천연해수 용액에서 STS 304와 용융 알루미늄 도금된 STS 304의 캐비테이션-침식 환경 하에서의 전기화학적 특성
Electrochemical Characteristics under Cavitation-Erosion Environment of STS 304 and Hot-Dip Aluminized STS 304 in Sea Water Solution
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
In this paper, the characteristics of a cavitation-erosion damage behavior on the STS 304 and hot-dip aluminized STS 304 under cavitation environment in sea water solution was investigated. The electrochemical experiments were carried out by potential measurement, anodic/cathodic polarization test, Tafel analysis, and also galvanostatic experiment in current density variables for the samples. The apparatus of cavitation-electrochemical experiment was manufactured in compliance with modified ASTM G-32 standard, with the conditions of sea water temperature of 25oC and the measurement, amplitude of 30 μm. The damage behavior was analyzed by an observation of surface mophologies and a measurement of damage depth by a scanning electron microscope(SEM) and a 3D microscope, respectively, after electrochemical test. After polarization experiment under cavitation environment, much higher damage depths for the hot-dip aluminized STS 304 were observed comparing to the untreated STS 304. In addition, higher corrosion current density in hotdip aluminized STS 304 presented than that of untreated STS 304 as a result of Tafel analysis.
Abstract
In this paper, the characteristics of a cavitation-erosion damage behavior on the STS 304 and hot-dip aluminized STS 304 under cavitation environment in sea water solution was investigated. The electrochemical experiments were carried out by potential measurement, anodic/cathodic polarization test, Tafel analysis, and also galvanostatic experiment in current density variables for the samples. The apparatus of cavitation-electrochemical experiment was manufactured in compliance with modified ASTM G-32 standard, with the conditions of sea water temperature of 25oC and the measurement, amplitude of 30 μm. The damage behavior was analyzed by an observation of surface mophologies and a measurement of damage depth by a scanning electron microscope(SEM) and a 3D microscope, respectively, after electrochemical test. After polarization experiment under cavitation environment, much higher damage depths for the hot-dip aluminized STS 304 were observed comparing to the untreated STS 304. In addition, higher corrosion current density in hotdip aluminized STS 304 presented than that of untreated STS 304 as a result of Tafel analysis.
참고문헌 (17)
- W. J. Cheng, "Effect of Chromium on the Formation of Intermetallic Phases in Hot-Dipped Aluminide Cr-Mo Steels", Appl. Surf. Sci, 277, pp.139~145 (2013)
- D. Hwangbo, "Corrosion Properties for Hot-Dip Aluminized Steel and 304 Stainless Steel", Corro. & Protec, 9, pp.61~66 (2010)
- H. H. Liu, "The Mechanism of Oxide Whisker Growth and Hot Corrosion of Hot-Dipped Al–Si Coated 430 Stainless Steels in Air-NaCl(g) Atmosphere", Appl. Surf. Sci, 257, pp.10645~10652 (2011)
- 송전영, "페라이트계 스테인리스강의 고온염 부식특성에 관한 연구", 한국마린엔지니어링학회지, 33(6), pp.860~866 (2009), 한국마린엔지니어링학회
- E. Frutos, "Oxidation Behavior of AISI 316 Steel Coated by Hot Dipping in an Al-Si Alloy", Surf. & Coat. Tech, 236, pp.188~199 (2013)
- 정상옥, "알루미늄 용융 도금된 304 스테인리스강의 해수 내 전기화학적 부식 특성 평가", 한국표면공학회지, 48(6), pp.354~359 (2015), 한국표면공학회[DOI]
- "Annual Book of ASTM Standards G32-92", ASTM International, 113~ (1992)
- U. R. Kattner, "Binary Alloy Phase Diagrams", pp.147~ (1990), ASM International
- W. Cheng, "Growth of Iintermetallic Layer in the Aluminide Mild Steel during Hot-Dipping", Surf. & Coat. Tech, 204, pp.824~828 (2009)
- S. Kobayashi, "Control of Intermetallic Compound Layers at Interface Between Steel and Aluminum by Diffusion-Treatment", Mater. Sci. Eng., A338, pp.44~53 (2002)
- M. V. Akdeniz, "The Role of Si Addition on the Interfacial Interaction in Fe-Al Diffusion Layer", Scripta Metallurgica et materilia, 31, pp.1723~1728 (1994)
- M. G. Fontana, "Corrosion Engineering" (1986), McGraw-Hill Book Company
- D. A. Jones, "Principles and Prevention of Corrosion", pp.80~ (2011), Prentice Hall
- G. Bregliozzi, "Cavitation Wear Behaviour of Austenitic Stainless Steels with Different Grain Sizes", Wear, 258, pp.503~510 (2005)
- 김성종, "5052-O 알루미늄 합금의 워터 캐비테이션 피닝 시간에 따른 표면 경화와 부식 특성에 관한 연구", CORROSION SCIENCE AND TECHNOLOGY, 11(4), pp.151~156 (2012), 한국부식방식학회
- S. J. Kim, "Electrochemical Characteristics under Cavitation-Erosion for STS 316L in Seawater", Mater. Res. Bulletin, 58, pp.244~247 (2014)
- 장석기, "해수 환경 하에서 304 스테인리스강의 캐비테이션 조건에 따른 특성 평가", 한국표면공학회지, 45(6), pp.278~283 (2012), 한국표면공학회[DOI]