Super Bulky Yarn의 사가공 조건에 따른 물성변화
The Physical Properties of Super Bulky Yarn According to Textured Condition
1
조회
0
다운로드
6
인용
0
참고문헌
키워드
초록
In this study, physical properties were studied by using latent stretching yarn in order to develop the texturing yarn technique for super bulky yarn, which is better in bulkiness and handle than natural wool and also adds property of synthetic fiber to natural wool. In order to obtain textured conditions by analysing basic properties for manufacturing DTY yarn with super bulky property, DTY 50d/12 after spinning latent yarn spined POY 80d/12 was obtained under the two conditions of (i) false twist(T/M) level 3 in DTY texturing and (ii) draw ratio level 4 in draw texturing. For DTY texturing yarn, Elongation rate increased as the heat treatment time and temperatures increased. In addition, shrinkage became higher as false twist was higher, so that elongation rate became lower. When annealing became longer in time and higher in temperature, initial modulus increased. In addition, as the count of false twist increased, the initial modulus showed higher values. For draw texturing yarn, under the conditions of heat temperature 180 and heating time 30 minutes, shrinkage rate in draw ratio 1.55 and 1.6 draw ratio was 7%, and that in 1.65 and 1.7 draw ratio was 8.5%. High draw ratio samples'tenacity was much influenced by heating time and temperature, but low draw ratio samples' tenacity was influenced not by treated time, but by treated temperature.
Abstract
In this study, physical properties were studied by using latent stretching yarn in order to develop the texturing yarn technique for super bulky yarn, which is better in bulkiness and handle than natural wool and also adds property of synthetic fiber to natural wool. In order to obtain textured conditions by analysing basic properties for manufacturing DTY yarn with super bulky property, DTY 50d/12 after spinning latent yarn spined POY 80d/12 was obtained under the two conditions of (i) false twist(T/M) level 3 in DTY texturing and (ii) draw ratio level 4 in draw texturing. For DTY texturing yarn, Elongation rate increased as the heat treatment time and temperatures increased. In addition, shrinkage became higher as false twist was higher, so that elongation rate became lower. When annealing became longer in time and higher in temperature, initial modulus increased. In addition, as the count of false twist increased, the initial modulus showed higher values. For draw texturing yarn, under the conditions of heat temperature 180 and heating time 30 minutes, shrinkage rate in draw ratio 1.55 and 1.6 draw ratio was 7%, and that in 1.65 and 1.7 draw ratio was 8.5%. High draw ratio samples'tenacity was much influenced by heating time and temperature, but low draw ratio samples' tenacity was influenced not by treated time, but by treated temperature.
참고문헌 (13)
- Berkowitch, J. E., "In tomorrow's Ideal and Profits: Polyester 50 years of Achievement Textile Institute, Manchester", 112~ (1993)
- Masakatsu, O., "Multi Functional Fiber "Z-10"", J. Text, Mach. Soc. of Japan., 52, pp.136~138 (1999)
- Miller, R. W., "Investigation of Polyester Fiber Process", Structure, Text. Research., Journal., pp.1983, 53[DOI]
- Okamoto, M., "In tomorrow's Ideal and Profits: Polyester 50 years of Achievement Textile Institute, Manchester", 108~ (1993)
- Park, M. S., "The Change of Crystal Structure and Physical Properties of Partially Oriented Polyester Yarn(POY) on the Draw Ratio and Heat Setting Temperature", Journal. korean Society. Dyers & Finishers, 12, pp.103~110 (2000)
- Sigeki, H., "Technology of Hi-Component Spinning", J. Text, Mach. Soc. of Japan., 55, pp.270~272 (2002)
- Takayuki, I., "The Thought of Development Based on Bi-Component Spinning Technology", J. Text, Mach. Soc. of Japan., 55, pp.273~276 (2002)
- Teijin Ltd., "Elastic core-sheath type conjugate yarn and elastic woven or knitted fabric, Japan Patent. 200200094558", ~ (2002)
- Unitika Ltd., "Latent crimping polyamide yarn and method for producing the same, Japan Patent. 200100171170", ~ (2001)
- Valk, G., "The Non crystalline State Within PET Fibers-Meaning and Characterization by Mechanical-Relaxation Measurement", Text. Research., Journal., 50, pp.46~54 (1980)
- 주) 효성, "폴리에스테르계 복합섬유 및 그 제조방법, 대한민국특허청, 10-2001-0054945", ~ (2001)
- 주) 효성, "Korea Patent. 세데니어 나일론 잠제권축사의 제조방법, 대한민국특허청, 10-2001-0088721", ~ (2001)
- 주) 효성, "사이드 바이 사이드형 복합방사 구금, 대한민국특허청, 10-2002-0051300", ~ (2002)