TiC 첨가량에 따른 개량된 A6013-3wt.%Si 합금 분말성형체의 미세조직 변화
The Effects of TiC Content on Microstructure of Modified A6013-3wt.%Si Alloy Powder Compact
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Aluminum-based powders have attracted attention as key materials for 3D printing owing to their low density, high specific strength, high corrosion resistance, and formability. This study describes the effects of TiC addition on the microstructure of the A6013 alloy. The alloy powder was successfully prepared by gas atomization and further densified using an extrusion process. We have carried out energy dispersive X-ray spectrometry (EDS) and electron backscatter diffraction (EBSD) using scanning electron microscopy (SEM) in order to investigate the effect of TiC addition on the microstructure and texture evolution of the A6013 alloy. The atomized A6013-xTiC alloy powder is fine and spherical, with an initial powder size distribution of approximately 73 μm which decreases to 12.5, 13.9, 10.8, and 10.0 μm with increments in the amount of TiC.
Abstract
Aluminum-based powders have attracted attention as key materials for 3D printing owing to their low density, high specific strength, high corrosion resistance, and formability. This study describes the effects of TiC addition on the microstructure of the A6013 alloy. The alloy powder was successfully prepared by gas atomization and further densified using an extrusion process. We have carried out energy dispersive X-ray spectrometry (EDS) and electron backscatter diffraction (EBSD) using scanning electron microscopy (SEM) in order to investigate the effect of TiC addition on the microstructure and texture evolution of the A6013 alloy. The atomized A6013-xTiC alloy powder is fine and spherical, with an initial powder size distribution of approximately 73 μm which decreases to 12.5, 13.9, 10.8, and 10.0 μm with increments in the amount of TiC.
참고문헌 (13)
- J. Hirsch, , Acta Materialia, 61, pp.818~ (2013)
- C. Rui, , Transactions of Nonferrous Metals Society of China, 24, pp.1645~ (2014)
- M. Elmadagli, , Wear, 262, pp.79~ (2007)
- L. Kloc, , Metall. Mater. Trans. A, 27, pp.3871~ (1996)
- H. K. Feng, , J. Mater. Process. Technol, 208, pp.330~ (2008)
- A. Ambrosi, , Chem. Soc. Rev, 45, pp.2740~ (2016)
- 김환태, "자동차 경량화를 위한 알루미늄 합금의 강변형 가공 및 고능률 용접기술에 관한 동향", 대한용접접합학회지, 34(4), pp.62~66 (2016), 대한용접접합학회[DOI]
- 엄영성, "AlSi10Mg 합금분말 크기가 선택적 레이저 용융된 3차원 조형체 특성에 미치는 영향", 한국분말재료학회지, 27(2), pp.103~110 (2020), 한국분말재료학회[DOI]
- Z. Y. Cai, , Transactions of Nonferrous Metals Society of China, 28, pp.1475~ (2018)
- S. J. Hong, , Mater, Trans, 51, pp.1055~ (2010)
- A. Bellosi, , J. Eur. Ceram. Soc, 9, pp.83~ (1992)
- X. Cui, , Mater. Des, 86, pp.397~ (2015)
- G. S. Upadhyaya, , Mater. Des, 22, pp.483~ (2001)