Luminescence properties of (Y, Zn)₂O₃: Eu³+ red phosphor as the effect of Zn ion
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
To enhance the luminescence properties, the red phosphor composed of (Y, Zn)₂O₃ : Eu³+ as doping concentration of Zn ion is synthesized at 1200℃ for 6 hrs in air atmosphere by conventional solid reaction method. As a result of the red phosphor (Y, Zn)₂O₃ : Eu³+ is measured X-ray diffraction (XRD), The main peak is nearly corresponded to the same as JCPDS card (No. 41-1105). When the doping concentration of Zn ion is more than 5 mol%, However, the ZnO peak is showed by XRD analysis. Therefore, when the doping concentration of Zn ion is less than 5 mol%, the Zn ion is well mixed in Y₂O₃structure without the impurity phases. The photoluminescence (PL) properties is shown as this phosphor is excited in 254 nmregion and the highest emission spectra of (Y, Zn)₂O₃ : Eu³+ has shown in 612 nm region because of a typical energy transition (5D0→7F2) of Eu³+ ion. As the doping concentration of Zn ion is more than 10 mol%, the emission peak is suddenly decreased. when the highest emission peak as doping concentration of Zn ion is shown, the composition of this phosphor is (Y0.95, Zn0.05)₂O₃ : Eu³+ 0.075 and the particle size analyzed by FE-SEM is confirmed from 0.4 to 3 μm.
Abstract
To enhance the luminescence properties, the red phosphor composed of (Y, Zn)₂O₃ : Eu³+ as doping concentration of Zn ion is synthesized at 1200℃ for 6 hrs in air atmosphere by conventional solid reaction method. As a result of the red phosphor (Y, Zn)₂O₃ : Eu³+ is measured X-ray diffraction (XRD), The main peak is nearly corresponded to the same as JCPDS card (No. 41-1105). When the doping concentration of Zn ion is more than 5 mol%, However, the ZnO peak is showed by XRD analysis. Therefore, when the doping concentration of Zn ion is less than 5 mol%, the Zn ion is well mixed in Y₂O₃structure without the impurity phases. The photoluminescence (PL) properties is shown as this phosphor is excited in 254 nmregion and the highest emission spectra of (Y, Zn)₂O₃ : Eu³+ has shown in 612 nm region because of a typical energy transition (5D0→7F2) of Eu³+ ion. As the doping concentration of Zn ion is more than 10 mol%, the emission peak is suddenly decreased. when the highest emission peak as doping concentration of Zn ion is shown, the composition of this phosphor is (Y0.95, Zn0.05)₂O₃ : Eu³+ 0.075 and the particle size analyzed by FE-SEM is confirmed from 0.4 to 3 μm.
참고문헌 (11)
- K. Kang, "Preparation for a new green-emitting phosphor for cold cathode fluorescent lamp", Journal of Luminescence, 122-123, pp.804~ (2007)
- S. Yin, "Synthesis and characterization of wire-like and near-spherical Eu2O3-doped Y2O3 phosphors by solvothermal reaction", Journal of Luminescence, 126, pp.427~ (2007)
- C.R. Ronda, "Phosphor for lamps and displays: an applicational view", Journal of Alloys and Compounds, 225, pp.534~ (1995)
- K.Y. Jung, "Cathodoluminescence characteristics of particles and film of (Y, Zn)2O3 : Eu 3+ phosphor prepared by spray pyrolysis", Journal of Luminescence, 127, pp.391~ (2007)
- T. Okumura, "Highly-efficient backlight for liquid crystal display having no optical films", Applied Physics Letters, 83, pp.13~ (2003)
- Z. Wang, "A potential red-emitting phosphor for LED solid-state lighting", Electrochemical and Solid-State Letters, 8(4), pp.33~ (2005)
- L. Robindro Singh, "Probing of surface Eu 3+ ions present in ZnO : Eu 3+ nanoparticles by covering ZnO : Eu core with Y2O3 shell: Luminescence study", Journal of Luminescence, 128, pp.1544~ (2008)
- S.H. Shin, "Cathodoluminescence change of Y2O3: Eu 3+ phosphor by incorporation of Zn ions", Solid State Communications, 135, pp.30~ (2005)
- S. Sakuma, "Effect of La and Zn addition on Y2O3 : Eu phosphors", Applied Surface Science, 244, pp.458~ (2005)
- S. Shinoya, "Phosphor Handbook" (1999), CRC Press
- 박우정, "Luminescence characterization of YVO₄: Eu³+, Bi³+ red phosphor by rapid microwave heating synthesis", 한국결정성장학회지, 18(4), pp.169~173 (2008), 한국결정성장학회