Metal PCB에 있어서 양극산화법으로 제작한 Al2O3절연막의 방열특성
Heat dissipation of Al2O3 Insulation layer Prepared by Anodizing Process for Metal PCB
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
High efficiency LED device is being concerned due to its high heat loss, and such heat loss will cause a shorter lifespan and lower efficiency. Since there is a demand for the materials that can release heat quickly into the external air, the organic insulating layer was required to be replaced with high thermal conductive materials such as metal or ceramics. Through anodizing the upper layer of Al, the Breakdown Voltage of 3kV was obtained by using an uniform thickness of 60 μm aluminum oxide(Al2O3) and was carried out to determine the optimum process conditions when thermal cracking does not occur. Two Ni layers were formed above the layer of Al2O3 by sputtering deposition and electroplating process, and saccharin was added for the purpose of minimizing the remain stress in electroplating process. The results presented that the 3-layer film including the Ni layer has an adhesive force of 10N and the thermal conductivity for heat dissipation is achieved by 150W/mK level, and leads to improvement about 7 times or above in thermal conductivity, as opposed to the organic insulation layer.
Abstract
High efficiency LED device is being concerned due to its high heat loss, and such heat loss will cause a shorter lifespan and lower efficiency. Since there is a demand for the materials that can release heat quickly into the external air, the organic insulating layer was required to be replaced with high thermal conductive materials such as metal or ceramics. Through anodizing the upper layer of Al, the Breakdown Voltage of 3kV was obtained by using an uniform thickness of 60 μm aluminum oxide(Al2O3) and was carried out to determine the optimum process conditions when thermal cracking does not occur. Two Ni layers were formed above the layer of Al2O3 by sputtering deposition and electroplating process, and saccharin was added for the purpose of minimizing the remain stress in electroplating process. The results presented that the 3-layer film including the Ni layer has an adhesive force of 10N and the thermal conductivity for heat dissipation is achieved by 150W/mK level, and leads to improvement about 7 times or above in thermal conductivity, as opposed to the organic insulation layer.
참고문헌 (15)
- Z. G. Piao, , J. of Advanced Engineering and Technology, 2, pp.165~ (2009)
- J. Hu, , J. Phys. D:Appl. Phys, 41, pp.035107~ (2008)
- M. H. Shin, "Introduction to LED Packaging Technology", pp.289~ (2008), Bookshill co
- Se-Yeon Jung, "Improved Light Output Power of GaN-Based Flip-Chip Light-Emitting Diode Through SiO2 Cones", Electronic Materials Letters, 8(6), pp.549~552 (2012), 대한금속·재료학회[DOI]
- J. C. Hsieh, , IEEE Transaction on Electron Devices, 58, pp.1141~ (2011)
- L. Kim, , IEEE Transactions on Components and Packaging Technologies, 30, pp.897~ (2007)
- H. H. Kim, , Microelectron. Reliab, 48, pp.445~ (2008)
- 고민관, "LED 패키지 솔더 접합부의 기계적 신뢰성에 미치는 열처리의 영향", 대한금속·재료학회지, 50(1), pp.71~77 (2012), 대한금속·재료학회
- Y. B. Yoon, , IEEE Transactions on Components and Packaging Technologies, 32, pp.825~ (2009)
- 홍대운, "경장벽 산화막 절연층 MCPCB를 이용한 LED 모듈 구현", 한국광학회지, 20(4), pp.236~240 (2009), 한국광학회
- Kelvin Shih, "LED Junction Temperature Measurement and its Applications to Automotive Lamp Design", SPE international, pp.25~ (2004)
- J. H. Yuan, , Chem. Mater, 16, pp.1841~ (2004)
- W. Bensalahy, , J. Mater. Sci. Technol, 26, pp.113~ (2010)
- 신영의, "PCB SMT 품질관리", pp.667~ (2006), 도서출판 골드
- 장동규, "PCB 핵심기술 핸드북", pp.441~ (2005), 도서출판 골드