탄소강 볼트 체결된 GECM(Graphite Epoxy Composite Material)/ Al 판재의 구성 부재의 부식 거동
Corrosion Behavior of the parts of Carbon Steel Bolted GECM(Graphite Epoxy Composite Material)/Al plates
1
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
This work focused on corrosion of carbon steel bolted GECM/Al parts in tap water and NaCl solutions. In tap water and NaCl solutions, open circuit potential of GECM and its potentials in a series of carbon steel bolt>Ti>Al became active. Regardless of test materials, open circuit potentials in tap water were noble, and increasing NaCl concentration, its potentials became active. Immersion test of single specimen showed that no corrosion occur in Ti and GECM. In tap water, carbon steel bolt didn't show red corrosion product and in chloride solutions,corrosion rate in 1% NaCl solution was greater than its rate in 3.5% NaCl solution and red corrosion product in 1% NaCl solution was earlier observed than that in 3.5% NaCl solution. It seems that this behavior would be related to zinc-coatings on the surface of carbon stee l bolt. On the other hand, aluminium was corroded in tap water and chloride solutions. Corrosion of aluminium in tap water was due to the presence of chloride ion in tap water by sterilizing process.
Abstract
This work focused on corrosion of carbon steel bolted GECM/Al parts in tap water and NaCl solutions. In tap water and NaCl solutions, open circuit potential of GECM and its potentials in a series of carbon steel bolt>Ti>Al became active. Regardless of test materials, open circuit potentials in tap water were noble, and increasing NaCl concentration, its potentials became active. Immersion test of single specimen showed that no corrosion occur in Ti and GECM. In tap water, carbon steel bolt didn't show red corrosion product and in chloride solutions,corrosion rate in 1% NaCl solution was greater than its rate in 3.5% NaCl solution and red corrosion product in 1% NaCl solution was earlier observed than that in 3.5% NaCl solution. It seems that this behavior would be related to zinc-coatings on the surface of carbon stee l bolt. On the other hand, aluminium was corroded in tap water and chloride solutions. Corrosion of aluminium in tap water was due to the presence of chloride ion in tap water by sterilizing process.
참고문헌 (15)
- 유영란, "금속재료의 전기화학적 갈바닉 부식에 미치는 GECM의 영향", CORROSION SCIENCE AND TECHNOLOGY, 8(1), pp.27~39 (2009), 한국부식방식학회
- D. Lee, "Mechanics and Processing of Composite Materials" (1993), Seongandang
- T. J. Rcinhart, "Composites", pp.683~ (1987), ASM International
- Composite Motor Cases of Tactical Rockets, "H. V. Gerlach", ~, pp.AIAA-88-3327
- A. K. Munjal, "Use of Fiber-Reinforced Composites in Rocket Motor Industry", SAMPE Quarterly, pp.1~ (1986)
- The Effect of a Seawater Environment on the Galvanic Corrosion Behavior of Graphite, "Epoxy Composites Coupled to Metals", D. M. Aylor, 1992, CDNSWCSME-92-32
- Contact corrosion between carbon fiber reinforced composite materials and highstrength metals, "G. Mantong", National Air Intelligence Center(China), ~, pp.NAIC-ID(RS)T-0413-95 (1995)
- Accelrated Corrosion Testing of Graphite, "Epoxy Composites and Aluminum Alloy Mechanically - Fastened Joints", S. D. Thompson, 1985, AFWALTR-84-3115
- The Effect of a Seawater Environment on the Galvanic Corrosion Behavior of Graphite, "Epoxy Composites Coupled to Metals", D. M. Aylor, 1992, CDNSWCSME-91[DOI]
- F. Bellucci, , J. Appl. Electro. Chem, 16, pp.15~ (1986)
- F. Lu, , Acta Metall. Sin, 16, pp.41~ (2003)
- F. Lu, , Mater. Process, 4, pp.16~ (2004)
- F. Bellucci, , Corrosion, 47, pp.808~ (1991)
- F. Bellucci, , Corrosion, 48, pp.281~ (1992)
- 김영식, "3.5% NaCl 수용액 중에서의 금속과 GECM의 갈바닉 부식에 미치는 면적비의 영향", CORROSION SCIENCE AND TECHNOLOGY, 9(1), pp.39~47 (2010), 한국부식방식학회