Histomorphometry and Stability Analysis of Loaded Implants with two Different Surface Conditions in Beagle Dogs
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Despite an improved bone reactions of Mg-incorporated implants in the animals, little yet has been carried out by the experimental investigations in functional loading conditions. This study investigated the clinical and histologic parameters of osseointegrated Mg-incorporated implants in delayed loading conditions. A total of 36 solid screw implants (diameter 3.75 mm, length 10mm) were placed in the mandibles of 6 beagle dogs. Test groups included 18 Mg-incorporated implants. Turned titanium Implants served as control. Gold crowns were inserted 3 months. Radiographic assessments and stabilitytests were performed at the time of fixture installation, 2nd stage surgery, 1 and 3 months after loading. Histological observations and morphometrical measurements were also performed. Of 36 implants, 32 displayed no discernible mobility, corresponding to successful clinical function. There was no statistically significant difference between test implants and controls in marginal bone levels (p=0.413) and RFA values. The mean BIC % in the Mg-implants was 54.4 ± 20.2%. The mean BIC % in the turned implant was 48.9 ± 8.0%. These differences between the Mg-implant and control implant were not statistically significant (P=0.264). In the limitation of this study, bone-to-implant contact (BIC) and bone area of Mg-incorporated oxidized implant were similar to machine-turned implant. The stability analysis showed no significantly different ISQ values and marginal bone loss between two groups. Considering time-dependent bone responses of Mg-implant, it seems that Mg-implants enhanced bone responses in early loading conditions and osseointegrated similarly to cp Ti implants in delayed loading conditions. However, further investigations are necessary to obtain long-term bone response of the Mg-implant in human.
Abstract
Despite an improved bone reactions of Mg-incorporated implants in the animals, little yet has been carried out by the experimental investigations in functional loading conditions. This study investigated the clinical and histologic parameters of osseointegrated Mg-incorporated implants in delayed loading conditions. A total of 36 solid screw implants (diameter 3.75 mm, length 10mm) were placed in the mandibles of 6 beagle dogs. Test groups included 18 Mg-incorporated implants. Turned titanium Implants served as control. Gold crowns were inserted 3 months. Radiographic assessments and stabilitytests were performed at the time of fixture installation, 2nd stage surgery, 1 and 3 months after loading. Histological observations and morphometrical measurements were also performed. Of 36 implants, 32 displayed no discernible mobility, corresponding to successful clinical function. There was no statistically significant difference between test implants and controls in marginal bone levels (p=0.413) and RFA values. The mean BIC % in the Mg-implants was 54.4 ± 20.2%. The mean BIC % in the turned implant was 48.9 ± 8.0%. These differences between the Mg-implant and control implant were not statistically significant (P=0.264). In the limitation of this study, bone-to-implant contact (BIC) and bone area of Mg-incorporated oxidized implant were similar to machine-turned implant. The stability analysis showed no significantly different ISQ values and marginal bone loss between two groups. Considering time-dependent bone responses of Mg-implant, it seems that Mg-implants enhanced bone responses in early loading conditions and osseointegrated similarly to cp Ti implants in delayed loading conditions. However, further investigations are necessary to obtain long-term bone response of the Mg-implant in human.
참고문헌 (24)
- Albreksson T, "Hard tissue response. In: Handbook of Biomaterials Properties", pp.500~512 (1998), Chapman and Hall
- Sul YT, "The significance of the surface properties of oxidized titanium to the bone response: special emphasis on potential biochemical bonding of oxidized titanium implant", Biomaterials, 24, pp.3893~3907 (2003)
- Sul YT, "Bone reactions to oxidized titanium implants with electrochemical anion sulphuric acid and phosphoric acid incorporation", Clin Implant Dent Relat Res, 4(2), pp.78~87 (2002)
- Sul YT, "Oxidized implants in rabbit bone: effect of calcium surface chemistry of a novel implant", Clin Implant Dent Relat Res, 6(2), pp.101~110 (2004)
- Sul YT, "Bone tissue responses to Mg-incorporated oxidized implants and machine-turned implants in the rabbit femur", J of appl Biomaterials and Biomechanics, 3, pp.18~28 (2005)
- Sul YT, "Which surface properties enhance bone responses to implants? Comparision of oxidized magnesium, Tiunite, and Osseotite implant surfaces", Int J Proshtodont, 19, pp.319~329 (2006)
- Krause A, "Integrin- mediated signaling in osteoblasts on titanium implant materials", J Biomed Mater Res, 52, pp.738~747 (2000)
- Parise LV, "Fibronectin-binding properties of the purified platelet glycoprotein Ⅱb-Ⅲa comples", J Biol Chem, 261, pp.14011~14017 (1986)
- Zreiqat H, "Mechanisms of magnesium-stimulated adhesion of osteoblastic cells to commonly used orthopaedic implants", J Biomed Mater Res, 62, pp.175~184 (2002)
- Martin JY, "Effect of titanium surface-roughness on proliferation, differentiation, and protein-synthesis of human osteoblast-like cells(MG63)", J Biomed Mater Res, 29, pp.389~401 (1995)
- Kim DS, "Histomorphometry and stability anlaysis of early loaded implants with two different surface: conditions in beagle dogs", 박사, pp.2005
- Sul YT, "The electrochemical oxide growth behavior on titanium in acid and alkaline electrolytes", Med Eng Phys, 23, pp.329~346 (2001)
- Donath K, "A method for the study of undecalcified bones and teeth with attached soft tissues: The Säge-Schliff(sawing and grinding) technique", J Oral Pathol, 11, pp.318~326 (1982)
- Satomi K, "Bone -implant interface structures after nontapping, and tapping insertion of screw-type titanium alloy endosseous implants", J Proshtet Dent, 59, pp.339~342 (1985)
- Cochran DL, "Evaluation of an endosseous titanium implant with a sandblasted and acid-etched surface in the canine mancible: radiographic results", Clin Oral Implants Res, 7, pp.240~252 (1996)
- Pham AN, "Longitudinal radiographic study of crestal bone levels adjacent nonsubmerged dental implants", J Oral Implantol, 20, pp.26~34 (1994)
- Pilliar RM, "Dental implant design effect on bone remodeling", J Biomed Mater Res, 25, pp.467~483 (1991)
- Isidor F, "Loss of osseointegration caused by occlusal load of oral implants. A clinical and radiographic study in monkeys", Clin Oral Implants Res, 7, pp.143~152 (1996)
- Randow K, "Immediate functional loading of Brånemark dental implants. An 18 month clinical follow-up study", Clin Oral Implants Res, 10, pp.8~15 (1999)
- Sagara M, "Immediate loading of bilaterally splinted titanium root-form implants in fixed prosthodontics- a technique re-examined: two case reports", Int J Periodontics Restorative Dent, 15, pp.345~361 (1995)
- Piatelli A, "Immediate loading of titanium plasma-sprayed implants: a histologic analysis in monkeys", J Periodontol, 69, pp.321~327 (1998)
- Evans GH, "Loaded and nonloaded titanium versus hydroxyapatite-coated threaded implants in the canine mandible", Int J Oral Maxillofac Implants, 11, pp.360~371 (1996)
- Watzak G, "Histologic and histomorphometric analysis of three types of dental implants following 18 months of occlusal loading: a preliminary study in baboons", Clin Oral Impl Res, 16, pp.408~416 (2005)
- Ellingsen JE, "Improved retention and bone-to-implant contact with fluoride-modified titanium implants", Int J Oral Maxillofac Implants, 19, pp.659~666 (2004)