24개월 대기 노출된 Al1050 및 Al7075 알루미늄 합금 산화막에 대한 투과전자현미경 분석
TEM Analysis on Oxide Films of Al1050 and Al7075 Exposed to 24-month Atmospheric Conditions
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Al1050 and Al7075 alloy specimens were exposed to atmospheric conditions for 24 months and analyzed by Transmission Electron Microscopy to characterize their corrosion behavior and oxide film characteristics, especially focusing on intergranular corrosion or oxidation. In general, the intergranular oxygen penetration depth of Al1050 was deeper than Al7075. Since O and Si signals were overlapped at the oxidized grain boundaries of Al1050 and Mg is not included in Al1050, it is concluded that Si segregated along the grain boundaries directly impacts on the intergranular corrosion of Al1050. Cr-Si or Mg-Si intermetallic particles were not observed along the grain boundaries of Al7050, but Mg-Si particle was barely observed in the matrix. 10-nm size Mg-Zn particles were also found all over the matrix. Mg was mainly observed along the oxidized grain boundary of Al7075, but Si was not detected due to the Mg-Si particle formation in the matrix and relatively low concentration of Si in Al7075. Therefore, it is thought that Mg plays an important role in the intergranular corrosion of Al7075 under atmospheric corrosion conditions.
Abstract
Al1050 and Al7075 alloy specimens were exposed to atmospheric conditions for 24 months and analyzed by Transmission Electron Microscopy to characterize their corrosion behavior and oxide film characteristics, especially focusing on intergranular corrosion or oxidation. In general, the intergranular oxygen penetration depth of Al1050 was deeper than Al7075. Since O and Si signals were overlapped at the oxidized grain boundaries of Al1050 and Mg is not included in Al1050, it is concluded that Si segregated along the grain boundaries directly impacts on the intergranular corrosion of Al1050. Cr-Si or Mg-Si intermetallic particles were not observed along the grain boundaries of Al7050, but Mg-Si particle was barely observed in the matrix. 10-nm size Mg-Zn particles were also found all over the matrix. Mg was mainly observed along the oxidized grain boundary of Al7075, but Si was not detected due to the Mg-Si particle formation in the matrix and relatively low concentration of Si in Al7075. Therefore, it is thought that Mg plays an important role in the intergranular corrosion of Al7075 under atmospheric corrosion conditions.
참고문헌 (20)
- ASM International, "ASM Handbook Vol 13A Corrosion: Fundamentals, Testing, and Protection", 196~209 (2003)
- T. F. Otero, "Prediction of Pitting Probability on 1050 Aluminum in Environmental Conditions", Corrosion, 48, pp.785~791 (1992)
- S. Sun, "Long-term atmospheric corrosion behaviour of aluminium alloys 2024 and 7075 in urban, coastal and industrial environments", Corros. Sci, 51, pp.719~727 (2009)
- T. Zhang, "Long-Term Atmospheric Corrosion of Aluminum Alloy 2024-T4 in a Coastal Environment", J. Mater. Eng. Perform, 24, pp.2764~2773 (2015)
- X. K. Yang, "Properties degradation and atmospheric corrosion mechanism of 6061aluminum alloy in industrial and marine atmosphere environments", Mater. Corros, 68, pp.529~535 (2017)
- M. Poltavtseva, "Long term corrosion behavior of clad aluminum materials under different atmospheric conditions", Mater. Corros, 64, pp.723~730 (2013)
- J. Ryl, "Effect of native airformed oxidation on the corrosion behavior of AA 7075 aluminum alloys", Corros. Sci, 87, pp.150~155 (2014)
- 김영식, "Corrosion Cost and Corrosion Map of Korea - Based on the Data from 2005 to 2010", CORROSION SCIENCE AND TECHNOLOGY, 10(2), pp.52~59 (2011), 한국부식방식학회
- 김선규, "대기 부식에 의해 생성된 Al1050 및 Al7075 알루미늄 합금 산화막에 대한 투과전자현미경 분석", 한국표면공학회지, 50(6), pp.447~454 (2017), 한국표면공학회[DOI]
- S. P. Knight, "The study of intergranular corrosion in aircraft aluminium alloys using X-ray tomography", Corros. Sci, 53, pp.727~734 (2011)
- Yoshiyuki Oya, "Influence of Silicon on Intergranular Corrosion for Aluminum Alloys", MATERIALS TRANSACTIONS, 54(7), pp.1200~1208 (2013)
- Binger, W. W, "Aluminium Vol. I", pp.209~ (1967), ASM
- M. Kaifu, "Influence of Mn contents and heat treatments on intergranular corrosion of Al-Mn alloys", J. Japan Inst. Met, 32, pp.135~142 (1982)
- M. Zamin, "The Role of Mn in the Corrosion Behavior of Al-Mn Alloys", Corrosion, 37, pp.627~632 (1981)
- A. K. Bhattamishra, "Microstructural studies on the effect of Si and Cr on the intergranular corrosion in Al-Mg-Si alloys", Materials & Design, 18(1), pp.25~28 (1997)
- Y. Zheng, "Study of the Precipitation Hardening Behavior and Intergranular Corrosion of Al-Mg-Si Alloys with Differing Si Contents", Metals, 7, pp.387~ (2017)
- J. R. Galvele, "Mechanism of intergranular corrosion of Al-Cu alloys", Corros. Sci, 10, pp.795~807 (1970)
- Y. Zou, "The intergranular corrosion behavior of 6000-series alloys with different Mg", Si and Cu content, 2017, pp.405, 489~496
- American Society for Testing and Materials (ASTM) International, "ASTM G50-10 Standard Practice for Conducting Atmospheric Corrosion Tests on Metals", ~ (2010)
- M. Navaser, "Effect of Friction Stir Processing on Pitting Corrosion and Intergranular Attack of 7075 Aluminum Alloy", J. Mater. Sci. Tech, 33, pp.155~165 (2017)