ATY 사가공에 의한 Fluffy Spun-like Yarn의 물성 (1)
The Mechanical Properties of Fluffy Spun-like Yarn by ATY Textured (1)
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
This research has a main focus on providing fundamental data for on-the-spot industrial fields by comparing and contrasting physical properties of fluffy spun-like material. The fluffy spun-like yarn is developed as fluffy yarn similar to natural spun-like yarn by treating polyester(FDY and + type shaped DTY) with ATY machine. In this experiment, using ATY machine for raw material texturing, we produced two fluffy yarns: (ⅰ) + type shaped(50d/36f, DTY) as core yarn and 100d/192f FDY as effect yarn[ATY(D)], (ⅱ) FDY(75/36) as core yarn and 100d/192f FDY [ATY(F)] as effect yarn. After producing thous yarns, we twisted them with 500T/M, 700T/M, 1000T/M, respectively. produced yarns through this process were used as the samples for this experiment. Even though the shrinkage of fluffy yarn ATY(F) and ATY(D) becomes high as treated temperature rises and treated time lengthens, it is more affected by treated temperature then by treated time. In this experiment, produced fluffy yarn[ATY(D)] shows a little high values for temperature, but almost same values for higher temperatures. When we compare ATY(F) with ATY(D) fluffy yarn shows more natural fluffy yarn surface structure like natural cotton. The shrinkage of 700T/M twisted ATY(D) fluffy yarn show about 11% under treated temperature 180℃ and treated time 30min, and about 7% under 120℃ and 30min, respectively. But the shrinkage of 1000T/M fluffy yarn shoes about 9% and 6% under same conditions. Regarding treated time, tenacity and initial modulus of ATY(D) fluffy yarn rise high until 30min, but do not show much increase above 30min. Regarding treated temperature, tenacity and initial modulus of it rise high aboyer 140℃.
Abstract
This research has a main focus on providing fundamental data for on-the-spot industrial fields by comparing and contrasting physical properties of fluffy spun-like material. The fluffy spun-like yarn is developed as fluffy yarn similar to natural spun-like yarn by treating polyester(FDY and + type shaped DTY) with ATY machine. In this experiment, using ATY machine for raw material texturing, we produced two fluffy yarns: (ⅰ) + type shaped(50d/36f, DTY) as core yarn and 100d/192f FDY as effect yarn[ATY(D)], (ⅱ) FDY(75/36) as core yarn and 100d/192f FDY [ATY(F)] as effect yarn. After producing thous yarns, we twisted them with 500T/M, 700T/M, 1000T/M, respectively. produced yarns through this process were used as the samples for this experiment. Even though the shrinkage of fluffy yarn ATY(F) and ATY(D) becomes high as treated temperature rises and treated time lengthens, it is more affected by treated temperature then by treated time. In this experiment, produced fluffy yarn[ATY(D)] shows a little high values for temperature, but almost same values for higher temperatures. When we compare ATY(F) with ATY(D) fluffy yarn shows more natural fluffy yarn surface structure like natural cotton. The shrinkage of 700T/M twisted ATY(D) fluffy yarn show about 11% under treated temperature 180℃ and treated time 30min, and about 7% under 120℃ and 30min, respectively. But the shrinkage of 1000T/M fluffy yarn shoes about 9% and 6% under same conditions. Regarding treated time, tenacity and initial modulus of ATY(D) fluffy yarn rise high until 30min, but do not show much increase above 30min. Regarding treated temperature, tenacity and initial modulus of it rise high aboyer 140℃.
참고문헌 (13)
- M. Ymaguchi, "Development of “Z-10” Functional Fiber", SEN,I GAKKAISHI, 58, pp.220~ (2002)
- O. Masakatsu, "Multi Functional Fiber “Z-10”", J. Text. Mach. Soc. of Japan, 52, pp.136~ (1999)
- 박명수, "Super Bulky Yarn의 사가공 조건에 따른 물성변화", 한국의류산업학회지, 12(4), pp.500~507 (2010), 한국의류산업학회
- Dongyang Ltd, "Process of Producing Polyester of Spun-like, Korean Patent, 1019860005837", ~ (1986)
- J. H. Park, "Process of Producing Polyester Draw Textured Yarn Having of Spun-like Effect, Korean Patent, 10-1077677", ~ (2011)
- Milican, "Face Plate Spun-like Textured Yarn, Korean Patent, 1020037004817", ~ (2003)
- Sunkyung Industry Ltd., "Process of Producing Multi -filament Polyester Yarn of Spun-like, Korean Patent, 1019920025479", ~ (1992)
- 박명수, "복합가공사를 이용한 Wool-like 직물의 역학적성질", 한국의류산업학회지, 5(4), pp.408~412 (2003), 한국의류산업학회
- 박명수, "잠재 권축사를 이용한 New Worsted Wool-like 직물의 역학적 특성", 한국염색가공학회지, 23(4), pp.233~240 (2011), 한국염색가공학회
- 박명수, "이형단면(+Type) DTY사의 물성변화", 한국의류산업학회지, 13(1), pp.130~134 (2011), 한국의류산업학회
- R. H. Broughton, "Mechanical of Yarn Failure", Textile Rec. J., 62(3), pp.31~ (1992)
- J. W. S. Hearle, "Structural Mechanics of Fiber, Yarns and Fabrics 1", pp.191~205 (1969), Wiley-interscience
- N. Pan, "Relationship between Fiber and Yarn Strength", Textile Rec. J., 71(11), pp.960~ (2001)