Duplex Stainless Steel의 저온 플라즈마 침질탄화시 Pulse Frequency 및 Duty Factor에 따른 표면 특성평가
The Influence of Pulse Frequency and Duty Factor on Surface Characteristics during Low Temperature Plasma Nitrocarburizing Treatment of Duplex Stainless Steel
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
A low temperature plasma nitrocarburizng was implemented on the duplex stainless steel to achieve the enhancement of surface hardness without degradation of its corrosion resistance. Attempts were made to investigate the influence of Pulse frequency and Duty factor of pulsed power in a high Pulse frequency regime on the surface characteristics of the hardened layer. The hardened layer (S-phase) was formed on all of the treated surfaces. Surface hardness reached up to 1300 HV0.1 which is about 4.6 times higher than that of the untreated material (280 HV0.1). The thickness of the hardened layer tends to increase lightly with the higher Pulse frequency and the higher Duty factor. The corrosion resistance of nitrocarburized duplex stainless steel was almost similar to that of the untreated material. Both the Pulse frequency and the Duty factor do not have a significant influence on the corrosion property of plasma treated duplex stainless steel.
Abstract
A low temperature plasma nitrocarburizng was implemented on the duplex stainless steel to achieve the enhancement of surface hardness without degradation of its corrosion resistance. Attempts were made to investigate the influence of Pulse frequency and Duty factor of pulsed power in a high Pulse frequency regime on the surface characteristics of the hardened layer. The hardened layer (S-phase) was formed on all of the treated surfaces. Surface hardness reached up to 1300 HV0.1 which is about 4.6 times higher than that of the untreated material (280 HV0.1). The thickness of the hardened layer tends to increase lightly with the higher Pulse frequency and the higher Duty factor. The corrosion resistance of nitrocarburized duplex stainless steel was almost similar to that of the untreated material. Both the Pulse frequency and the Duty factor do not have a significant influence on the corrosion property of plasma treated duplex stainless steel.
참고문헌 (7)
- 안용식, "22Cr 린 듀플렉스 스테인리스강의 공식저항성에 미치는 Mn 과 Ni 첨가의 영향", 한국동력기계공학회지, 16(5), pp.76~82 (2012), 한국동력기계공학회
- 장휘운, "화학적 부동태 처리에 따른 듀플렉스 스테인리스 강의 피막 특성에 관한 연구", 한국표면공학회지, 45(6), pp.219~225 (2012), 한국표면공학회[DOI]
- 이인섭, "AISI 316L stainless steel에 저온 플라즈마 침탄 및 질화처리 시 가스조성이 표면특성에 미치는 영향", 한국표면공학회지, 42(3), pp.116~121 (2009), 한국표면공학회
- T. Bell, , Vacuum, 59, pp.14~ (2000)
- D. Song, , J. Kor. Mater. Res, 11(12), pp.1063~ (2001)
- B. Y. Jeong, , Surf. Coat. Tech, 137, pp.249~ (2001)
- T. Wierzchon, , Vacuum, 48(6), pp.499~ (1997)