시편의 준비 방법 및 접촉저항이 알루미늄 합금의 아노다이징 피막 형성에 미치는 영향
Effects of specimen preparation method and contact resistance on the formation of anodizing films on aluminum alloys
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, five different specimen preparation methods were introduced and their advantages and disadvantages were presented. One of them, an epoxy mounting method has advantages of constant exposure area, ease of surface preparation without touching the specimen surface during polishing or cleaning, use of small amount of material and ease of specimen reuse by polishing or etching. However, in order to eliminate unexpected errors resulting from preferable reaction at the specimen/epoxy interface and contact resistance between the specimen and copper conducting line for electrical connection, it is recommended to cover the wall side of the specimen with porous anodic oxide films and to remain the contact resistance lower than 1 ohm. The increased contact resistance between the specimen and Cu conducting line appeared to result in increases of anodizing voltage and solution temperature during anodizing by which thickness and hardness of anodizing film on Al2024 alloy were drastically decreased and color of the films became more brightened.
Abstract
In this study, five different specimen preparation methods were introduced and their advantages and disadvantages were presented. One of them, an epoxy mounting method has advantages of constant exposure area, ease of surface preparation without touching the specimen surface during polishing or cleaning, use of small amount of material and ease of specimen reuse by polishing or etching. However, in order to eliminate unexpected errors resulting from preferable reaction at the specimen/epoxy interface and contact resistance between the specimen and copper conducting line for electrical connection, it is recommended to cover the wall side of the specimen with porous anodic oxide films and to remain the contact resistance lower than 1 ohm. The increased contact resistance between the specimen and Cu conducting line appeared to result in increases of anodizing voltage and solution temperature during anodizing by which thickness and hardness of anodizing film on Al2024 alloy were drastically decreased and color of the films became more brightened.
참고문헌 (13)
- 정용수, "실용표면처리기술시리즈 제 5권 양극산화", pp.5~ (2014), 화신문화(주)
- 문성모, "금속의 양극산화처리 기술", 한국표면공학회지, 51(1), pp.1~11 (2018), 한국표면공학회[DOI]
- 문상혁, "6xxx계 알루미늄 합금의 경질 아노다이징 피막 형성 특성 연구", 한국표면공학회지, 52(4), pp.203~210 (2019), 한국표면공학회[DOI]
- 문성모, "황산 용액에서 Al6061 합금의 아노다이징 피막 형성거동", 한국표면공학회지, 51(6), pp.393~399 (2018), 한국표면공학회[DOI]
- S. Moon, "Growth of anodic oxide films on AC2A alloy in sulphuric acid solution", Corrosion Science, 53, pp.1547~1155 (2011)
- T. Aerts, "Influence of the anodizing temperature on the porosity and the mechanical properties of the porous anodic film", Surf. Coat. Technol, 201, pp.7310~7317 (2007)
- S. -M. Moon, "Growth Mechanism of Anodic Oxide Film on Pure Aluminium in Acidic and Alkaline Solutions", J. of Solid State Electrochemistry, 2, pp.156~161 (1998)
- S. -M. Moon, "A review of Al anodizing", J. Corros. Sci. Soc. of Korea, 26, pp.498~508 (1997)
- Y. -S. Kim, "The Effects of Applied Potential and pH on the Electrochemical Dissolution of Barrier Layer in Porous Anodic Oxide Film on Pure Aluminium", Corrosion Science, 38, pp.329~336 (1996)
- G. Knörnschild, "Effect of the anodization conditions on the growth and volume expansion of porous alumina films in malonic acid electrolyte", Surface and Coatings Technology, 275, pp.17~25 (2015)
- Daiki Nakajima, "Growth behavior of anodic oxide formed by aluminum anodizing in glutaric and its derivative acid electrolytes", Applied Surface Science, 321, pp.364~370 (2014)
- Y. Ma, "Anodic film growth on Al–Li–Cu alloy AA2099-T8", Electrochim. Acta, 80, pp.148~159 (2012)
- E. Matykina, "Plasma electrolytic oxidation of pre-anodized aluminium", Corrosion Science, 51, pp.2897~2905 (2009)