API 2W Gr. 50 강재 용접부의 피로균열전파거동의 거시적 및 미시적 관찰
Marco and Microscopic Observations of Fatigue Crack Growth Behavior in API 2W Gr. 50 Steel Joints
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
It is well known that a considerable amount of scatter is shown in experimental results relating to fatigue crack growth even under identical and constant amplitude cyclic loading conditions. Moreover, flux cored arc welding (FCAW) is a common method used to join thick plates such as the structural members of large scale offshore structures and very large container ships. The objective of this study was to investigate the macro‐ and microscopic observations of the fatigue crack growth (FCG) behavior of the FCAWed API 2W Gr. 50 steel joints typically applied for offshore structures. In order to clearly understand the randomness of the fatigue crack growth behavior in the materials of three different zones, the weld metal (WM), heat affected zone (HAZ), and base metal (BM), experimental fatigue crack growth tests for each of five specimens were performed on ASTM standard compact tension (CT) specimens under constant amplitude cyclic loading. Special focus was placed on the fatigued fracture surfaces. As a result, a different behavior was observed at the macro‐level, depending on the type of material property: BM, HAZ, or WM.The variability in the fatigue crack growth rate for WM was higher than that of BM and HAZ.
Abstract
It is well known that a considerable amount of scatter is shown in experimental results relating to fatigue crack growth even under identical and constant amplitude cyclic loading conditions. Moreover, flux cored arc welding (FCAW) is a common method used to join thick plates such as the structural members of large scale offshore structures and very large container ships. The objective of this study was to investigate the macro‐ and microscopic observations of the fatigue crack growth (FCG) behavior of the FCAWed API 2W Gr. 50 steel joints typically applied for offshore structures. In order to clearly understand the randomness of the fatigue crack growth behavior in the materials of three different zones, the weld metal (WM), heat affected zone (HAZ), and base metal (BM), experimental fatigue crack growth tests for each of five specimens were performed on ASTM standard compact tension (CT) specimens under constant amplitude cyclic loading. Special focus was placed on the fatigued fracture surfaces. As a result, a different behavior was observed at the macro‐level, depending on the type of material property: BM, HAZ, or WM.The variability in the fatigue crack growth rate for WM was higher than that of BM and HAZ.
참고문헌 (16)
- 김선진, "피로균열전파저항의 변동성에 의한 균열전파율의해석", 대한기계학회논문집, 23(7), pp.1139~1146 (1999)
- 김선진, "일정 응력확대계수 제어하의 피로균열전파수명 분포의 파라메터 특성", 한국해양공학회지, 17(2), pp.54~59 (2003), 한국해양공학회
- 박희선, "조선용 극후물 강재 EH36 FCAW 용접부의 역학적 특성 고찰", 한국용접학회2008년도 추계학술대회 발표 초록, pp.123~ (2008)
- 손상훈, "피로균열전파의 확률모델과 통계적 양상", 2009년도 한국해양공학회 추계학술대회논문집, pp.573~576 (2009)
- 손혜정, "다층 플럭스코아드아크 용접한 API2W Gr.50 강재의 피로균열전파의 시험편간 변동", 2011년도 한국해양과학기술협의회 공동학술대회 논문집, pp.1616~1619 (2011)
- 임성우, "API 2W Gr.50 강재를 이용한 대형 Tubular Joint 피로성능평가", 한국해양공학회지, 19(3), pp.54~58 (2005), 한국해양공학회
- 임성우, "API 2W Gr.50 강재를 이용한 해양구조물 Tendon Porch의 피로성능 평가", 한국해양공학회지, 20(5), pp.82~88 (2006), 한국해양공학회
- 황세윤, "EH40과 API2W강재의 극 후판재 다층 FCAW 버트 접합부 잔류응력해석", 대한용접접합학회지, 28(3), pp.65~72 (2010), 대한용접접합학회
- Ashok, S., "Review and Extension of Compliance Information for Common Crack Growth Specimens", International Journal of Fracture, 14(5), pp.453~461 (1978)
- ASTM, "Standard test Method for Measurement of Fatigue Crack Growth Rates", American Society for Testing and Materials, ASTM E647-08, ~ (2008)
- Itagaki, H., "Experimental Estimation of the Probability Distribution of Fatigue Crack Growth Lives", Probabilistic Engineering Mechanics, 8(1), pp.25~34 (1993)
- Kazuyuki, S., "Welding Consumables for Offshore Structures", Technical Paper of Kobe Steel, 53(2), pp.85~89 (2003)
- Ortiz, K., "Time Series Analysis of fatigue Crack Growth Rate Data", Engineering Fracture Mechanics, 25(4), pp.657~668 (1986)
- Paris, P.C., "A Critical Analysis of Fatigue Crack Propagation Laws", ASME J. Basic Engineering, 56, pp.528~534 (1963)
- Virkler, D. A., "The Statistical Nature of Fatigue Crack Propagation", J. Engineering Materials and Technology, 101, pp.148~153 (1979), ASME
- Wu, W.F., "Statistical Aspects of Some Fatigue Crack Growth Data", Engineering Fracture Mechanics, 74, pp.2951~2963 (2007)