전해액 중 Sodium silicate의 농도에 따라 양극 산화된 AZ31B 마그네슘 합금 양극 피막의 특성 평가
Characteristic Evaluation of Anodic Film Depending on the Concentration of Sodium Silicate in the Electrolyte Anodized AZ31B Magnesium Alloy
3
조회
0
다운로드
2
인용
0
참고문헌
초록
Magnesium is one of the lightest metals, and magnesium alloys have excellent physical and mechanical properties such as high stiffness/weight ratios, good castability, good vibration and shock absorption. However their poor corrosion resistance, wear resistance, hardness and so on, have limited their application. To improve these defects, many techniques are developed. Micro arc oxidation(MAO) is a one of the surface treatments under anodic oxidation in which ceramic coating is directly formed on the surface of magnesium alloy. In this study, the characteristics of anodic film were examined after coating the AZ31B magnesium alloy through the MAO process. MAO was carried out in potassium hydroxide, potassium fluoride, and various concentration of sodium silicate in electrolyte. The morphology and chemical composition of the coating layer were characterized by SEM, XRD, EPMA and EDS. The hardness of anodic films was measured by micro-vickers hardness tester. As a result, the morphology and composition of anodic film were changed by concentration of sodium silicate. Thickness and Si composition of anodic film was increased with increasing concentration of sodium silicate in electrolyte. The hardness of anodic film was highly increased when the concentration of sodium silicate was above 40g/l in electrolyte.
Abstract
Magnesium is one of the lightest metals, and magnesium alloys have excellent physical and mechanical properties such as high stiffness/weight ratios, good castability, good vibration and shock absorption. However their poor corrosion resistance, wear resistance, hardness and so on, have limited their application. To improve these defects, many techniques are developed. Micro arc oxidation(MAO) is a one of the surface treatments under anodic oxidation in which ceramic coating is directly formed on the surface of magnesium alloy. In this study, the characteristics of anodic film were examined after coating the AZ31B magnesium alloy through the MAO process. MAO was carried out in potassium hydroxide, potassium fluoride, and various concentration of sodium silicate in electrolyte. The morphology and chemical composition of the coating layer were characterized by SEM, XRD, EPMA and EDS. The hardness of anodic films was measured by micro-vickers hardness tester. As a result, the morphology and composition of anodic film were changed by concentration of sodium silicate. Thickness and Si composition of anodic film was increased with increasing concentration of sodium silicate in electrolyte. The hardness of anodic film was highly increased when the concentration of sodium silicate was above 40g/l in electrolyte.
참고문헌 (16)
- D. L. Albright, "Life Cycle Inventory of Magnesium", 54th Annual World Magnesium Conference (1997)
- H. Tateishi, , Japan Inst. Light Metals, 48, pp.19~ (1998)
- S. Ono, , Electrochem. Soc., 143, pp.62~ (1996)
- A. K. Sharma, , Met. Finish., 91, pp.57~ (1993)
- O. Khaselev, , Electrochem. Soc., 146, pp.1757~ (1999)
- H.-I. Wu, , Surf. Sci., 253, pp.9387~ (2007)
- P. Bala Srinivasan, , Mater. Sci. Eng., A, 494, pp.401~ (2008)
- Liyuan Chai, , Corrosion Science, 50, pp.3274~ (2008)
- H. Duan, , Electrochim. Acta, 52, pp.5002~ (2007)
- D. Duly, , Actametal. Mater, 42, pp.3035~ (1994)
- D. Duly, , Actametal. Mater, 43, pp.101~ (1995)
- C. B. Wei, , Surface & Coatings Tech., 201, pp.5021~ (2007)
- C. Blawert, , Adv. Eng. Mater., 8, pp.511~ (2006)
- V. I. Belevantsev, , Prot. Met., 34, pp.469~ (1998)
- V. Brass, , J. Electrochem. Soc., 151, pp.B1~ (2004)
- H. F. Guo, , Appl. Surf. Sci., 252, pp.7911~ (2006)