용액 교반이 미세 패턴 내 무전해 구리 도금에 미치는 영향
The Effect of Solution Agitation on the Electroless Cu Deposition Within Nano-patterns
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The effect of solution agitation on the copper electroless deposition process of ULSI (ultra large scale integration) interconnections was investigated by using physical, electrochemical and electrical techniques. It was found that proper solution agitation was effective to obtain superconformal copper configuration within the trenches of 130~80 nm width. The transition of open potential during electroless deposition process showed that solution agitation induced compact structure of copper deposits by suppressing mass transfer of cuprous ions toward substrate. Also, the specific resistivity of copper layers was lowered by increasing agitation speed, which made the deposited copper particles smaller. Considering both copper deposit configuration and electric property, around 500 rpm of solution agitation was the most suitable for the homogeneous electroless copper filling within the ultra-fine patterns.
Abstract
The effect of solution agitation on the copper electroless deposition process of ULSI (ultra large scale integration) interconnections was investigated by using physical, electrochemical and electrical techniques. It was found that proper solution agitation was effective to obtain superconformal copper configuration within the trenches of 130~80 nm width. The transition of open potential during electroless deposition process showed that solution agitation induced compact structure of copper deposits by suppressing mass transfer of cuprous ions toward substrate. Also, the specific resistivity of copper layers was lowered by increasing agitation speed, which made the deposited copper particles smaller. Considering both copper deposit configuration and electric property, around 500 rpm of solution agitation was the most suitable for the homogeneous electroless copper filling within the ultra-fine patterns.
참고문헌 (15)
- J. J. Kim, , J. Vac. Sci. Technol, B 21, pp.33~ (2003)
- K. Weiss, , Microelectron. Eng, 50, pp.433~ (2000)
- T. Hara, , Electrochem. Solid-State Lett, 6, pp.C8~ (2003)
- G. Oskam, , J. Electrochem. Soc, 146, pp.1436~ (1999)
- T. P. Moffat, , J. Electrochem. Soc, 147, pp.4524~ (2000)
- S.-K. Kim, , Electrochem. Solid-State Lett, 8, pp.C19~ (2005)
- S. P. Muraka, , Mater. Sci. Eng, R19(3-4), pp.87~ (1997)
- T. Osaka, , J. Electrochem. Soc, 149, pp.573~ (2002)
- I. Koiwa, , J. Electrochem. Soc, 135, pp.1222~ (1998)
- M. Yoshino, , Electrochim. Acta, 51, pp.916~ (2005)
- J. H. Huang, , J. Electrochem. Soc, 148, pp.F133~ (2001)
- S. Ezhilvalavn, , Mater. Chem. Phys, 65, pp.227~ (2000)
- T. Aoyama, , Jpn. J. Appl. Phys. Part 1, 38, pp.2194~ (1999)
- M. Hasegawa, , Electrochem. Solid-State Lett, 9, pp.C138~C140 (2006)
- M. Hasegawa, , Appl. Phys. Lett, 90(10), pp.101916~ (2007)