Effect of asymmetric magnetic fields on the interface shape in Czochralski silicon crystals
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Silicon single crystals are grown by Czochralski (CZ) method in different growing conditions. The different shapes of the crystal-melt interface are obtained with various magnetic fields. Effects of zero-Gauss plane (ZGP) shape and magnetic intensity (MI) on the crystal-melt interface in the crystal experimentally are investigated. The shape of ZGP is not only flat but also parabolic, which is due to magnetic ratio (MR) of the lower to upper current densities in the configurations of the cusp-magnetic fields. As the MR increases, the crystal-melt interface becomes more concave. It means that the hot melt can be easily transported to the crystal-melt interface with increasing the MR. Effective shape of the crystal-melt interface is found to depend on the magnetic field in cusp-magnetic CZ method. The experimental results are compared with other studies and discussed.
Abstract
Silicon single crystals are grown by Czochralski (CZ) method in different growing conditions. The different shapes of the crystal-melt interface are obtained with various magnetic fields. Effects of zero-Gauss plane (ZGP) shape and magnetic intensity (MI) on the crystal-melt interface in the crystal experimentally are investigated. The shape of ZGP is not only flat but also parabolic, which is due to magnetic ratio (MR) of the lower to upper current densities in the configurations of the cusp-magnetic fields. As the MR increases, the crystal-melt interface becomes more concave. It means that the hot melt can be easily transported to the crystal-melt interface with increasing the MR. Effective shape of the crystal-melt interface is found to depend on the magnetic field in cusp-magnetic CZ method. The experimental results are compared with other studies and discussed.
참고문헌 (12)
- V.V. Voronkov, "The mechanism of swirl defects formation in silicon", J. Crystal Growth, 59, pp.625~ (1982)
- Y. Won, "Transient threedimensional numerical computation for unsteady oxygen concentration in a silicon melt during a Czochralski process under a cusp-shaped magnetic field", J. Crystal Growth, 233, pp.622~ (2001)
- K. Kakimoto, "Oxygen distribution in silicon melt under inhomogeneous transverse-magnetic fields", J. Crystal Growth, 230, pp.100~ (2001)
- K. Hoshikawa, "Oxygen transportation during Czochralski silicon crystal growth”, Mater. Sci. Eng B 72 (2000) 73.", Mater. Sci. Eng B, 72, pp.73~ (2000)
- M. Watanabe, "Flow and temperature field in molten silicon during Czochralski crystal growth in a cusp magnetic field", J. Crystal Growth, 193, pp.402~ (1998)
- K. Nakamura, "Effect of the shape of crystal-melt interface on point defect reaction in silicon crystals", ECS Proceeding, 17, pp.31~ (2000)
- B.C. Sim, "Effect of the crystal-melt interface on the grown-in defects in silicon CZ growth", J Crystal Growth, 299, pp.152~ (2007)
- D. Vizman, "Influence of different types of magnetic fields on the interface shape in a 200 mm Si-EMCZ configuration", J. Crystal Growth, 303, pp.221~ (2007)
- Y.H. Hong, "Effect of zero- Gauss plane and magnetic intensity on oxygen concentration in cusp-magnetic CZ crystals", J Crystal Growth, 295, pp.141~ (2006)
- Y.H. Hong, "Distribution coefficient of boron in Si crystal ingots grown in cuspmagnetic Czochralski process", J. Crystal Growth, 310, pp.83~ (2008)
- V. Galindo, "Crystal growth melt flow control by means of magnetic fields", Energy Conversion Manage, 43, pp.309~ (2002)
- D. Vizman, "Three dimensional numerical simulation of thermal convection in an industrial Czochralski melt: comparison to experimental results", J. Crystal Growth, 233, pp.687~ (2001)