Effects of Alloying Element and Heat Treatment on Properties of Cu-Ti Alloys
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Cu-Ti alloys with titanium in the range of 0.5-6.0wt% were developed to evaluate the effect of the titanium content and heat treatment on microstructure, hardness, and electrical conductivity. The hardness of the Ti-added copper alloys generally increased with the increase in titanium content and hardening was effective up to the 2.5wt%-Ti addition. Microstructural examination showed that the second phase of Cu4Ti started to precipitate out from the 3.0wt% Ti-addition, and the precipitate size and volume fraction increased with further Ti addition. Aging of the present Cu-Ti alloys at 450℃ for 1 h increased the hardness; however, the further aging up to 10 h did not much change the hardness. In the present study, it was inferred that in optimal Ti addition and aging condition Cu-Ti alloy could have the hardness and electrical conductivity values which are comparable to those of commercial Cu-Be alloy.
Abstract
Cu-Ti alloys with titanium in the range of 0.5-6.0wt% were developed to evaluate the effect of the titanium content and heat treatment on microstructure, hardness, and electrical conductivity. The hardness of the Ti-added copper alloys generally increased with the increase in titanium content and hardening was effective up to the 2.5wt%-Ti addition. Microstructural examination showed that the second phase of Cu4Ti started to precipitate out from the 3.0wt% Ti-addition, and the precipitate size and volume fraction increased with further Ti addition. Aging of the present Cu-Ti alloys at 450℃ for 1 h increased the hardness; however, the further aging up to 10 h did not much change the hardness. In the present study, it was inferred that in optimal Ti addition and aging condition Cu-Ti alloy could have the hardness and electrical conductivity values which are comparable to those of commercial Cu-Be alloy.
참고문헌 (12)
- A. A. Hameda, , Mater. Eng., A254, pp.83~ (1998)
- I. S. Batra, , Mater. Sci. Eng., A402, pp.118~ (2005)
- S. Nagarjuna, , Bull. Mater. Sci., 27, pp.69~ (2004)
- W. A. Soffa, , Prog. Mater. Sci., 49, pp.347~ (2004)
- I. S. Batra, , Mater. Sci. Eng., A, pp.360~ (2003)
- 오영주, "펄스전류인가가 황동-알루미나 나노복합도금층의 경도에 미치는 영향", 한국표면공학회지, 35(3), pp.158~164 (2002), 한국표면공학회
- S. Nagarjuna, , Acta Mater., 44, pp.2285~ (1996)
- S. Nagarjuna, , Mater. Sci. Eng., A313, pp.251~ (2001)
- S. Nagarjuna, , Mater. Sci. Eng., A335, pp.89~ (2002)
- R. Markandeya, , Mater. Sci. Eng., A404, pp.305~ (2005)
- T. B. Massalski, "Binary Alloy Phase Diagrams" (1990), ASM
- R. P. Elliott, "Constitution of Binary Alloys" (1965), McGraw- Hill