Effects of CoO doping on sintering and electrical conductivity of Ce0.8Gd0.2O1.9 prepared using CeO2 powder and Gd precipitation
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
This paper reports on the preparation of a fully dense Gd-doped CeO2 (GDC) at low sintering temperature using CeO2 powderand Gd precipitation in the presence of CoO as a sintering aid. A mixture of CeO2 powder and Gd precipitates was calcinedat 700 oC followed by milling that resulted in the GDC (Ce0.8Gd0.2O1.9) powder with an average particle size of 0.46 µm. Sintering of the undoped sample showed a relative density of 99.2% at 1500 oC, whereas the samples doped with 3 mol% and5 mol% CoO exhibited a significant densification at the lower temperature reaching a relative density of 98.8% at 1200 oC. The electrical conductivities of both doped samples were almost identical but higher than those of the undoped sample at allmeasuring temperatures.
Abstract
This paper reports on the preparation of a fully dense Gd-doped CeO2 (GDC) at low sintering temperature using CeO2 powderand Gd precipitation in the presence of CoO as a sintering aid. A mixture of CeO2 powder and Gd precipitates was calcinedat 700 oC followed by milling that resulted in the GDC (Ce0.8Gd0.2O1.9) powder with an average particle size of 0.46 µm. Sintering of the undoped sample showed a relative density of 99.2% at 1500 oC, whereas the samples doped with 3 mol% and5 mol% CoO exhibited a significant densification at the lower temperature reaching a relative density of 98.8% at 1200 oC. The electrical conductivities of both doped samples were almost identical but higher than those of the undoped sample at allmeasuring temperatures.
참고문헌 (17)
- H. Inaba, , Solid Sate Ionics, 83, pp.1~16 (1996)
- K. Higashi, , J. Mater. Res, 14, pp.957~967 (1999)
- D. Hari Prasad, , J. Alloys & Comp, 495, pp.238~241 (2010)
- J.-G. Li, , J. Am. Ceram. Soc, 86, pp.915~921 (2003)
- A.I.Y. Tok, , Mat. Sci. & Eng. A, 383, pp.229~234 (2004)
- L.D. Jadhav, , J. Alloys & Comp, 470, pp.383~386 (2009)
- D.Hari Prasad, "Correlation between the powder properties and sintering behaviors of nano-crystalline gadolinium-doped ceria", Journal of Ceramic Processing Research, 11(5), pp.523~526 (2010), 세라믹공정연구센터
- R.R. Kondakindia, , Mat. Chem. & Phys, 115, pp.728~734 (2009)
- C.M. Kleinlogel, , Solid State Ionics, 135, pp.567~573 (2000)
- G.S. Lewis, , State Ionics, 152-153, pp.567~573 (2002)
- J.D. Nicholas, , Solid State Ionics, 178, pp.1187~1194 (2007)
- D. Hari Prasad, , Ceram. Int, 38S, pp.S497~S500 (2012)
- E. Jud, , J. Electroceram, 16, pp.191~197 (2006)
- "Powder Diffraction File, Joint Committee on Powder Diffraction Standards", ASTM, Card No. 75-0162, ~ (1996)
- "Powder Diffraction File, Joint Committee on Powder Diffraction Standards", ASTM, Card Nos. 34-394 and 12-797, ~ (1996)
- M. Mori, , J. Fuel Cell Sci. and Tech, 8, pp.011007-1~011007-6 (2011)
- J.D. Sirman, , Electrochem. Soc, pp.1159~1168 (1997)