Characterization of Electro-deposited Ni-P Layer by Using Dynamic Nano-Indentation Method
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Dynamic nano-indentation method was applied to characterize thin electroformed Ni-P layers. The Ni-P layers were produced in a sulphamic acid bath at 50oC in 0.02 A/cm2 for 10-60 minutes. The chemical analyses by XRD and EDX showed that the Ni-P layers were very fine grains with mainly Ni3P with Ni. The surface roughness determined by atomic force microscopy increased with thickness, which was relative to the surface morphology. The nano-hardness and the stiffness of the thin Ni-P layers with thickness of 1.9, 6.2 and 7.5 μm were 5.52, 6.52 and 6.77 [GPa] and 56.7, 76.2 and 108.0 [μN/nm], respectively. The elastic modulus of the Ni-P layer increased with thickness such as 37.29, 54.50 and 78.76 [GPa], respectively. The surface roughness of the electroplated Ni-P layers with diverse thickness was 8.66, 18.56 and 35.22 [nm], respectively. The enhanced nano-mechanical properties were related to mainly residual stress of the Ni-P layers.
Abstract
Dynamic nano-indentation method was applied to characterize thin electroformed Ni-P layers. The Ni-P layers were produced in a sulphamic acid bath at 50oC in 0.02 A/cm2 for 10-60 minutes. The chemical analyses by XRD and EDX showed that the Ni-P layers were very fine grains with mainly Ni3P with Ni. The surface roughness determined by atomic force microscopy increased with thickness, which was relative to the surface morphology. The nano-hardness and the stiffness of the thin Ni-P layers with thickness of 1.9, 6.2 and 7.5 μm were 5.52, 6.52 and 6.77 [GPa] and 56.7, 76.2 and 108.0 [μN/nm], respectively. The elastic modulus of the Ni-P layer increased with thickness such as 37.29, 54.50 and 78.76 [GPa], respectively. The surface roughness of the electroplated Ni-P layers with diverse thickness was 8.66, 18.56 and 35.22 [nm], respectively. The enhanced nano-mechanical properties were related to mainly residual stress of the Ni-P layers.
참고문헌 (12)
- H.B. Lee, "Wear and Immersion Corrosion of Ni-P Electrodeposit in NaCl Solution", Tribology International, 43, pp.235~244 (2010)[DOI]
- 최명희, "열처리 시간에 따른 Ni-P", Cr 이중 도금 층의 계면 거동에 관한 연구, 2015, pp.48(6), 260~268[DOI]
- Amir Ahmadi Ashtiani, "The Study of Electroless Ni-P with Different Complexing Agents on Ck45 Steel Substrate", Arabian Journal of Chemistry, 10, pp.1541~1545 (2017)[DOI]
- P. Peeters, "Properties of Electroless and Electroplated Ni-P and its Application in Microgalvanics", Electrochimica Acta, 47, pp.161~169 (2001)[DOI]
- Kazimierz Czapczyk, "Influence of the Thickness of Ni-P Coating Applied on 7075 Aluminum Alloy on its Hardness", Advances in Science and Technology, 10, pp.53~58 (2016)
- Cheng-Hsun Hsu, "Effects of Thickness of Electroless Ni-P Deposit on Corrosion Fatigue Damage of 7075-T6 under Salt Spray", Atmosphere, 45, pp.3201~3208 (2004)
- Moo Hong Seo, "The Study on Residual Stresses of Ni Alloy Electrodeposits for Steam Generator Tube Repair", Proceedings of the Korean Nuclear Society Autumn Meeting, 35 (2003)
- G. Mcmahon, "Structural Transitions in Electroplated Ni-P alloys", Journal of Materials Science Letters, 8, pp.865~868 (1989)[DOI]
- Raj Narayan, "Electrodeposition of Ni-P Alloy Coatings", Surface Technology, 24, pp.233~239 (1985)[DOI]
- A.P. Ordine, "Electrochemical Study on Ni-P Electrodeposition", Electrochimica Acta, 51, pp.1480~1486 (2006)[DOI]
- R. Rofagha, "The Effects of Grain Size and Phosphorus on the Corrosion of Nanocrystalline Ni-P Alloys", Nanostructured Materials, 2, pp.1~10 (1993)[DOI]
- N. Du M. Pritzker, "Investigation of electroless plating of Ni-W-P alloy films", Journal of Applied Electrochemistry, 33, pp.1001~1009 (2003)[DOI]