Characterization of PVDF/PU fibers prepared by electrospinning
1
조회
0
다운로드
4
인용
0
참고문헌
키워드
초록
The 23 wt% polyvinylidene fluoride (PVDF)/15 wt% polyurethane (PU) fibers were electrospun using the conjugated nozzle at a flow rate of 1.0 mL/h and an electric field of 1 kV/cm. The formation of β crystal phase in the PVDF and the PVDF/PU fibers was confirmed by Fourier transform infrared spectroscopy. After electrospinning, the asspun fibers were immersed in a boiling water and then dried at 100oC in a convection oven to make a crimp phenomenon. The crimps with a diameter of 2.0 ± 0.08 μm were observed for the PVDF/PU fibers after hydrothermal treatment without sacrificing the extent of β crystal phase. All the PU, PVDF and PVDF/PU fibers exhibited average cell viability of more than 98 %. The cell proliferation results suggested that L-929 cells adhered well to the PU, PVDF and PVDF/PU fibers and proliferated continuously with increasing time, indicating that the PVDF/PU fibers are highly applicable to the biomedical applications.
Abstract
The 23 wt% polyvinylidene fluoride (PVDF)/15 wt% polyurethane (PU) fibers were electrospun using the conjugated nozzle at a flow rate of 1.0 mL/h and an electric field of 1 kV/cm. The formation of β crystal phase in the PVDF and the PVDF/PU fibers was confirmed by Fourier transform infrared spectroscopy. After electrospinning, the asspun fibers were immersed in a boiling water and then dried at 100oC in a convection oven to make a crimp phenomenon. The crimps with a diameter of 2.0 ± 0.08 μm were observed for the PVDF/PU fibers after hydrothermal treatment without sacrificing the extent of β crystal phase. All the PU, PVDF and PVDF/PU fibers exhibited average cell viability of more than 98 %. The cell proliferation results suggested that L-929 cells adhered well to the PU, PVDF and PVDF/PU fibers and proliferated continuously with increasing time, indicating that the PVDF/PU fibers are highly applicable to the biomedical applications.
참고문헌 (13)
- 이현재, "전기방사에 의한 PVDF", PU 복합나노섬유의 제조 및 특성 분석, 2015, pp.52(2), 88~96[DOI]
- C. Pan, "Near-field electrospinning enhances the energy harvesting of hollow PVDF piezoelectric fibers", RSC Adv., 5, pp.85073~ (2015)
- 정건, "하이브리드 습식 공정을 통한 PVDF 섬유의 제조 및 특성에 관한 연구", Composites Research, 29(4), pp.145~150 (2016), 한국복합재료학회
- E. Nilsson, "Poling and characterization of piezoelectric polymer fibers for use in textile sensors", Sens. Actuators A, 201, pp.477~ (2013)
- 이세영, "전극일체형 polyvinyliden difluoride 압전 섬유에 관한 연구", 한국섬유공학회지, 53(4), pp.279~284 (2016), 한국섬유공학회
- G.T. Davis, "Electric-field-induced phase changes in poly(vinylidene fluoride)", J. Appl. Phys., 49, pp.4998~ (1978)
- S.M. Damaraju, "Structural changes in PVDF fibers due to electrospinning and its effect on biological function", Biomed. Mater., 8, pp.045007~ (2013)
- 설보경, "전기방사법으로 제조한 PU", PEG 복합 지지체의 특성, 2017, pp.38(5), 248~255[DOI]
- 김진태, "Biocompatibility of Hyaluronic Acid Hydrogels Prepared by Porous Hyaluronic Acid Microbeads", Metals and Materials International, 20(3), pp.555~563 (2014), 대한금속·재료학회[DOI]
- 김진태, "Tissue Response to Implants of Hyaluronic Acid Hydrogel Prepared by Microbeads", 조직공학과 재생의학, 11(1), pp.32~38 (2014), 한국조직공학과 재생의학회[DOI]
- 김예나, "Effect of PEG Addition on Pore Morphology and Biocompatibility of PLLA Scaffolds Prepared by Freeze Drying", Biomedical Engineering Letters (BMEL), 6(4), pp.287~295 (2016), 대한의용생체공학회[DOI]
- 손시원, "다공성 폴리(ε-카프로락톤)", 실리카 복합체의 제조 및 특성평가, 2015, pp.39(2), 323~328[DOI]
- 전철병, "Effect of molecular weight of hyaluronic acid (HA) on viscoelasticity and particle texturing feel of HA dermal biphasic fillers", 생체재료학회지, 20(4), pp.275~281 (2016), 한국생체재료학회[DOI]