Growth of O- and Zn-polar ZnO films by DC magnetron sputtering
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
O- and Zn-polar ZnO films were grown by DC magnetron sputtering. Growth of high-quality, single-crystal ZnO thin films were confirmed by XRD and pole figure analysis. O-polar ZnO was grown on an Al2O3 substrate, which was confirmed by a slow growth rate (378 nm/hr), a fast etching rate (59 nm/min), and by the hillocks on the surface after etching. Zn-polar ZnO was grown on a GaN/Al2O3 substrate, which was confirmed by a fast growth rate (550 nm/hr), a slow etching rate (28 nm/min), and by pits on the surface after etching. Results from the present study show that it is possible to use DC-sputtering to grow ZnO film with the same polarity as other epitaxial growth methods.
Abstract
O- and Zn-polar ZnO films were grown by DC magnetron sputtering. Growth of high-quality, single-crystal ZnO thin films were confirmed by XRD and pole figure analysis. O-polar ZnO was grown on an Al2O3 substrate, which was confirmed by a slow growth rate (378 nm/hr), a fast etching rate (59 nm/min), and by the hillocks on the surface after etching. Zn-polar ZnO was grown on a GaN/Al2O3 substrate, which was confirmed by a fast growth rate (550 nm/hr), a slow etching rate (28 nm/min), and by pits on the surface after etching. Results from the present study show that it is possible to use DC-sputtering to grow ZnO film with the same polarity as other epitaxial growth methods.
참고문헌 (15)
- T. Dethprohm, "Hydride vapor phase epitaxial growth of a high quality GaN film using a ZnO buffer layer", Appl. Phys. Lett, 61, pp.2688~ (1992)
- T. Detchprohm, "The growth of thick GaN film on sapphire substrate by using ZnO buffer layer", J. Cryst. Growth, 128, pp.384~ (1993)
- S. Gu, "Hydride vapor phase epitaxy growth of GaN on sapphire with ZnO buffer layers", Appl. Phys. A, 74, pp.537~ (2002)
- S.W. Lee, "Strain-free GaN thick films grown on single crystalline ZnO buffer layer with in situ lift-off technique", Appl. Phys. Lett, 90, pp.061907~ (2007)
- 김경국, "The grain size effects on the photoluminescence of ZnO", α-Al2O3 grown by radio-frequency magnetron sputtering, 200004, pp.87(7), 3573~3575[DOI]
- J.-H. Lim, "V electroluminesecence emission from ZnO light-emitting diodes grown by hightemperature radiofrequency sputtering", Adv. Mater, 18, pp.2720~ (2006)
- X. Gu, "GaN epitaxy on thermally treated c-plane bulk ZnO substrates with O and Zn faces", Appl. Phys. Lett, 84, pp.2268~ (2004)
- R. Cebulla, "Al-doped zinc oxide films deposited by simultaneous rf and dc excitation of a magnetron plasma: Relationships betweenm plasma parameters and structural and electrical film properties", J. Appl. Phys, 83, pp.1087~ (1998)
- K.K. Kim, "The grain size effects on the photoluminescence of ZnO", α-Al2O3 grown by radio-frequency magnetron sputtering, 2000, pp.87, 3573~
- X. Wang, "Polarity control of ZnO films grown on nitrided c-sapphire by molecular-beam epitaxy", Appl. Phys. Lett, 86, pp.011921~ (2005)
- H. Tampo, "Determination of crystallographic polarity of ZnO layers", Appl. Phys. Lett, 87, pp.141904~ (2005)
- J.S. Park, "Growth of polarity-controlled ZnO films on (0001) Al2O3", JOURNAL OF ELECTRONIC MATERIALS, 37, pp.736~742 (2008), SPRINGER
- H. Kato, "Polarity control of ZnO on c-plane sapphire by plasma-assisted MBE", J. Cryst. Growth, 275, pp.e2459~ (2005)
- K. Sakurai, "Effects of oxygen plasma condition on MBE growth of ZnO", J. Cryst. Growth, 209, pp.522~ (2000)
- 박주훈, "Growth and characterization of single crystal ZnO thin films using inductively coupled plasma metal organic chemical vapor deposition", APPLIED PHYSICS LETTERS, 89, pp.599~611 (2006), AMER INST PHYSICS