si alloy performance.
Abstract
In this study, Al-Si-Mg alloys are additively manufactured using a selective laser melting (SLM) process from AlSi10Mg powders prepared from a gas-atomization process. The processing parameters such as laser scan speed and laser power are investigated for 3D printing of Al-Si-Mg alloys. The laser scan speeds vary from 100 to 2000 mm/ s at the laser power of 180 and 270W, respectively, to achieve optimized densification of the Al-Si-Mg alloy. It is observed that the relative density of the Al-Si-Mg alloy reaches a peak value of 99% at 1600 mm/s for 180W and at 2000 mm/s for 270W. The surface morphologies of the both Al-Si-Mg alloy samples at these conditions show significantly reduced porosities compared to those of other samples. The increase in hardness of as-built Al-Si-Mg alloy with increasing scan speed and laser power is analyzed due to high relative density. Furthermore, it was found that cooling conditions after the heat-treatment for homogenization results in the change of dispersion status of Si phases in the Al-Si matrix but also affects tensile behaviors of Al-Si-Mg alloys. These results indicate that combination between SLM processing parameters and post-heat treatment should be considered a key factor to achieve optimized Al-Si alloy performance.
참고문헌 (13)
- 신기훈, "선택적 레이저 용융공정을 이용한 316L 스테인리스강 분말 3차원 조형체의 미세조직 및 경도 연구", 한국분말재료학회지, 24(3), pp.210~215 (2017), 한국분말재료학회[DOI]
- A. Ambrosi, , Chem. Soc. Rev, 45, pp.2740~ (2016)
- L. Thijs, , Acta Mater, 58, pp.3303~ (2010)
- H. Attar, , Mater. Lett, 142, pp.38~ (2015)
- J. Suryawanshi, , Acta Mater, 115, pp.285~ (2016)
- P. Nandwana, , Curr, Opin, Soild State Mater. Sci, 21, pp.207~ (2017)
- H. T. Kim, , JWJ, 34, pp.62~ (2016)
- N. Read, , Mater. Des, 65, pp.417~ (2015)
- E. Louvis, , J. Mater. Process. Technol, 211, pp.275~ (2011)
- N. T. Aboulkhair, , Addit. Manuf., 1-4, pp.77~ (2014)
- 이규홍, "주조 A356 알루미늄 합금의 기계적 성질과 파괴인성에 미치는 공정 Si 입자의 영향", 대한금속·재료학회지, 45(1), pp.18~29 (2007), 대한금속·재료학회
- K. Kempen, , Physics Procedia, 39, pp.439~ (2012)
- N. O. Larrosa, , Theor. Appl. Fract. Mech, 98, pp.123~ (2018)