The Electrochemical Behavior of Ni-base Metallic Glasses Containing Cr in H₂SO₄ Solutions
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In order to develop alloy resistance in aggressive sulphat ion, the corrosion behavior of metallic glasses $Ni_{92{\cdot}3}Si_{4.5}B_{32}$, $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ (at %) at different concentrations of H₂SO₄ solutions was examined by electrochemical methods and Scanning Electron Microscope (SEM) and X-ray Photoelectron Microscopy (XPS) analyses. The corrosion kinetics and passivation behavior was studied. A direct proportion was observed between the corrosion rate and acid concentration in the case of $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ alloys. Critical concentration was observed in the case of $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ alloy. The influence of the alloying element is reflected in the increasing resistance of the protective film. XPS analysis confirms that the protection film on the $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ alloy was NiS which is less protective than that formed on Cr containing alloys. The corrosion rate of $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$. alloys containing 7% and 13% Cr are $7.90-26.1{\times}10^{-3}$ mm/y which is lower about 43-54 times of the alloy $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ (free of Cr). The high resistance of $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ alloy at the very aggressive media may due to thicker passive film of Cr2O3 which hydrated to hydrated chromium oxyhydroxide.
Abstract
In order to develop alloy resistance in aggressive sulphat ion, the corrosion behavior of metallic glasses $Ni_{92{\cdot}3}Si_{4.5}B_{32}$, $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ (at %) at different concentrations of H₂SO₄ solutions was examined by electrochemical methods and Scanning Electron Microscope (SEM) and X-ray Photoelectron Microscopy (XPS) analyses. The corrosion kinetics and passivation behavior was studied. A direct proportion was observed between the corrosion rate and acid concentration in the case of $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ alloys. Critical concentration was observed in the case of $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ alloy. The influence of the alloying element is reflected in the increasing resistance of the protective film. XPS analysis confirms that the protection film on the $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ alloy was NiS which is less protective than that formed on Cr containing alloys. The corrosion rate of $Ni_{82,3}Cr_7Fe_3Si_{4.5}B_{3.2}$ and $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$. alloys containing 7% and 13% Cr are $7.90-26.1{\times}10^{-3}$ mm/y which is lower about 43-54 times of the alloy $Ni_{92{\cdot}3}Si_{4.5}B_{32}$ (free of Cr). The high resistance of $Ni_{75.5}Cr_{13}Fe_{4.2}Si_{4.5}B_{2.8}$ alloy at the very aggressive media may due to thicker passive film of Cr2O3 which hydrated to hydrated chromium oxyhydroxide.
참고문헌 (47)
- Naka, M, , J. Non-Cryst. Solids, 34, pp.257~ (1979)
- Hashimoto, K, "Passivity of Metals and Semiconductors", Proc. 5th Int. Symp. Passivity, pp.247~ (1983)
- Scully, C., "Passivity of Metals and semiconductors", Proc.5th Int. Symp. Passivity, pp.253~ (1983)
- Lee, H. J, , Corros. Sci, 37, pp.1313~ (1995)
- Lee, H. J, , Corros. Sci, 39, pp.321~ (1997)
- Habazaki, H, , Mater. Sci. Eng, 304, pp.696~ (2001)
- Pardo, A, , Corros. Sci, 44, pp.1193~ (2002)
- Zhang, T, , Mater. Trans, 44, pp.2322~ (2003)
- Hashimoto, K, , Corros. Sci, 49, pp.42~ (2007)
- Matsuura, M, , J. Alloys Compd, 496, pp.135~ (2010)
- Rife, G, , Mater. Sci. Eng, 48, pp.73~ (1981)
- Mitsuhashi, A, , Corros. Sci, 27, pp.957~ (1987)
- Lian, K, , Electrochim. Acta, 37, pp.169~ (1992)
- Gassa, L. M, , Mater. Sci. Forum, 192, pp.825~ (1995)
- Lee, H. J, , Corros. Sci., 38, pp.469~ (1996)
- Pang, S, , Corros. Sci, 48, pp.625~ (2006)
- Katagiri, H, , Corros. Sci, 43, pp.183~ (2001)
- Pang, S, , Mater. Trans, 43, pp.1771~ (2002)
- Pang, S, , Mater. Sci. Eng, 375, pp.368~ (2004)
- Pang, S, , J. Alloys Compd, 434, pp.240~ (2007)
- Arab, S. T., , Orient. J. Chem, 23, pp.777~ (2007)
- [URL]
- Boukamp, B. A, "Equivalent Circuits (User Manual)" (1989), University of Twente
- Hukovic, M. M, , J. Electroanal. Chem, 455, pp.181~ (1998)
- Girault, P, , Nucl. Instrum. Methods Phys. Res., Sect. B, 174, pp.439~ (2001)
- Martini, E. M. A, , Corros. Sci, 46, pp.2097~ (2004)
- Perez, F. J, , Corros. Sci, 48, pp.472~ (2006)
- Arab, S. T, "Influence of Cr addition on the electrochemical behavior of Ni-base metallic glasses in HCl", accepted in Physical and Chemical News
- Le Canut, J. M, , J. Nucl. Mater, 334, pp.13~ (2004)
- Goncalves, R. S, , Corros. Sci, 44, pp.467~ (2002)
- Fontana, M. G, "Corrosion Engineering, 3th ed" (1987), Mc Graw- Hill
- Singh, V. B, , Mater. Chem. Phys, 85, pp.12~ (2004)
- West, J. M, "Electrodeposition and Corrosion Processes" (1970), Van Nostrand Reinhold Company
- Pourbaix, M, "Atlas of Electrochemical Equilibria in Aqueous Solutions" (1966), Pergamon Press Inc
- Diggle, J. W, , Chem. Rev, 65, pp.365~ (1969)
- Abd El Aal, M. S, , Corrosion, 36, pp.591~ (1980)
- Chaudhary, R. S, , Br. Corros. J, 28, pp.277~ (1993)
- Bojinov, M, , Electrochim. Acta, 45, pp.2791~ (2000)
- Bojinov, M, , J. Phys. Chem, 107, pp.5101~ (2003)
- Hashimoto, K, "Passivity of Metals and Semiconductors", Proc. 5th Int. Symp. Passivity, pp.235~ (1983)
- Moffat, T. P, , J. Electrchem. Soc, 139, pp.1869~ (1992)
- Macdonald, D. D, , J. Electroanal. Chem, 572, pp.421~ (2004)
- Gray, J. J, , Surf. Sci, 600, pp.2488~ (2006)
- Ogihara, H, , Surf. Coat. Technol, 206, pp.2933~ (2012)
- Zhang, B. P, , Corros. Sci, 33(10), pp.1519~ (1992)
- Zhang, B. P, , Corros. Sci, 33(5), pp.667~ (1992)
- Tjong, S. C, , Surf. Coat. Technol, 201, pp.6781~ (2007)