This paper is concerned with the surface hardness measurement of NiP-coated AA7050 using different loads from 10 to 100 g. The surface hardness was observed to increase from 180 to 600 Hv with increasing NiP layer thickness, depending on the load applied for indentation. When NiP coating thickness is thinner than 2 ㎛, the surface hardness of NiP-coated AA7050 was mainly determined by AA7050 substrate, while it was significantly increased by NiP coating layer when NiP coating thickness is thicker than 2 ㎛. Hardness of AA7050 substrate itself was not dependent on the applied load but the hardness of NiP-coated AA7050 was largely influenced by the load applied for indentation. The largest difference of hardness between 10 g and 100g of applied loads, was obtained at the NiP thickness of about 8 ㎛ above which the measured hardness at 10 g reached a maximum value of about 600 Hv. It was also observed that indentation-induced plastic deformation next to the indented zone occurs when NiP layer is 5.64 times thicker than the depth of impression formed by indentation.
Abstract
This paper is concerned with the surface hardness measurement of NiP-coated AA7050 using different loads from 10 to 100 g. The surface hardness was observed to increase from 180 to 600 Hv with increasing NiP layer thickness, depending on the load applied for indentation. When NiP coating thickness is thinner than 2 ㎛, the surface hardness of NiP-coated AA7050 was mainly determined by AA7050 substrate, while it was significantly increased by NiP coating layer when NiP coating thickness is thicker than 2 ㎛. Hardness of AA7050 substrate itself was not dependent on the applied load but the hardness of NiP-coated AA7050 was largely influenced by the load applied for indentation. The largest difference of hardness between 10 g and 100g of applied loads, was obtained at the NiP thickness of about 8 ㎛ above which the measured hardness at 10 g reached a maximum value of about 600 Hv. It was also observed that indentation-induced plastic deformation next to the indented zone occurs when NiP layer is 5.64 times thicker than the depth of impression formed by indentation.
참고문헌 (10)
- Jieqin Lu, "Aluminum alloy AA2024 anodized from the mixed acid system with enhanced mechanical properties", Surfaces and Interfaces, 13, pp.46~50 (2018)
- T. Aerts, "Influence of the anodizing temperature on the porosity and the mechanical properties of the porous anodic oxide film", Surface & Coatings Technology, 201, pp.7310~7317 (2007)
- Moonsu Kim, "Non-nickel-based sealing of anodic porous aluminum oxide in NaAlO2", Surface & Coatings Technology, 310, pp.106~112 (2017)
- Dongya Zhang, "Electrophoretic deposition of PTFE particles on porous anodicaluminum oxide film and its tribological properties", Applied Surface Science, 290, pp.466~474 (2014)
- Cheng Lu, "Influence of surface microstructure on tribological properties of PEO-PTFEcoating formed on aluminum alloy", Surface and Coatings Technology, 364, pp.127~134 (2019)
- M. H. Staia, "Tribological response of AA 2024-T3aluminium alloy coated with aDLC duplex coating", Tribology International, 85, pp.74~ (2015)
- C. D’Amato, "Tribological characteristics of an A356aluminium alloy laser surfacealloyed with nickel and Ni–Ti–C", Applied Surface Science, 313, pp.720~729 (2014)
- 문성모, "알루미늄 합금 양극산화피막의 표면경도 측정법", 한국표면공학회지, 53(1), pp.36~42 (2020), 한국표면공학회
- 문성모, "Surface hardness measurement of anodic oxide films on AA2024 based an ink-impregnation method", 한국표면공학회지, 53(2), pp.80~86 (2020), 한국표면공학회
- I. Saravanan, "Wear behaviour of electroless Ni-P and Ni-P-TiO2composite coatings on En8steel", Materials Today: Proceedings, 22, pp.1135~1139 (2020)