선택적 금속 전착에 대한 전해질 온도 및 전류밀도 영향분석
The Characteristics of Electrolyte Temperature and Current Density on Selective Jet Electrodeposition
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
A metal 3D printer has been developed on its own to electrodeposit the localized area. Nozzles were used to selectively laminate the electrolytic plating method. To analyze the factors affecting the deposition, the stack height, thickness and surface roughness were experimentally analyzed according to the current density and the temperature of the electrolyte. Electrolytic temperature and current are electrodeposited when the deposition conditions are dominant over the etching conditions, but the thickness is kept constant. On the contrary, when the etching conditions are dominant, the electrodeposited shape is rather the etched. As a result, the uniformity of surface quality and electrodeposition rate could be improved by conducting experiments under constant conditions of electrolyte temperature and current density.
Abstract
A metal 3D printer has been developed on its own to electrodeposit the localized area. Nozzles were used to selectively laminate the electrolytic plating method. To analyze the factors affecting the deposition, the stack height, thickness and surface roughness were experimentally analyzed according to the current density and the temperature of the electrolyte. Electrolytic temperature and current are electrodeposited when the deposition conditions are dominant over the etching conditions, but the thickness is kept constant. On the contrary, when the etching conditions are dominant, the electrodeposited shape is rather the etched. As a result, the uniformity of surface quality and electrodeposition rate could be improved by conducting experiments under constant conditions of electrolyte temperature and current density.
참고문헌 (8)
- Berman, B., "3-D Printing: The New Industrial Revolution", Bus. Horiz, pp.155~162 (2012)
- Nandwana, P., "Powder bed binder jet 3D printing of Inconel 718:Densification, microstructural evolution and challenges", Curr. Opin. Solid State and Mater. Sci., pp.207~218 (2017)
- Fletcher, J. C., "Scanning Nozzle Plating System", U.S Patent 3,810,829, ~ (1974)
- S.K. Seol, "Electrodeposition-based 3D printing of metallic microacrchitectures with controlled interanl structure", nano micro small, 11(32), pp.3896~3902
- J.U. Park, "High-resolution electrohydrodynamic jet printing", nature materials, 6, pp.782~789 (2007)
- Frederick, C. S., "Faraday’s Laws in One Equation", j. Chem. Educ, 38, pp.98~ (1961)
- "Nomenclature for Transport Phenomena in Electrolytic Systems", pp.1836~1839 (1981), Pergamon Press Ltd
- Matula, R. A, "Electrical Resistivity of Copper, Gold, Palladium, and Silver", J. Phys. Chem. Ref. Data, pp.1147~1298 (1979)