동종금속(SUS304, SS400)과 이종 금속(SUS304-SS400)의 용접 특성에 관한 분석
Analysis for Welding Characteristics of a Same Kind Metal(SUS304, SS400) and Different Kind Metal(SUS304-SS400)
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this research, the welding experiment was carried out with both the steel materials (SS400+SS400, SUS304+SUS304) and the different steel materials (SS400+ SUS304), where SS400 is a general structural rolled steel material and SUS304 is a cold strip stainless steel sheet. The average of yield point of a SS400 experimental piece was the most highest point with 2015.54 N/m2. Although welding defects were not found with the naked eye, it was sure that there were some wilding defects because there were no stress against load through experiments. The rate of yield point of experimental piece A, experimental piece B and experimental piece C was respectively 1.7mm, 1.3mm and 2.6mm. The rate of breakdown was respectively 39.77mm, 17.97mm and 2.6mm. So considering price and efficiency with use condition is very important. SS400 and SUS304 will be profited from considering price and mechanical property with use condition.
Abstract
In this research, the welding experiment was carried out with both the steel materials (SS400+SS400, SUS304+SUS304) and the different steel materials (SS400+ SUS304), where SS400 is a general structural rolled steel material and SUS304 is a cold strip stainless steel sheet. The average of yield point of a SS400 experimental piece was the most highest point with 2015.54 N/m2. Although welding defects were not found with the naked eye, it was sure that there were some wilding defects because there were no stress against load through experiments. The rate of yield point of experimental piece A, experimental piece B and experimental piece C was respectively 1.7mm, 1.3mm and 2.6mm. The rate of breakdown was respectively 39.77mm, 17.97mm and 2.6mm. So considering price and efficiency with use condition is very important. SS400 and SUS304 will be profited from considering price and mechanical property with use condition.
참고문헌 (6)
- Wu,T, "Numerical simulation of welding induced damage and residual stress of martensitic steel 15-5PH", International Journal of Solid and Structure, 45(18), pp.1973~1989 (2008)
- 이경만, "용접 작업 중 발생하는 유해물질의 영향", 한국생산제조시스템학회지, 17(1), pp.43~49 (2008), 한국생산제조시스템학회
- 강봉용, "CO2 용접의 스패터 발생에 미치는 용접이행 모드의 영향", 대한용접학회 지, 15(2), pp.72~80 (1997)
- 조상명, "이종재 접합부에서의 응력 집중현상에 관한 연구", 대한용접학회지, 10(1), pp.35~42 (1992)
- 서정, "이종두께 강 판의 CO2 레이저 용접 및 성형성", 대한용접 학회지, 14(1), pp.82~91 (1996)
- 이용복, "SS400 정접부 의 표면피로균열거동에 관한 연구", 대한용접학 회지, 14(2), pp.90~95 (1996)