Post space preparation timing of root canals sealed with AH Plus sealer
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Objectives: To determine the optimal timing for post space preparation of root canals sealed with epoxy resin-based AH Plus sealer in terms of its polymerization and influence on apical leakage. Materials and Methods: The epoxy polymerization of AH Plus (Dentsply DeTrey) as a function of time after mixing (8, 24, and 72 hours, and 1 week) was evaluated using Fourier transform infrared (FTIR) spectroscopy and microhardness measurements. The change in the glass transition temperature (Tg) of the material with time was also investigated using differential scanning calorimetry (DSC). Fifty extracted human single-rooted premolars were filled with gutta-percha and AH Plus, and randomly separated into five groups (n = 10) based on post space preparation timing (immediately after root canal obturation and 8, 24, and 72 hours, and 1 week after root canal obturation). The extent of apical leakage (mm) of the five groups was compared using a dye leakage test. Each dataset was statistically analyzed by one-way analysis of variance and Tukey’s post hoc test (α = 0.05). Results: Continuous epoxy polymerization of the material with time was observed. Although the Tg values of the material gradually increased with time, the specimens presented no clear Tg value at 1 week after mixing. When the post space was prepared 1 week after root canal obturation, the leakage was significantly higher than in the other groups (p < 0.05), among which there was no significant difference in leakage. Conclusions: Poor apical seal was detected when post space preparation was delayed until 1 week after root canal obturation. (Restor Dent Endod 2017;42(1):27-33)
Abstract
Objectives: To determine the optimal timing for post space preparation of root canals sealed with epoxy resin-based AH Plus sealer in terms of its polymerization and influence on apical leakage. Materials and Methods: The epoxy polymerization of AH Plus (Dentsply DeTrey) as a function of time after mixing (8, 24, and 72 hours, and 1 week) was evaluated using Fourier transform infrared (FTIR) spectroscopy and microhardness measurements. The change in the glass transition temperature (Tg) of the material with time was also investigated using differential scanning calorimetry (DSC). Fifty extracted human single-rooted premolars were filled with gutta-percha and AH Plus, and randomly separated into five groups (n = 10) based on post space preparation timing (immediately after root canal obturation and 8, 24, and 72 hours, and 1 week after root canal obturation). The extent of apical leakage (mm) of the five groups was compared using a dye leakage test. Each dataset was statistically analyzed by one-way analysis of variance and Tukey’s post hoc test (α = 0.05). Results: Continuous epoxy polymerization of the material with time was observed. Although the Tg values of the material gradually increased with time, the specimens presented no clear Tg value at 1 week after mixing. When the post space was prepared 1 week after root canal obturation, the leakage was significantly higher than in the other groups (p < 0.05), among which there was no significant difference in leakage. Conclusions: Poor apical seal was detected when post space preparation was delayed until 1 week after root canal obturation. (Restor Dent Endod 2017;42(1):27-33)
참고문헌 (30)
- Chen G, "Effect of immediate and delayed post space preparation on apical leakage using three root canal obturation techniques after rotary instrumentation", J Formos Med Assoc, 110, pp.454~459 (2011)
- Amin SA, "The effect of prior calcium hydroxide intracanal placement on the bond strength of two calcium silicate-based and an epoxy resin-based endodontic sealer", J Endod, 38, pp.696~699 (2012)
- Chen G, "The effect of immediate and delayed post-space preparation using extended working time root canal sealers on apical leakage", J Dent Sci, 8, pp.31~36 (2013)
- Arab B, "Molecular dynamics simulation of cross-linked epoxy polymers: the effect of force field on the estimation of properties", J Nano- Electron Phys, 5, pp.01013~ (2013)
- Dhaded N, "Evaluation of immediate and delayed post space preparation on sealing ability of Resilon-Epiphany and Gutta perchaAH plus sealer", J Conserv Dent, 16, pp.514~517 (2013)
- Reyhani MF, "Comparing the coronal seal of different thicknesses of MTA with guttapercha after post space preparation", Scientific World J, 2015, pp.708639~ (2015)
- Ghanadan K, "Effect of different endodontic sealers on push-out bond strength of fiber posts", Braz J Oral Sci, 14, pp.166~170 (2015)
- Reyhani MF, "Apical microleakage of AH Plus and MTA Fillapex sealers in association with immediate and delayed post space preparation: a bacterial leakage study", Minerva Stomatol, 64, pp.129~134 (2015)
- Ørstavik D, "Materials used for root canal obturation:technical, biological and clinical testing", Endod Topics, 12, pp.25~38 (2005)
- Tyagi S, "Evolution of root canal sealers: an insight story", Eur J Gen Dent, 2, pp.199~218 (2013)
- Versiani MA, "A comparative study of physicochemical properties of AH Plus and Epiphany root canal sealants", Int Endod J, 39, pp.464~471 (2006)
- Baldi JV, "Variability of physicochemical properties of an epoxy resin sealer taken from different parts of the same tube", Int Endod J, 45, pp.915~920 (2012)
- Nagas E, "Effect of timing of post space preparation on the apical seal when using different sealers and obturation techniques", J Dent Sci, 11, pp.79~82 (2016)
- Solano F, "Comparison of apical leakage between immediate versus delayed post space preparation using AH Plus sealer", J Endod, 31, pp.752~754 (2005)
- Lyons WW, "Comparison of coronal bacterial leakage between immediate versus delayed post-space preparation in root canals filled with Resilon", Epiphany, 2009, pp.42, 203~207
- Rigail-Cedeño A, "Fluorescence and IR characterization of epoxy cured with aliphatic amines", Polymer, 46, pp.9378~9384 (2005)
- Yan YL, "Changes in degree of conversion and microhardness of dental resin cements", Oper Dent, 35, pp.203~210 (2010)
- American Society for Testing and Materials, "ASTM E1356-08. Standard test method for assignment of the glass transition temperatures by differential scanning calorimetry", Annual book of ASTM standards, ~ (2014)
- Reis A, "Durability of resin dentin interfaces: effects of surface moisture and adhesive solvent component", Dent Mater, 20, pp.669~676 (2004)
- Kim YK, "Degree of conversion of dual-cured resin cement light-cured through three fibre posts within human root canals: an ex vivo study", Int Endod J, 42, pp.667~674 (2009)
- De Almeida WA, "Evaluation of apical sealing of three endodontic sealers", Int Endod J, 33, pp.25~27 (2000)
- Corrêa Pesce AL, "Effect of post space preparation on apical seal:influence of time interval and sealer", Med Oral Patol Oral Cir Bucal, 12, pp.E464~E468 (2007)
- Ebert J, "Clinical adhesive sealing of the pulp chamber following endodontic treatment: influence of thermomechanical loading on microleakage", J Adhes Dent, 11, pp.311~317 (2009)
- Marks MJ, "Effect of conversion on the structure-property relationships of amine-cured epoxy thermosets", ACS Appl Mater Interfaces, 1, pp.921~926 (2009)
- McMichen FR, "A comparative study of selected physical properties of five root-canal sealers", Int Endod J, 36, pp.629~635 (2003)
- Mazinis E, "An FTIR study of the setting reaction of various endodontic sealers", J Endod, 33, pp.616~620 (2007)
- Sostena MM, "Glass transition and degree of conversion of a light-cured orthodontic composite", J Appl Oral Sci, 17, pp.570~573 (2009)
- Heikkinen TT, "Thermocycling effects on resin bond to silicatized and silanized zirconia", J Adhes Sci Technol, 23, pp.1043~1051 (2009)
- Bernardi MIB, "Thermal analysis and structural investigation of different dental composite resins", J Therm Anal Calorim, 94, pp.791~796 (2008)
- Urbaniak M, "A relationship between the glass transition temperature and the conversion degree in the curing reaction of the EPY epoxy system", Polimery, 56, pp.240~243 (2011)