In this study, Mg films were prepared on hot dip aluminized steel (HDA) by using a sputtering method as a high corrosion resistance coating. The corrosion resistance of the Mg films was improved by controlling the morphology and the crystal structure of films by adjusting the Ar gas pressure during the coating process. Anodic polarization measurement results confirm that the corrosion resistance of the Mg films was affected by surface morphology and crystal structure. The corrosion resistance of the Mg coated HDA specimen increased with decreasing crystal size of the Mg coating and it was also improved by forming a film with denser morphology. The crystal structure oriented at Mg(101) plane showed the best corrosion resistance among crystal planes of the Mg metals, which is attributed to its relatively low surface energy. Neutral salt spray test confirmed that corrosion resistance of HDA can be greatly improved by Mg coating, which is superior to that of HDG (hot dip galvanized steel). The reason for the improvement of the corrosion resistance of Mg films on hot dip aluminized steel was due to the barrier effect by the Mg corrosion products formed by the corrosion of the Mg coating layer.
Abstract
In this study, Mg films were prepared on hot dip aluminized steel (HDA) by using a sputtering method as a high corrosion resistance coating. The corrosion resistance of the Mg films was improved by controlling the morphology and the crystal structure of films by adjusting the Ar gas pressure during the coating process. Anodic polarization measurement results confirm that the corrosion resistance of the Mg films was affected by surface morphology and crystal structure. The corrosion resistance of the Mg coated HDA specimen increased with decreasing crystal size of the Mg coating and it was also improved by forming a film with denser morphology. The crystal structure oriented at Mg(101) plane showed the best corrosion resistance among crystal planes of the Mg metals, which is attributed to its relatively low surface energy. Neutral salt spray test confirmed that corrosion resistance of HDA can be greatly improved by Mg coating, which is superior to that of HDG (hot dip galvanized steel). The reason for the improvement of the corrosion resistance of Mg films on hot dip aluminized steel was due to the barrier effect by the Mg corrosion products formed by the corrosion of the Mg coating layer.
참고문헌 (13)
- D.L. Piron, "The electrochemistry of corrosion" (1991)
- 정재인, "박막제조 기술의 동향과 전망", 한국자기학회지, 21(5), pp.185~192 (2011), 한국자기학회
- M.H. Lee, "Influence of interlayers on corrosion resistance of ion-plated Mg thin films", Surf. Coatings Technol, 202, pp.5603~5606 (2008)[DOI]
- F. Sanchette, "Nanostructured aluminium based coatings deposited by electronbeam evaporative PVD", Thin Solid Films, 518, pp.1575~1580 (2009)[DOI]
- J. Katoh, "CORROSION RESISTANCE OF VAPOR-DEPOSITED ZINC ALLOY COATED STEEL SHEETS", Recent Adv. Coat. Steels Used Automob, 16, pp.125~ (1996)
- 강재욱, "PVD법에 의해 제작한 Al-Mg 코팅 강판의 내식성에 미치는 Mg 함량 및 열처리의 영향", 한국표면공학회지, 49(2), pp.202~210 (2016), 한국표면공학회[DOI]
- 이명훈, "이온프레이팅법에 의한 Al-Mg 합금 코팅막의 제작과 내식성에 관한 연구", 한국마린엔지니어링학회지, 18, pp.157~164 (1994)
- P.J. Riley, "Anti corrosion treatment of aluminium or aluminium alloy surfaces" (1996)
- M. He, "Influence of microstructure on corrosion properties of multilayer Mg-Al intermetallic compound coating", Corros. Sci, 53, pp.1312~1321 (2011)[DOI]
- L. Liu, "Corrosion behaviour of Mg-rich Al coatings in the protection of Al alloys", Surf. Coatings Technol, 205, pp.332~337 (2010)[DOI]
- 이명훈, "물리증착법에 의해 제작한 마그네슘 박막의 형성기구와 내식특성", 한국마린엔지니어링학회지, 18, pp.178~187 (1994)
- S. Yamaguchi, "Composition and Corrosion Behavior of Hot-dip Al-Si-Mg Alloy Coated Steel Sheets", TETSU TO HAGANE-JOURNAL IRON STEEL Inst. JAPAN, 99, pp.25~32 (2013)
- J.I. Jeong, "Super anticorrosion of aluminized steel by a controlled Mg supply", Sci. Rep, 8, pp.3760~ (2018)[DOI]