SDSS (Super Duplex Stainless Steel) 강관의 미세조직 및 부식특성에 미치는 열처리 온도의 영향
The Influence of Heat Treatment Temperature on Microstructure and Corrosion Behavior of SDSS Tube
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The aim of this paper is to determine the proper heat treatment temperature for SDSS tube production without σ-phase precipitation. When Mother steel tube was heat treated at 800oC temperature, relatively a large amount of σ-phase precipitated and grain refinement of ferrite phase occurred simultaneously. However, in Pilgered and Drawn steel tubes, grain refinement of the ferrite phase did not occur and a small amount of σ-phase precipitated. For all three types of steel tubes, the pitting potential was reduced to 2/5 or less compared with the untreated one and corrosion also occurred in the salt spray test due to the precipitation of σ-phase. When heat treatment temperature was 900oC, grain refinement of the ferrite phase occurred and very little σ-phase precipitated in Pilgered and Drawn steel tubes. But when heat treatment was done at 1,000oC temperature, all three types of steel tubes had a similar corrosion properties of that of untreated one and also corrosion did not occur in the salt spray test, as σ-phase did not precipitate. Therefore, the optimum heat treatment temperature range is determined to be more than 1000oC for the SDSS at which corrosion does not occur.
Abstract
The aim of this paper is to determine the proper heat treatment temperature for SDSS tube production without σ-phase precipitation. When Mother steel tube was heat treated at 800oC temperature, relatively a large amount of σ-phase precipitated and grain refinement of ferrite phase occurred simultaneously. However, in Pilgered and Drawn steel tubes, grain refinement of the ferrite phase did not occur and a small amount of σ-phase precipitated. For all three types of steel tubes, the pitting potential was reduced to 2/5 or less compared with the untreated one and corrosion also occurred in the salt spray test due to the precipitation of σ-phase. When heat treatment temperature was 900oC, grain refinement of the ferrite phase occurred and very little σ-phase precipitated in Pilgered and Drawn steel tubes. But when heat treatment was done at 1,000oC temperature, all three types of steel tubes had a similar corrosion properties of that of untreated one and also corrosion did not occur in the salt spray test, as σ-phase did not precipitate. Therefore, the optimum heat treatment temperature range is determined to be more than 1000oC for the SDSS at which corrosion does not occur.
참고문헌 (7)
- 안석환, "0.2% N을 첨가한 수퍼 2상 스테인리스강의 열처리 조건에 따른 특성 평가 - 제3보: 부식특성", 한국해양공학회지, 23(5), pp.85~91 (2009), 한국해양공학회
- 이재형, "슈퍼듀플렉스강 용접금속의 공식에 미치는 시효처리의 영향", 한국동력기계공학회지, 18(2), pp.70~76 (2014), 한국동력기계공학회[DOI]
- H. J. Kang, , J. Kor. Oce. Eng. Tech, 17(2), pp.40~ (2009)
- Sang-Ho Byun, "Kinetics of Cr", Mo-rich Precipitates Formation for 25Cr-6.9Ni-3.8Mo-0.3N Super Duplex Stainless Steel, 2012, pp.18(2), 201~207[DOI]
- 도재윤, "슈퍼이상스테인리스강 용접열영향부의 피로균열전파거동 및 음향방출 특성", 대한금속·재료학회지, 40(9), pp.924~931 (2002), 대한금속·재료학회
- 김수천, "슈퍼 2상 스테인리스강의 미세조직 및 기계적 성질에 미치는 시효의 영향", 한국해양공학회지, 23(3), pp.40~45 (2009), 한국해양공학회
- 김수천, "텅스텐이 첨가된 슈퍼 2상 스테인리스강의 내식성에 미치는 시효처리의 영향", 한국해양공학회지, 23(6), pp.87~92 (2009), 한국해양공학회