Parametric study on stress distribution of thin disk specimen of rupture disk corrosion test influencing SCC initiation using finite element analysis
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Rupture disk corrosion test (RDCT) method has been recently developed for real-time measurement of initiation of stress corrosion cracking (SCC) in a high-temperature water. This work presents a parametric study on the stress distribution of a thin disk specimen of RDCT to consider the fixture shape and friction using finite element analysis (FEA). The FEA results showed a dome-shaped deformation of the specimen. From the stress analysis as a function of friction coefficient, it was suggested that the maximum stress was applied around the dome-edge, which was invariant with change to the friction coefficient. This indicates that friction between the fixture and the specimen has little effect on stress distribution. On the other hand, the stress analysis as a function of a rounded-corner radius (Rc) revealed the location at which the maximum stress was applied shifted from the dome edge to the dome center as Rc increased. From SCC initiation tests using the RDCT apparatus in a primary water environment, it was found that SCC initiates at the dome edge when Rc is 0.5 mm, while SCC initiates near the disk center when Rc is 2.0 mm. This experimental result is in good agreement with the results of FEA.
Abstract
Rupture disk corrosion test (RDCT) method has been recently developed for real-time measurement of initiation of stress corrosion cracking (SCC) in a high-temperature water. This work presents a parametric study on the stress distribution of a thin disk specimen of RDCT to consider the fixture shape and friction using finite element analysis (FEA). The FEA results showed a dome-shaped deformation of the specimen. From the stress analysis as a function of friction coefficient, it was suggested that the maximum stress was applied around the dome-edge, which was invariant with change to the friction coefficient. This indicates that friction between the fixture and the specimen has little effect on stress distribution. On the other hand, the stress analysis as a function of a rounded-corner radius (Rc) revealed the location at which the maximum stress was applied shifted from the dome edge to the dome center as Rc increased. From SCC initiation tests using the RDCT apparatus in a primary water environment, it was found that SCC initiates at the dome edge when Rc is 0.5 mm, while SCC initiates near the disk center when Rc is 2.0 mm. This experimental result is in good agreement with the results of FEA.
참고문헌 (16)
- D. Feron, "Corrosion Issues in Light Water Reactors – Stress Corrosion Cracking" (2007), Woodhead Publishing Ltd
- M. Le Calvar, "Corrosion issues in pressurized water reactor (PWR)systems", Nucl. Corros. Sci. Eng, pp.473~547 (2012)
- S. S. Hwang, "Review of factors affecting IASCC initiation of stainless steels in PWRs", Corrosion Science and Technology, 20, pp.210~229 (2021)
- François Cattant, "Corrosion issues in nuclear industry today", Mater. Today, 11, pp.32~37 (2008)[DOI]
- G. W. Jeon, "New Test Method for Real-Time Measurement of SCC Initiation of Thin Disk Specimen in High-Temperature Primary Water Environment", Nuclear Engineering and Technology (2022)[DOI]
- T. Y. Kim, "Finite Element Analysis of Stress and Strain Distribution on Thin Disk Specimen for Initiation Test in High Temperature and Pressure Environment", Corrosion Science and Technology (2023)[DOI]
- I. Simonovski, "Small punch tensile testing of curved specimens : finite element analysis and experiment", Int. J. Mech. Sci, 120, pp.204~213 (2017)
- K. F. Nilsson, "A Numerical and Experimental Assessment of the Small Punch Creep Test for 316L(N)Stainless Steels", Metals (2021)
- V. Brown, "Finite Element Modelling of the Small Punch Test for Structure Critical Design", PhD, pp.2020
- J. Petruška, "Applied Mechanics and Materials" (2012), Trans Tech Publications
- K. K. Pathak, "Influence of key test parameters on SPT results", Indian J. Eng. Mater. Sci, 16, pp.385~389 (2009)
- F. Cortellino, "On the effects of friction modelling on small punch creep test responses : a numerical investigation", J. Strain Anal. Eng. Des, 51, pp.493~506 (2016)[DOI]
- Sisheng Yang, "Effect of Geometric Factors and Processing Parameters on Plastic Damage of SUS304 Stainless Steel by Small Punch Test", Materials & Design, 41, pp.447~452 (2012)[DOI]
- M. Smith, "ABAQUS", Standard User’s Manual, Version 6.9, 2009
- Z. Zhai, "Stress corrosion crack initiation of alloy 600 in PWR primary water", Corrosion Sci, 123, pp.76~87 (2017)
- P. J. Meadows, "International round-robin on stress corrosion crack initiation of Alloy 600 material in pressurized water reactor primary water", Corrosion, 76, pp.719~733 (2020)