SiO₂/ZnS:Cu/ZnS Triplex Layer Coatings for Phosphorescence Enhancement
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The objective of this study is to coat the SiO₂ layer uniformly on the ZnS:Cu phosphors by using Sol-Gel method. From results of SEM micrographs observation, XRD and XPS analysis, it could be confirmed that SiO₂ layer was relatively well coated on ZnS:Cu particles. Ag₂S was used as a decoding chemical to analyze the dense and uniform coating performance of SiO₂ layer on phosphor particles. It could be concluded that phosphors synthesized from our two step replacement method showed strong blue peak comparing to other method and rather weak green peak also. Obtained particle size of phosphors were about 20m diameter. Luminescence properties of the phosphors were examined by photoluminescence spectra at the excitation wavelength of 270 nm.
Abstract
The objective of this study is to coat the SiO₂ layer uniformly on the ZnS:Cu phosphors by using Sol-Gel method. From results of SEM micrographs observation, XRD and XPS analysis, it could be confirmed that SiO₂ layer was relatively well coated on ZnS:Cu particles. Ag₂S was used as a decoding chemical to analyze the dense and uniform coating performance of SiO₂ layer on phosphor particles. It could be concluded that phosphors synthesized from our two step replacement method showed strong blue peak comparing to other method and rather weak green peak also. Obtained particle size of phosphors were about 20m diameter. Luminescence properties of the phosphors were examined by photoluminescence spectra at the excitation wavelength of 270 nm.
참고문헌 (18)
- L. Qi, , Journal of Luminescence, 104, pp.261~ (2003)
- V. Dimitrova, , Thin Solid Films, 365, pp.134~ (2000)
- M. W. Wang, , Solid State Communications, 115, pp.493~ (2000)
- S. W. Lee, , Materials Science and Engineering: B, 103, pp.241~ (2003)
- L. X. Cao, , Spectroscopy and Spectral Analysis, 26, pp.2000~ (2006)
- J. Mu, , Materials Research Bulletin, 40, pp.2198~ (2005)
- L. Yang, , Journal of Hunan University, 34(4), pp.45~47 (2007)
- S. K. Panda, , Chemical Physics Letters, 440, pp.235~ (2007)
- S. D. Han, , Materials Chemistry and Physics, 103, pp.89~ (2007)
- Z. J. Li, , J. of Alloys and Compounds, 443, pp.16905~ (2007)
- W. Park, , Materials Science and Engineering: B, 76, pp.122~ (2000)
- Y. L. Lin, , Powder Technology, 123, pp.194~ (2002)
- C. F. Guo, , Journal of Luminescence, 105, pp.121~ (2003)
- J. Merikhi, , J. of Colloid and Interface Science, 228, pp.121~ (2000)
- Y. L. Yuan, , Materials Letters, 60, pp.1284~ (2006)
- Z. Q. Li, , Spectroscopy and Spectral Analysis, 25, pp.1730~ (2005)
- H. Y. Song, , Materials Science and Engineering: B, 143, pp.70~ (2007)
- Y. Su, , Materials Letters, 62, pp.3310~ (2008)