열처리가 Al-Mg 코팅 강판의 내식성에 미치는 영향
Effect of Heat Treatment on the Corrosion Resistance of the Al-Mg Coated Steel Sheet
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Double layer films which consisted of aluminum(Al) and magnesium(Mg) have been prepared by e-beam deposition. The structure, alloy phase, and corrosion resistance of the prepared films were investigated before and after heat treatment. The first (bottom) layer fixed with Al, and the thickness ratio between Al and Mg layers has been changed from 1 : 1 to 5 : 1, respectively. Total thickness of Al-Mg film was fixed at 3 μm. The cold-rolled steel sheet was used as a substrate. Heat treatment was fulfilled in an nitrogen atmosphere at the temperature of 400oC for 2, 3 and 10 min. Surface morphology of as-deposited Al-Mg film having Mg top layer showed plate-like structure. The morphology was not changed even after heat treatment. However, cross-sectional morphology of Al-Mg films was drastically changed after heat treatment, especially for the samples heat treated for 10 min. The morphology of as-deposited films showed columnar structure, while featureless structure of the films appeared after heat treatment. The x-ray diffraction data for as-deposited Al-Mg films showed only pure Al and Mg peaks. However, Al-Mg alloy peaks such as Al3Mg2 and Al12Mg17 appeared after heat treatment of the films. It is believed that the formation of Al-Mg alloy phase affected the structure change of Al-Mg film. It was found that the corrosion resistance of Al-Mg film was increased after heat treatment.
Abstract
Double layer films which consisted of aluminum(Al) and magnesium(Mg) have been prepared by e-beam deposition. The structure, alloy phase, and corrosion resistance of the prepared films were investigated before and after heat treatment. The first (bottom) layer fixed with Al, and the thickness ratio between Al and Mg layers has been changed from 1 : 1 to 5 : 1, respectively. Total thickness of Al-Mg film was fixed at 3 μm. The cold-rolled steel sheet was used as a substrate. Heat treatment was fulfilled in an nitrogen atmosphere at the temperature of 400oC for 2, 3 and 10 min. Surface morphology of as-deposited Al-Mg film having Mg top layer showed plate-like structure. The morphology was not changed even after heat treatment. However, cross-sectional morphology of Al-Mg films was drastically changed after heat treatment, especially for the samples heat treated for 10 min. The morphology of as-deposited films showed columnar structure, while featureless structure of the films appeared after heat treatment. The x-ray diffraction data for as-deposited Al-Mg films showed only pure Al and Mg peaks. However, Al-Mg alloy peaks such as Al3Mg2 and Al12Mg17 appeared after heat treatment of the films. It is believed that the formation of Al-Mg alloy phase affected the structure change of Al-Mg film. It was found that the corrosion resistance of Al-Mg film was increased after heat treatment.
참고문헌 (14)
- H. PARK, , Corrosion Science, 40, pp.525~ (1998)
- S. Khorsand, , Corrosion Science, 53, pp.2676~ (2011)
- P. Fellener, , Surf. Technol, 14, pp.101~ (1981)
- C. C. Yang, , Mater. Chem. Phys, 37, pp.355~ (1994)
- 정재인, "NdFeB 영구자석에의 Al", Al2O3 다층막 코팅 및 부식 특성, 2009, pp.42(2), 86~94[DOI]
- 박혜선, "빗각 증착으로 제조한 Al 박막의 특성", 한국표면공학회지, 45(3), pp.111~116 (2012), 한국표면공학회[DOI]
- G. S. Frankel, , J. Electrochem. Soc, 145, pp.2186~ (1998)
- K. R. Baldwin, , Corrosion Science, 38, pp.155~ (1996)
- J. E. Hatch, "Aluminum: Properties and Physical Metallurgy" (1984), American Society for Metal
- M. He, , Corrosion Science, 53, pp.1312~ (2011)
- X. Gu, , Chinese Journal of Materials Research, 23, pp.529~ (2009)
- 정재인, "전자빔 증발원을 이용한 물질의 증발 특성", 한국표면공학회지, 44(4), pp.155~164 (2011), 한국표면공학회
- J. L. Murray, , Bulletin of Alloy Phase Diagrams, 60 (1982)
- Yutaka S. Sato, , Scripta Materialia, 50, pp.1233~ (2004)