PEO 전류밀도 조건에 따른 알루미늄도금 강재상 산화코팅막의 특성
Characteristics of Coating Films on Hot-Dipped Aluminized Steel Formed by Plasma Electrolytic Oxidation Process at Different Current Densities
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Plasma electrolytic oxidation(PEO) has attracted attention as a surface treatment which has high wear resistance and corrosion resistance. PEO is generally considered as cost-effective, environmentally friendly and superior in terms of coating performance. Most of studies about the PEO processes have been applied to light metals such as Al and Mg. Because the strength of Al and Mg is weaker than that of steel, there is a limit to the application. In this study, PEO process was used to form oxide coatings on Hot dipped aluminized( HDA) steel and the characteristics of the coating film according to the PEO current density were studied. The morphology was observed by SEM and component was analyzed by using EDS. The corrosion behaviors of PEO coating films were estimated by exposing salt spray test at 5 wt.% NaCl solution and measuring polarization curves in deaerated 3 wt.% NaCl solution. With the increase of PEO process current density, the pore size of the coating surface and the thickness of coating increased. It was confirmed that no Fe component was present on the coating surface. PEO coating films obviously showed good corrosion resistance compared with HDA. It is considered that the PEO coating acts as a barrier to protect the base material from external factors causing corrosion.
Abstract
Plasma electrolytic oxidation(PEO) has attracted attention as a surface treatment which has high wear resistance and corrosion resistance. PEO is generally considered as cost-effective, environmentally friendly and superior in terms of coating performance. Most of studies about the PEO processes have been applied to light metals such as Al and Mg. Because the strength of Al and Mg is weaker than that of steel, there is a limit to the application. In this study, PEO process was used to form oxide coatings on Hot dipped aluminized( HDA) steel and the characteristics of the coating film according to the PEO current density were studied. The morphology was observed by SEM and component was analyzed by using EDS. The corrosion behaviors of PEO coating films were estimated by exposing salt spray test at 5 wt.% NaCl solution and measuring polarization curves in deaerated 3 wt.% NaCl solution. With the increase of PEO process current density, the pore size of the coating surface and the thickness of coating increased. It was confirmed that no Fe component was present on the coating surface. PEO coating films obviously showed good corrosion resistance compared with HDA. It is considered that the PEO coating acts as a barrier to protect the base material from external factors causing corrosion.
참고문헌 (13)
- Hisashi Hayashi, "Recent trends in sheet metals and their formability in manufacturing automotive panels", Journal of Materials Processing Technology, 46, pp.455~487 (1994)
- S. M. A. Shibli, "Development of high performance aluminum alloy sacrificial anodes reinforced with metal oxides", Materials Letters, 61, pp.3000~3004 (2007)
- Gul Hameed Awan, "The morphology of coating", substrate interface in hot-dip-aluminized steels, 2008, pp.472, 157~165
- V. N. Yeremenko, "The effect of dissolution on the growth of the Fe2Al5interlayer in the solid iron -liquid aluminum system", J. Mater. Sci, 16(7), pp.1748~1756 (1981)
- Toshiaki Yamamoto, "Aluminum Surface Treatment Using Three Different Plasma-Assisted Dry Chemical Processes", IEEE Transactions on Industry Applications, 40(5), pp.1220~1225 (2004)
- J.M.Montero-Moreno, "Influence of the aluminum surface on the final results of a twostep anodizing", Surface and Coatings Technology, 201(14), pp.6352~6357 (2007)
- 문성모, "황산용액에서 Al7075 합금 표면의 양극산화피막 형성거동", 한국표면공학회지, 47(4), pp.155~161 (2014), 한국표면공학회[DOI]
- A. L. Yerokhin, "Plasma electrolysis for surface engineering", Surface and coatings Technology, 122, pp.73~93 (1999)
- L. O Snizhko, "Anodic processes in plasma electrolytic oxidation of aluminum in alkaline solution", Electrochimica Acta, 49, pp.2085~2095 (2004)
- R. O. Hussein, "Matthews, Spectroscopic study of electrolytic plasma and discharging behaviour during the plasma electrolytic oxidation PEO process", Journal of physics D: Applied physics, 43, pp.1~13 (2010)
- A. L. Yerokhin, "Discharge characterization in plasma electrolytic oxidation of aluminum", Journal of Physiscs D: Applied Physics, 36, pp.2110~2120 (2003)
- R. O. Hussein., "Influence of process parameters on electrolytic plasma discharging behaviour and aluminum oxide coating microstructure", Surface & Coatings Technology, 205, pp.1659~1667 (2010)
- Zhenqiang Wu, "Structure and mechanical properties of ceramic coatings fabricated by plasma electrolytic oxidation on aluminized steel", Applied Surface Science, 253, pp.8398~8403 (2007)