주조 스테인리스강의 해양환경 하에서 플라즈마 이온질화 공정온도에 따른 부식특성 연구
Corrosion Characteristics of Cast Stainless Steel under Plasma Ion Nitriding Process Temperature in Marine Environment
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In order to improve corrosion resistance for cast stainless steel in seawater, the characteristics of corrosion resistance after plasma ion nitriding was investigated. Plasma ion nitriding process was conducted in a mixture of nitrogen of 25% and hydrogen of 75% at substrate temperature ranging from 350 to 500oC for 10 hours using pulsed-DC glow discharge plasma with working pressure of 250 Pa in vacuum condition. Corrosion tests were carried out for as-received and plasma ion nitrided specimens. The corrosion characteristics were investigated by measurement of weight loss and observation of surface morphology. In anodic polarization experiment, relatively less damage depth and weight loss were presented at a nitrided temperature of 400oC, attributing to the formation of S-phase.
Abstract
In order to improve corrosion resistance for cast stainless steel in seawater, the characteristics of corrosion resistance after plasma ion nitriding was investigated. Plasma ion nitriding process was conducted in a mixture of nitrogen of 25% and hydrogen of 75% at substrate temperature ranging from 350 to 500oC for 10 hours using pulsed-DC glow discharge plasma with working pressure of 250 Pa in vacuum condition. Corrosion tests were carried out for as-received and plasma ion nitrided specimens. The corrosion characteristics were investigated by measurement of weight loss and observation of surface morphology. In anodic polarization experiment, relatively less damage depth and weight loss were presented at a nitrided temperature of 400oC, attributing to the formation of S-phase.
참고문헌 (22)
- N. Nagata, "Environmentally assisted cracking of structural materials for light water reactors", NIMS Research Activities, 94, pp.1~31 (1994)
- E. C. Bain, "The nature and prevention of intergranular corrosion in austenitic stainless steels", Trans. ASM, 21, pp.481~509 (1933)
- D. A. Jones, "Principles and prevention", pp.334~ (1996), John Wiley & Sons
- A. Wahid, "Corrosion of Weldments, Metals Handbook, Vol 6", pp.1065~1069 (1993), ASM International
- 김대환, "A356 알루미늄 합금 슈퍼차저 하우징의 미세조직과 기계적 성질에 미치는 열처리의 영향", 한국주조공학회지, 32(5), pp.231~240 (2012), 한국주조공학회[DOI]
- 정호신, "오스테나이트계 스테인리스강의 용접성과 내식성에 미치는 합금원소의 영향(I) - 응고균열 감수성을 중심으로 -", 대한용접접합학회지, 30(3), pp.255~263 (2012), 대한용접접합학회
- 김국진, "셀 몰드 주조한 SSC13 엘보우 피팅 주강의 고용화율에 따른 델타 페라이트 분율 변화와 내부식특성", 한국주조공학회지, 35(5), pp.109~113 (2015), 한국주조공학회
- E. Menthe, "Further investigation of the structure and properties of austenitic stainless steel after plasma nitriding", Surf. Coatings Technol, 116-119, pp.199~204 (1999)
- R. R. M. De Sousa, "Nitriding using cathodic cage technique of martensitic stainless steel AISI 420 with addition of CH4", Revista Matéria, 13, pp.342~347 (2008)
- F. A. P. Fernandes, "Ion nitriding of a superaustenitic stainless steel:Wear and corrosion characterization", Surf. Coatings Technol, 204, pp.3087~3090 (2010)
- L. Nosei, "Corrosion behavior of ion nitrided AISI 316L stainless steel", Thin Solid Films, 516, pp.1044~1050 (2008)
- W. J. Yang, "Enhancement of mechanical property and corrosion resistance of 316 L stainless steels by low temperature arc plasma nitriding", Surf. Coatings Technol, 298, pp.64~72 (2016)
- A. Mendes, "Lowtemperature plasma nitriding of sintered PIM 316L austenitic stainless steel", Mater. Res, 17, pp.100~108 (2014)
- T. Nakanishi, "Effect of partial solution nitriding on mechanical properties and corrosion resistance in a type 316L austenitic stainless steel plate", Mater. Sci. Eng, 460-461, pp.186~194 (2007)
- T. Moskalioviene, "Modeling of nitrogen penetration in polycrystalline AISI 316L austenitic stainless steel during plasma nitriding", Surf. Coatings Technol, 205, pp.3301~3306 (2011)
- M. G Fontana, "Corrosion Engineering" (1996), McGraw-Hill Book Company
- Y. C. Lin, "Effect of Residual Stress on Thermal Fatigue in a Type 420Martensitic Stainless Steel Weldment", J. Mater. Processing Technol, 138, pp.22~27 (2003)
- 정상옥, "천연 해수에서 304 스테인리스강의 내식성에 미치는 DC glow 방전 플라즈마 이온질화처리 온도의 영향", 한국마린엔지니어링학회지, 41(3), pp.238~244 (2017), 한국마린엔지니어링학회[DOI]
- S. O. Chong, "Optimum temperature on corrosion resistance for plasma ion nitrided 316L stainless steel in sea water solution", Jpn. J. Appl. Phys, 56, pp.01AG04-1~01AG04-6 (2017)
- A. J. Sedriks, "Corrosion of Stainless Steels", pp.13~100 (1996), Wiley-Interscience
- G. P. Singh, "Phase formation in selected surface-roughened plasma-nitrided 304 austenite stainless steel", Sci. Technol. Adv. mater, 9, pp.1~5 (2008)
- Y. C. Lin, "Effect of residual stress on thermal fatigue in a type 420 martensitic stainless steel weldment", J. Mater. Proc. Technol, 138, pp.22~27 (2003)