코팅제의 가교 밀도에 따른 고무와 코팅원단의 물성 변화
Properties of Rubbers and Coated Fabrics according to Different Cross-linking Density of Coating Agent
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Silicone rubber is widely used in most industries due to diverse advantages like heat stability, UV stability, durability, chemical resistance, environment friendliness, inertness and so on. But there is limitation to expand applications due to relatively weak rubber strengths such as tensile strength and tear strength, especially in fabric coating applications. The purpose of this study is to find influence of coating agent on performances of rubber and coated fabrics and their correlation according to different crosslinking densities of silicone rubbers. Addition cure type of silicones were formulated using crosslinked MQ-type silicone resin consisting of M (R3SiO1/2) and Q (SiO4/2) and linear polymers. Raw materials used were; 1) linear vinyl endblocked polymers and vinyl functional MQ resin as main polymers, 2) linear silicone hydride polymers as crosslinkers, 3) platinum catalyst and 4) inhibitor to control curing speed. Rubber specimens were prepared to check mechanical strength using universal testing machine (UTM). Crosslinking density was calculated using Flory-Rhener equation using solvent swelling method. Differential scanning calorimetry (DSC) and scanning electron microscope (SEM-EDS) were used to characterize rubbers. Consequently, it was found that physical properties of silicone rubbers and coated fabrics can be expected by crosslinking density of rubbers. Silicone rubber formulations that contain 20 ~ 30 wt% of vinyl MQ resin showed strongest balanced performances.
Abstract
Silicone rubber is widely used in most industries due to diverse advantages like heat stability, UV stability, durability, chemical resistance, environment friendliness, inertness and so on. But there is limitation to expand applications due to relatively weak rubber strengths such as tensile strength and tear strength, especially in fabric coating applications. The purpose of this study is to find influence of coating agent on performances of rubber and coated fabrics and their correlation according to different crosslinking densities of silicone rubbers. Addition cure type of silicones were formulated using crosslinked MQ-type silicone resin consisting of M (R3SiO1/2) and Q (SiO4/2) and linear polymers. Raw materials used were; 1) linear vinyl endblocked polymers and vinyl functional MQ resin as main polymers, 2) linear silicone hydride polymers as crosslinkers, 3) platinum catalyst and 4) inhibitor to control curing speed. Rubber specimens were prepared to check mechanical strength using universal testing machine (UTM). Crosslinking density was calculated using Flory-Rhener equation using solvent swelling method. Differential scanning calorimetry (DSC) and scanning electron microscope (SEM-EDS) were used to characterize rubbers. Consequently, it was found that physical properties of silicone rubbers and coated fabrics can be expected by crosslinking density of rubbers. Silicone rubber formulations that contain 20 ~ 30 wt% of vinyl MQ resin showed strongest balanced performances.
참고문헌 (17)
- D. Graiver, "A Review of the Fate and Effects of Silicones in the Environment", Journal of Polymers and the Environment, 11, pp.129~ (2003)
- S. C. Shit, "A Review on Silicone Rubber", National Academy Science Letters, 36(4), pp.355~ (2013)
- S. Joanne, "High Performance Silicone-coated Textiles : Developments and Applications", Journal of Coated Fabrics, 26(1), pp.65~ (1996)
- M. J. Wang, "Effect of Fumed Silica Surface Area on Silicone Rubber Reinforcement", Kautsch, Gummi Kunstst, 61, pp.107~ (2008)
- Q. Xu, "Mechanical Properties of Silicone Rubber Composed of Diverse Vinyl Content Silicone Gums Blending", Materials and Design, 31(9), pp.4083~ (2010)
- J. Shen, "Effects of Cross-link Density and Distribution on Static and Dynamic Properties of Chemically Cross-linked Polymers", Macromolecules, 52(1), pp.121~ (2018)
- 임창하, "실리콘폴리머의 혼합사용이 폴리비닐실록산 치과용 인상재의 물성에 미치는 영향", 엘라스토머 및 콤포지트, 44(1), pp.76~83 (2009), 한국고무학회
- 주동현, "실리콘 폴리머의 비닐그룹에 대한 가교제의 Si-H 비율이 폴리비닐실록산 치과용 인상재의 물성에 미치는 영향", 엘라스토머 및 콤포지트, 44(2), pp.150~155 (2009), 한국고무학회
- D. H. Flagg, "Rediscovering Silicones : MQ Copolymers", Macromolecules, 49(22), pp.8581~ (2016)
- K. Yoshii, "Photo-probe Study of Siloxane Polymers I, Local Free Volume of an MQ-type Silicone Resin Containing Crosslinked Nanoparticles Probed by Photoisomerization of Azobenzene", Journal of Non-crystalline Solids, 246(1-2), pp.90~ (1999)
- J. Ji, "Synthesis and Characterization of Room Temperature Vulcanized Silicone Rubber using Methoxylcapped MQ Silicone Resin as Self-reinforced Cross-linker", Polymers, 11(7), pp.1142~ (2019)
- A. M. Sawvel, "Spectroscopic Signatures of MQ-resins in Silicone Elastomers", Macromolecules, 54(9), pp.4300~ (2021)
- J. Zhao, "The Influence of Crosslink Density on the Failure Behavior in Amorphous Polymers by Molecular Dynamics Simulations", Materials, 9(4), pp.234~ (2016)
- J. Schweitzer, "Determination of the Crosslinking Density of a Silicone Elastomer", Journal of Chemical Education, 96(7), pp.1472~ (2019)
- S. S. Choe, "Analysis Method of Rubber Materials using DSC", Rubber Technology, 22(1), pp.15~ (2021)
- A. J. Marzocca, "Evaluation of the Polymer-solvent InteractionParameter χ for the System Cured Styrene Butadiene Rubber and Toluene", European Polymer Journal, 43(6), pp.2682~ (2007)
- Q. Han, "Relationship between Dynamic Fatigue Crack Propagation Properties and Viscoelasticity of Natural Rubber", silicone Rubber Composites, 2019, pp.9(51), 29813~