3.5% NaCl 수용액 내 TWIP강의 부식거동에 미치는 합금원소 (Cu, Al, Si)의 영향
Effect of Alloying Elements (Cu, Al, Si) on the Electrochemical Corrosion Behaviors of TWIP Steel in a 3.5 % NaCl Solution
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
The corrosion behaviors of twinning-induced plasticity (TWIP) steels with different alloying elements (Cu, Al, Si) in a neutral aqueous environment were investigated in terms of the characteristics of the corrosion products formed on the steel surface. The corrosion behavior was evaluated by measuring potentiodynamic polarization test and electrochemical impedance spectroscopy. For compositional analysis of the corrosion products formed on the steel surface, an electron probe x-ray micro analyzer was also utilized. This study showed that the addition of Cu to the steel contributed to the increase in corrosion resistance to a certain extent by the presence of metallic Cu in discontinuous form at the oxide/steel interface. Compared to the case of steel with Cu, the Al-bearing specimen exhibited much higher polarization resistance and lower corrosion current by the formation of a thin Al-enriched oxide layer. On the other hand, Si addition (3.0 wt%) to the steel led to an increase in grain size, which was twice as large as that of the other specimens, resulting in a deterioration of the corrosion resistance. This was closely associated with the localized corrosion attacks along the grain boundaries by the formation of a galvanic couple with a large cathode-small anode.
Abstract
The corrosion behaviors of twinning-induced plasticity (TWIP) steels with different alloying elements (Cu, Al, Si) in a neutral aqueous environment were investigated in terms of the characteristics of the corrosion products formed on the steel surface. The corrosion behavior was evaluated by measuring potentiodynamic polarization test and electrochemical impedance spectroscopy. For compositional analysis of the corrosion products formed on the steel surface, an electron probe x-ray micro analyzer was also utilized. This study showed that the addition of Cu to the steel contributed to the increase in corrosion resistance to a certain extent by the presence of metallic Cu in discontinuous form at the oxide/steel interface. Compared to the case of steel with Cu, the Al-bearing specimen exhibited much higher polarization resistance and lower corrosion current by the formation of a thin Al-enriched oxide layer. On the other hand, Si addition (3.0 wt%) to the steel led to an increase in grain size, which was twice as large as that of the other specimens, resulting in a deterioration of the corrosion resistance. This was closely associated with the localized corrosion attacks along the grain boundaries by the formation of a galvanic couple with a large cathode-small anode.
참고문헌 (37)
- O. Grassel, , Int. J. Plast, 16, pp.1391~ (2000)
- O. Bouaziz, , Curr. Opin. Solid St. M, 15, pp.141~ (2011)
- B. C. De Cooman, , Acta Mater, 142, pp.283~ (2018)
- Y. S. Chun, , Scr. Mater, 67, pp.681~ (2012)
- D. Barbier, , Mater. Sci. Eng. A, 500, pp.196~ (2009)
- J. E. Jin, , Acta Mater, 60, pp.1680~ (2012)
- H. Idrissi, , Acta Mater, 58, pp.2464~ (2010)
- K. G. Chin, , Mater. Sci. Eng. A, 528, pp.2922~ (2011)
- R. Ueji, , Scr. Mater, 59, pp.963~ (2008)
- S. Lee, , Scr. Mater, 65, pp.1073~ (2011)
- X. Peng, , Mater. Design, 45, pp.518~ (2013)
- S. M. Lee, , Acta Mater, 144, pp.738~ (2018)
- M. Bobby Kannan, , Corros. Sci, 50, pp.2879~ (2008)
- W. Wang, , Mater. Lett, 248, pp.60~ (2019)
- X. Yuan, , Mater. Sci. Technol, 33, pp.1555~ (2017)
- Y. S. Zhang, , Corros. Sci, 41, pp.1817~ (1999)
- H. Geng, , J. Mater. Sci, 43, pp.83~ (2008)
- B. Q. Hu, , Trans. Nonferrous Met. Soc. China, 19, pp.149~ (2009)
- S. Suzuki, , Corros. Sci, 49, pp.1081~ (2007)
- B. Kim, , Adv. Mater. Sci. Eng, 2018, pp.1~ (2018)
- A. Saeed-Akbari, , Metall. Mater. Trans. A, 40, pp.3076~ (2009)
- A. Dumay, , Mater. Sci. Eng. A, 483, pp.184~ (2008)
- J. K. Hwang, , Mater. Sci. Eng. A, 737, pp.188~ (2018)
- S. J. Lee, , Acta Mater, 59, pp.6809~ (2011)
- Y. N. Dastur, , Metall. Trans. A, 12, pp.749~ (1981)
- B. Sun, , Acta Mater, 148, pp.249~ (2018)
- S. Y. Jo, , J. Alloy. Compd, 627, pp.374~ (2015)
- 장영욱, "Effects of Copper on the Corrosion Properties of Low-Alloy Steel in an Acid-Chloride Environment", Metals and Materials International, 15(4), pp.623~629 (2009), 대한금속·재료학회
- A. A. Hermas, , Electrochem. Acta, 40, pp.837~ (1995)
- M. Seo, , Corros. Sci, 26, pp.949~ (1986)
- Y. S. Choi, , J. Alloy. Compd, 391, pp.162~ (2005)
- Z. B. Zheng, , Corros. Sci, 112, pp.657~ (2016)
- G. S. Frankel, , J. Electrochem. Soc, 145, pp.2186~ (1998)
- J. H. Park, , J. Electrochem. Soc, 163, pp.791~ (2016)
- A. S. Hamada, "Passivation of Metals and Semiconductors and the Properties of Thin Oxide Layers", pp.77~ (2005)
- I. J. Park, , Int. J. Hydrogen Energ, 37, pp.9925~ (2012)
- M. Koyama, , Int. J. Hydrogen Energ, 42, pp.12706~ (2017)