가스분무 공정에 의한 고강도 과공정 Al-Si 합금 분말의 제조 및 특성 연구Ⅱ. 압출재 제조 및 기계적 특성
Fabrication and Properties of High Strength Hypereutectic Al-Si Powders by a Gas Atomization ProcessⅡ. Extrusion and Mechanical Properties
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The hypereutectic Al-20 wt%Si powders including some amount of Cu, Fe, Mg, Mn were prepared by a gas atomization process. In order to get highly densified Al-Si bulk specimens, the as-atomized and sieved powders were extruded at 500℃. Microstructure and tensile properties of the extruded Al-Si alloys were investigated in this study. Relative density of the extruded samples was over 98%. Ultimate tensile strength (UTS) in stress-strain curves of the extruded powders increased after T6 heat treatments. Elongation of the samples was also increased from 1.4% to 3.2%. The fracture surfaces of the tested pieces showed a fine microstructure and the average grain size was about 1 μm.
Abstract
The hypereutectic Al-20 wt%Si powders including some amount of Cu, Fe, Mg, Mn were prepared by a gas atomization process. In order to get highly densified Al-Si bulk specimens, the as-atomized and sieved powders were extruded at 500℃. Microstructure and tensile properties of the extruded Al-Si alloys were investigated in this study. Relative density of the extruded samples was over 98%. Ultimate tensile strength (UTS) in stress-strain curves of the extruded powders increased after T6 heat treatments. Elongation of the samples was also increased from 1.4% to 3.2%. The fracture surfaces of the tested pieces showed a fine microstructure and the average grain size was about 1 μm.
참고문헌 (9)
- "Aluminum Industry Technology Roadmap" (2003), the Aluminum Association
- J. M. Torralba, , J. Materials Processing Technology, 133, pp.203~ (2003)
- "Automotive Light weighting Materials, FY 2002 Progress Report", ~ (2002)
- Z. J. Huang, , Materials Science and Engineering, 351, pp.15~ (2003)
- J.-C. Kim, , Materials Letters, 57, pp.1689~ (2003)
- H. Yamagata, , Materials Science Forum, 797, pp.304~ (1999)
- K. H. Min, , J. Korean Powder Metall. Inst, 10, pp.40~ (2003)
- M. S. Gong, , J. Korean Powder Metall. Inst, 11, pp.69~ (2004)
- Y. J. Kim, , J. Korean Powder Metall. Inst, 12, pp.296~ (2005)