대기 노출된 Al2024 알루미늄 합금 산화막에 대한 미세조직 분석
Microstructural Analysis on Oxide Film of Al2024 Exposed to Atmospheric Conditions
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Al2024 aluminum alloy specimens were exposed to atmospheric conditions for maximum 24 months and analyzed by electron microscopes to characterize their corrosion behavior and oxide film characteristics. As the exposure time increased from 12 months to 24 months, the number of pitting sites per 1 mm2 increased from ~100 to ~200. The uniform oxidation (or non-pitting) region of the 12-month exposure specimen showed 30~120 nm thick oxide layer, whereas the 24-month exposure specimen showed 170~200 nm thick oxide with the local oxygen penetration region up to 1 μm deep. There was no local corrosion area observed in the 12-month exposure specimen except pitting. However, in the 24-month exposure specimen, local oxygen penetration region was observed beneath the uniform oxide layer and near the pitting cavity. Al2024 showed two times thicker uniform oxide layer but much shallower local oxygen penetration region than Al1050, which appears to be related to low Si concentration. Further research is needed on the effects of Mg segregation near the tip of the oxygen penetration region.
Abstract
Al2024 aluminum alloy specimens were exposed to atmospheric conditions for maximum 24 months and analyzed by electron microscopes to characterize their corrosion behavior and oxide film characteristics. As the exposure time increased from 12 months to 24 months, the number of pitting sites per 1 mm2 increased from ~100 to ~200. The uniform oxidation (or non-pitting) region of the 12-month exposure specimen showed 30~120 nm thick oxide layer, whereas the 24-month exposure specimen showed 170~200 nm thick oxide with the local oxygen penetration region up to 1 μm deep. There was no local corrosion area observed in the 12-month exposure specimen except pitting. However, in the 24-month exposure specimen, local oxygen penetration region was observed beneath the uniform oxide layer and near the pitting cavity. Al2024 showed two times thicker uniform oxide layer but much shallower local oxygen penetration region than Al1050, which appears to be related to low Si concentration. Further research is needed on the effects of Mg segregation near the tip of the oxygen penetration region.
참고문헌 (24)
- ASM International, "ASM Handbook Vol 13A Corrosion: Fundamentals, Testing, and Protection", 196~209 (2003)
- N. D. Alexopoulos, "Accelerated corrosion exposure in ultra thin sheets of 2024 aircraft aluminum alloy for GLARE applications", Corro. Sci, 55, pp.289~300 (2012)
- S. Sun, "Long-term atmospheric corrosion behaviour of aluminium alloys 2024 and 7075 in urban, coastal and industrial environments", Corros. Sci, 51, pp.719~727 (2009)
- B. B. Wang, "Atmospheric corrosion of aluminum alloy 2024-T3 exposed to salt lake environment in Western China", Corros. Sci, 59, pp.63~70 (2012)
- S. Sun, "Exfoliation Corrosion of Extruded AA2024-T4 in the Industrial and Coastal-Industrial Environment", Corrosion, 70, pp.1064~1073 (2014)
- T. Zhang, "Long-Term Atmospheric Corrosion of Aluminum Alloy 2024-T4 in a Coastal Environment", J. Mater. Eng. Perform, 24, pp.2764~2773 (2015)
- S. Zhang, "Long-term atmospheric corrosion of aluminum alloy 2024-T4 in coastal environment : Surface and sectional corrosion behavior", J. Alloys Comp, 789, pp.460~471 (2019)
- T. F. Otero, "Prediction of Pitting Probability on 1050 Aluminum in Environmental Conditions", Corrosion, 48, pp.785~791 (1992)
- X. K. Yang, "Properties degradation and atmospheric corrosion mechanism of 6061 aluminum alloy in industrial and marine atmosphere environments", Mater. Corros, 68, pp.529~535 (2017)
- M. Poltavtseva, "Long term corrosion behavior of clad aluminum materials under different atmospheric conditions", Mater. Corros, 64, pp.723~730 (2013)
- J. Ryl, "Effect of native air-formed oxidation on the corrosion behavior of AA 7075 aluminum alloys", Corros. Sci, 87, pp.150~155 (2014)
- S. P. Knight, "The study of intergranular corrosion in aircraft aluminium alloys using X-ray tomography", Corros. Sci, 53, pp.727~734 (2011)
- Yoshiyuki Oya, "Influence of Silicon on Intergranular Corrosion for Aluminum Alloys", MATERIALS TRANSACTIONS, 54(7), pp.1200~1208 (2013)
- Binger, W. W., "In Aluminium Vol. I", pp.209~ (1967), ASM
- M. Kaifu, "Influence of Mn contents and heat treatments on intergranular corrosion of Al-Mn alloys", J. Japan Inst. Met, 32, pp.135~142 (1982)
- M. Zamin, "The Role of Mn in the Corrosion Behavior of Al-Mn Alloys", Corrosion, 37, pp.627~632 (1981)
- Y. Zheng, "Study of the Precipitation Hardening Behavior and Intergranular Corrosion of Al-Mg-Si Alloys with Differing Si Contents", Metals, 7(10), pp.387~ (2017)
- J. R. Galvele, "Mechanism of intergranular corrosion of Al-Cu alloys", Corros. Sci, 10, pp.795~807 (1970)
- Y. Zou, "The intergranular corrosion behavior of 6000-series alloys with different Mg", Si and Cu content, 2017, pp.405, 489~496
- 김영식, "Corrosion Cost and Corrosion Map of Korea - Based on the Data from 2005 to 2010", CORROSION SCIENCE AND TECHNOLOGY, 10(2), pp.52~59 (2011), 한국부식방식학회
- 김선규, "대기 부식에 의해 생성된 Al1050 및 Al7075 알루미늄 합금 산화막에 대한 투과전자현미경 분석", 한국표면공학회지, 50(6), pp.447~454 (2017), 한국표면공학회[DOI]
- 김대건, "24개월 대기 노출된 Al1050 및 Al7075 알루미늄 합금 산화막에 대한 투과전자현미경 분석", 한국표면공학회지, 52(2), pp.62~71 (2019), 한국표면공학회[DOI]
- American Society for Testing and Materials (ASTM) International, "ASTM G50-10Standard Practice for Conducting Atmospheric Corrosion Tests on Metals", ~ (2010)
- Z. Cui, "Atmospheric corrosion behavior of 2A12 aluminum alloy in a tropical marine environment", Advances Mater. Sci. Eng (2015)