용접구조물의 부식피로수명에 미치는 용접부 개선처리 효과
Effect of Weld Improvement on the Corroded Fatigue Life of Welded Structures
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
The effect of weld improvement on the corroded fatigue life of welded structures was investigated. Toe grinding, TIG dressing and weld profiling were used as the geometric improvement methods. Fatigue tests under the corroded condition in artificial seawater were carried out to investigate the corrosion fatigue behavior of API 2W Gr.50T steel plate produced by POSCO. The test results in weld improved conditions were compared with those in as-welded condition. The test results were also compared with the design curves in UK DEn Class F. Corroded fatigue life of weld improved specimens was longer than that of as-welded specimen. Especially, the corroded fatigue life exceeded the mean SN curve in air of UK DEn Class F.
Abstract
The effect of weld improvement on the corroded fatigue life of welded structures was investigated. Toe grinding, TIG dressing and weld profiling were used as the geometric improvement methods. Fatigue tests under the corroded condition in artificial seawater were carried out to investigate the corrosion fatigue behavior of API 2W Gr.50T steel plate produced by POSCO. The test results in weld improved conditions were compared with those in as-welded condition. The test results were also compared with the design curves in UK DEn Class F. Corroded fatigue life of weld improved specimens was longer than that of as-welded specimen. Especially, the corroded fatigue life exceeded the mean SN curve in air of UK DEn Class F.
참고문헌 (10)
- ASM, "ASM Handbook", pp.905~ (1997), Corrosion
- Hara,M.Kawai, "Corrosion Fatigue Strength of 490 MPa Class High-Strength Steels Produced by the Thermo-Mechanical Control Process", OTC, 5311, pp.179~185 (1986)
- 김원범, "선체의 부식쇠모강판의 대기중 및 해수중 피로강도평가에 관한 연구", 대한조선학회 논문집, 43(4), pp.467~475 (2006), 대한조선학회
- Kirhope,K.J., "Detail Fatigue Life Improvement Techniques", pp.447~474 (1999), Marine Structure
- Kobatyashi,Y., "Corrosion Fatigue Strength of a Butt Welded Joint of a Ship Structural Steel in Synthetic Seawater", Journal of Japan Welding Society, 16(3), pp.382~387 (1998)
- Larrabee,C.P., "Steel Has Low Corrosion Rate During Long Sea Water Exposure", pp.95~96 (1962), Materials Protection, NACE
- Murphy,D.S.R., "Corrosion Fatigue Life of Cathodically Protected Tubular Joints of Offshore Structures", International Conference on Corrosion CONCORN, pp.390~397 (1997)
- Park,Y.K., "A Study on the Fatigue Characteristics at the Weldment by Spot Heating", the 16thInternational Offshore and Polar Engineering Conference, pp.106~111 (2006)
- Ummenhofer,T., "Concepts for Fatigue Design of Welds Improved by High Frequency Peening Methods", the 17th International Offshore and Polar Engineering Conference, pp.356~362 (2007)
- mm2-Class High Tensile Steel Plates, "Fatigue Strength in Seawater of High Heat-Input Welded Joints for TMCP Type 50kgf", pp.1985, Yajima,H.