RF 스퍼터링과 이온소스 복합방식에 의한 플라스틱사출금형(SKD11)의 DLC막 응용
The Application of DLC(diamond-like carbon) Film for Plastic Injection Mold by Hybrid Method of RF Sputtering and Ion Source
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
DLC film was synthesized on plastic injection mold(SKD11, 30 mm×19 mm×0.5 mm) and Si(100) wafer for 2 h at 130 ℃ under 6 mTorr using hybrid method of rf sputtering and ion source. The obtained film was analysed by Raman spectroscopy, AFM, TEM, Nano indenter and scratch tester, etc. The film was defined as an amorphous phase. In the Raman spectrum, broad peak of sp2-bonded carbon attributed to graphite at 1550 cm-1 were observed, and the ratio of ID(sp3 diamond intensity)/IG(sp2 graphite intensity) was approximately 0.54. The adhesion of DLC film was more than 80 N with scratch tester when 0.2 μm thickness Cr was coated as interlayer. The micro-hardness was distributed at 35~37 GPa. The friction coefficient was 0.02~0.07, and surface roughness(Ra) was 0.34~1.64 nm. The lifetime of DLC coated plastic injection mold using as a connector part in computer was more than 2 times of non-coated mold.
Abstract
DLC film was synthesized on plastic injection mold(SKD11, 30 mm×19 mm×0.5 mm) and Si(100) wafer for 2 h at 130 ℃ under 6 mTorr using hybrid method of rf sputtering and ion source. The obtained film was analysed by Raman spectroscopy, AFM, TEM, Nano indenter and scratch tester, etc. The film was defined as an amorphous phase. In the Raman spectrum, broad peak of sp2-bonded carbon attributed to graphite at 1550 cm-1 were observed, and the ratio of ID(sp3 diamond intensity)/IG(sp2 graphite intensity) was approximately 0.54. The adhesion of DLC film was more than 80 N with scratch tester when 0.2 μm thickness Cr was coated as interlayer. The micro-hardness was distributed at 35~37 GPa. The friction coefficient was 0.02~0.07, and surface roughness(Ra) was 0.34~1.64 nm. The lifetime of DLC coated plastic injection mold using as a connector part in computer was more than 2 times of non-coated mold.
참고문헌 (11)
- 김미선, , 한국표면공학회 추계학술발표회 초록집, pp.164~ (2007), 한국표면공학회
- G. J. Vadentop, , J. Vac. Sci. Technol, A9, pp.1157~ (1991)
- N. Savvides, , J. Appl. Phys., 59, pp.4133~ (1986)
- B. A. Banks, , J. Vac. Sci. Technol., 21, pp.807~ (1982)
- C. B. Collins, , Appl. Phys. Lett., 54, pp.216~ (1989)
- W. D. Munz, , Surf. Coat. Technol., 48, pp.81~ (1991)
- W. D. Sproul, , Surf. Coat. Technol., 61, pp.139~ (1993)
- J. A. Thornton, "Thin Film Process", pp.75~ (1978), Academic Press
- S. Schiller, , Thin Solid Films, 40, pp.327~ (1977)
- J. A. Thornton, , J. Vac. Sci. Technol., 46, pp.267~ (1997)
- W. D. Davis, , J. Appl. Phys., 40, pp.2212~ (1969)