Effect of Cobalt Loading on the Performance and Stability of Oxygen Reduction and Evolution Reactions in Rechargeable Zinc-air Batteries
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The commercialization of rechargeable metal-air batteries is extremely desirable but designing stable oxygen reduction reaction (ORR) catalysts with non-noble metal still has faced challenges to replace platinum-based catalysts. The nonnoble metal catalysts for ORR were prepared to improve the catalytic performance and stability by the thermal decomposition of ZIF-8 with optimum cobalt loading. The porous carbon was obtained by the calcination of ZIF-8 and different loading amounts of Co nanoparticles were anchored onto porous carbon forming a Co/PC catalyst. Co/PC composite shows a significant increase in the ORR value of current and stability (500 h) due to the good electronic conductive PCN support and optimum cobalt metal loading. The significantly improved catalytic performance is ascribed to the chemical structure, synergistic effects, porous carbon networks, and rich active sites. This method develops a new pathway for a highly active and advantageous catalyst for electrochemical devices.
Abstract
The commercialization of rechargeable metal-air batteries is extremely desirable but designing stable oxygen reduction reaction (ORR) catalysts with non-noble metal still has faced challenges to replace platinum-based catalysts. The nonnoble metal catalysts for ORR were prepared to improve the catalytic performance and stability by the thermal decomposition of ZIF-8 with optimum cobalt loading. The porous carbon was obtained by the calcination of ZIF-8 and different loading amounts of Co nanoparticles were anchored onto porous carbon forming a Co/PC catalyst. Co/PC composite shows a significant increase in the ORR value of current and stability (500 h) due to the good electronic conductive PCN support and optimum cobalt metal loading. The significantly improved catalytic performance is ascribed to the chemical structure, synergistic effects, porous carbon networks, and rich active sites. This method develops a new pathway for a highly active and advantageous catalyst for electrochemical devices.
참고문헌 (34)
- Li, Y., , Chem. Sci, 11, pp.11646~ (2020)
- Meng, F. -L., , Small, 14, pp.1703843~ (2018)
- Lee, J. -S., , Adv. Energy Mater, 1, pp.34~ (2011)
- Cai, Z., , ACS Appl. Mater. Interfaces, 12, pp.5847~ (2020)
- Thanh, T. D., , ACS Appl. Mater. Interfaces, 10, pp.4672~ (2018)
- Kaneti, Y. V., , Adv. Mater., 29, pp.1604898~ (2017)
- Zhang, W., , Angew. Chemie Int. Ed., 56, pp.8435~ (2017)
- Wang, Y., , J. Mater. Chem. A, 4, pp.5428~ (2016)
- Chen, J., , Small, 15, pp.1901518~ (2019)
- Shinde, S. S., , Energy Environ. Sci., 12, pp.727~ (2019)
- Chen, C., , Energy storage Mater., 24, pp.402~ (2020)
- Hai, G., , Nano Energy, 44, pp.345~ (2018)
- Wang, X., , J. Am. Chem. Soc, 144, pp.13634~ (2022)
- Qian, Y., , Small, 14, pp.1704169~ (2018)
- Qian, Y., , ACS Appl. Energy Mater., 2, pp.1784~ (2019)
- Getie, F. A., , SN Appl. Sci, 4, pp.270~ (2022)
- He, M., , Microporous and Mesoporous Mater, 184, pp.55~ (2014)
- Ahmed, S., , Mater. Lett, 283, pp.128781~ (2021)
- Ahmed, S., , Surf. Coat. Tech., 408, pp.126786~ (2021)
- Guo, Q., , Adv. Powder Technol., 21, pp.529~ (2010)
- Deori, K., , Cryst. Eng. Comm., 15, pp.8465~ (2013)
- Xue, W., , J. Power Source, 423, pp.9~ (2019)
- Fan, K., , ACS Nano, 12, pp.12369~ (2018)
- Xu, M., , J. Power Source, 283, pp.358~ (2015)
- Liu, S., , ACS Appl. Mater. Interfaces, 9, pp.34269~ (2017)
- Lee, D. U., , Electrochem. Commun, 60, pp.38~ (2015)
- Li, Y., , Nat. Commun., 4, pp.1805~ (2013)
- Yang, H. -B., , Sci. Adv, 2, pp.e1501122~ (2016)
- Dou, S., , Chem. Commun., 52, pp.9727~ (2016)
- Zhu, J., , ACS Catal., 6, pp.6335~ (2016)
- Qian, Y., , Carbon N. Y, 111, pp.641~ (2017)
- Wang, Z., , Nano Energy, 30, pp.368~ (2016)
- Meng, T., , J. Mater. Chem. A, 5, pp.7001~ (2017)
- Wang, S., , Nano Energy, 39, pp.626~ (2017)